The desire of builders and architects of maximum transparency and homogeneous surfaces in glass façades and glass structures extends to interior all-glass applications such as glass partitions or all-glass doors. In conventional glass systems the interconnections are performed by eye-catching fittings and clamping details that reduce the transparency and disturb the aesthetics. Novel glass–plastic-composite panels show a significantly reduced self-weight by composition of a polymer polymethylmethacrylate (PMMA) interlayer core and cover layers of thin glass. The innovative composites show high structural performance with optical properties of conventional glass. The panels allow for a direct connection into the thick PMMA interlayer core with the supporting structure or other panels. Such an integrated connection design reduces stress concentrations and allows for the development of small and unobtrusive fittings. Different integrated connections for the glass–plastic-composite panels have been designed and investigated. This article presents an experimental study on different connections, such as mechanically fastened and adhesively integrated, tested under tensile loading. Based on video analyses, crack progressions and failure mechanisms are evaluated and discussed in detail. The tests investigate temperature effects as well as the influence of the interlayer core thickness and glass type of the cover layers in varying build-ups. The comprehensive evaluation includes a description of the mechanical load-bearing behaviour in form of load versus displacement graphs as well as an investigation of crack progression and failure mechanisms for the final assessment. The results from this experimental study elucidate the structural characteristics of integrated connections in glass–plastic-composite panels under tensile loading and represent a basis for the ongoing development of real application fittings.

Im Rahmen der Dissertation wurde ein Messsystem für die Bestimmung der komplexen Permittivität von inhomogenen Stoffen bei hohen Temperaturen entwickelt, gebaut und getestet. Die Messungen des Realteils sind wenig von Störungen betroffen, Messungen des Imaginärteils unterliegen Messschwankungen bis zu 20 %. Der Effekt nimmt mit steigendem Imaginärteil ε'' ab. Der Einfluss verschiedener Messsystemkomponenten wurde untersucht, darunter der Einfluss eines Wärmestrahlungsschutzes, der Probenposition und der Messauflösung des verwendeten Vektornetzwerkanalysators. Alle Fehlerquellen wurden als hinreichend klein bewertet. Anschließend wurden verschiedene Feuerfestmaterialien aus der Glasindustrie und ein beispielhaftes Glasgemenge untersucht und die Ergebnisse mit Mikrowellenerwärmungsversuchen verglichen. Eine qualitative Übereinstimmung konnte nachgewiesen werden. Abschließend wurden Empfehlungen für die Konstruktion von mikrowellengestützten Glasschmelzaggregaten gegeben.

Der derzeitige technische Fortschritt stützt sich maßgeblich auf die Nutzung von elektrischem Strom. Der Anteil der Stromerzeugung aus Sonnenlicht hat mittlerweile in Deutschland den der Wasserkraft überschritten, der 1990 noch der größte regenerative Energielieferant war. Die Technologie der Photovoltaik (PV) wandelt die hochenergetische Strahlung der Sonne in elektrischen Strom um und nutzt dabei häufig Glasplatten als tragende Struktur. Der Hauptanspruch dieser Arbeit liegt in der Entwicklung und Untersuchung eines Befestigungssystems mit einer höher- oder hochmoduligen Klebverbindung zum gläsernen PV-Modul sowie einer möglichst universell einsetzbaren Fügeverbindung zur Unterkonstrukion. Die systematische Enwicklung der Fügeverbindung zum PV-Modul basiert auf dem Ansatz eines flexiblen, stützenden \\hbox{Ringes} für das Fügeelement (Halter), um die durch eine mechanische Belastung der Module induzierten Zugspannungen im Glas über der Fügeelementkante zu reduzieren. Eine neuartige, kombinierte Klammer-Keil-Verbindung sichert die Befestigung auf einer von ihr unabhängigen Unterkonstruktion sowohl quer als auch längs zur Schienenrichtung. Experimentelle Arbeiten charakterisieren die eingesetzte Klebverbindung unter verschiedenen Beanspruchungsszenarien, um sowohl konstruktions- als auch klebstoffbedingte Möglichkeiten und Grenzen der Fügeverbindung für die vorliegende Anwendung zu identifizieren. Die Untersuchungen weisen zudem geeignete Vorbehandlungsmaßnahmen der Aluminiumoberflächen aus. Sowohl numerische Simulationen als auch die neuartig eingesetzte Nahbereichsphotogrammetrie bestätigen in Bauteiluntersuchungen die vorteilige Wirkung des flexiblen, höhermodulig geklebten Ringes. Die vorliegende Arbeit setzt sich hierbei auch kritisch mit unterschiedlichen Einflüssen auf die Ergebnisse auseinander, die einerseits durch verschiedene Prüfstände hervorgerufen werden können und andererseits auch den verwendeten Methoden zugrunde liegen. / Today much of technical advances are due to the usage of electricity. The contribution of solar power to the production of electricity in Germany currently surpasses water powered electricity which was in 1990 the almost exclusive renewable energy source. The technology of photovoltaic systems based on high-powered sun radiation, often utilizes glass plates as a supporting structure. This dissertation primarily focuses on the research and development of a mounting system with a higher or high modulus adhesively bonded joint to the PV-module as well as an all-purpose connection to the substructure. The systematical development process of the connection to the PV-module is based on the approach of a flexible supporting ring-shaped mounting element. This reduces the tension within the glass surface at the edge of the mounting element when mechanically loading the PV-module. A novel connection using a clamp-wedge combination ensures the ability to mount the PV-module horizontally or vertically to the rail substructure. Through the development process, the bonded joint is exposed to various scenarios where the construction as well as the adhesive possibilities and limitations under each scenario are analyzed. Research outcomes yield recommendations for appropriate pre-treatment of the aluminum surfaces. Numerical simulations as well as the novel use of the near-field photogrammetry method confirmed beneficial action of the flexible ring-shaped mounting element within assembly testing of large glass specimens. This dissertation discusses how different variables can have a considerable effect on results when introduced through the testing device and through monitoring methods.

Die Solarstromerzeugung mit Photovoltaikmodulen entwickelt sich zu einer wesentlichen Säule der Energieversorgung. Dabei kann die Integration der Module in die Gebäudehülle die Nachhaltigkeit der Systeme verbessern und neue Anwendungen in der Architektur erschließen. Die vorliegende Arbeit untersucht die bautechnischen Anforderungen, die sich bei der gebäudeintegrierten Verwendung von Photovoltaikmodulen im Hinblick auf die Sicherheit von Bauteilen aus Glas ergeben. Diese Anforderungen betreffen die materielle Zusammensetzung als Bauprodukt, die Konstruktionsweise und die zu erbringenden Nachweise. Die alleinige Produktqualifizierung nach der elektrotechnischen Normung und die üblichen Qualitätssicherungsmaßnahmen in der Modulproduktion bieten hierfür keine hinreichende Grundlage, da sie keine charakteristischen Materialkennwerte liefern. Infolgedessen bedarf die Integration von Photovoltaikmodulen in die Gebäudehülle in vielen Fällen gesonderter Zustimmungs- oder Zulassungsverfahren. Resttragfähigkeitsprüfungen an Glas-Glas-Photovoltaikmodulen verfolgten das Ziel, die mechanischen Sicherheitseigenschaften gängiger Modulaufbauten im Vergleich zu Verbund-Sicherherheitsglas zu ermitteln. Auf der Grundlage der Ergebnisse lassen sich die untersuchten Aufbauten als mindestens gleichwertig beurteilen. Mit einer bauaufsichtlichen Einstufung geeigneter Modulaufbauten als Verbund-Sicherherheitsglas könnte sich der zusätzliche Nachweisaufwand für gebäudeintegrierte Photovoltaik erheblich reduzieren. Im Vierpunkt-Biegeversuch wurde der Einfluss der Glasbeschichtung mit Dünnschichtsolarzellen auf die Festigkeit der verwendeten Gläser analysiert. Die für eine praktikable Qualitätssicherung durch die Hersteller wünschenswerte Prüfung im Fertigungsformat der Module erforderte eine Modifikation der Probengeometrie. Numerische Berechnungen konnten die Anwendbarkeit des Prüf- und Auswertungsverfahrens auf die vergrößerte Probenbreite nachweisen. Bei beiden untersuchten Dünnschichttechnologien ließ sich die Randentschichtung als Ursache für eine leichte Reduzierung der Biegezugfestigkeit identifizieren. Dabei blieben Mindestwerte für das Basisprodukt Floatglas eingehalten. Die Arbeit leistet einen Beitrag zum Nachweis der mechanischen Leistungseigenschaften von Photovoltaikmodulen, die für den Einsatz als Bauprodukt erforderlich sind. Darüber hinaus können die entwickelten Empfehlungen für die photovoltaikspezifischen Entwurfs- und Planungsaufgaben einen ganzheitlichen und interdisziplinären Planungs- und Bauablauf erleichtern. / Solar electricity produced by photovoltaic systems will play a major role in future energy supply systems. Integrating photovoltaic modules into the envelopes of buildings can improve the sustainability of these systems and stimulate new architectural applications. This thesis investigates the structural requirements related to building-integrated photovoltaic modules with regard to the structural safety of architectural glazing components. These requirements apply to the materials used, the structural design and the verification procedures. Neither type approval according to the electrical engineering standards nor customary quality control in module production provides characteristic material properties. Therefore, these standards are not sufficient to determine and declare the performance of a construction product. As a result, building-integrated photovoltaic modules require individual approval in many cases. Residual strength testing of glass-glass photovoltaic modules was carried out with the aim of determining the mechanical safety properties of common module configurations in comparison with laminated safety glass. Based on the results, the configurations tested can be evaluated to provide an equivalent safety level. The classification of suitable module configurations as laminated safety glass in the building codes could significantly reduce the need for additional testing and approval, and thus facilitate the use of building-integrated photovoltaics. The influence of photovoltaic thin-film coatings on the bending strength of the float glass used as a substrate or superstrate was analysed by applying four-point bending tests. As the direct use of full-size photovoltaic-coated glass sheets as samples would simplify quality control by the manufacturers, the dimensions of the specimens were modified with respect to the existing testing standard. Numerical calculations demonstrated the applicability of the test and evaluation procedures when the larger specimen width was used. For both types of investigated thin-film PV technology, edge ablation was determined to cause a slight reduction in the bending strength. The specimens tested still met the minimum values for float glass. The thesis contributes to knowledge on the mechanical performance of photovoltaic modules that are required for use as construction products. In addition, recommendations on the specific design and planning tasks for building-integrated photovoltaics were developed to promote a holistic and interdisciplinary planning and construction process.

Der derzeitige technische Fortschritt stützt sich maßgeblich auf die Nutzung von elektrischem Strom. Der Anteil der Stromerzeugung aus Sonnenlicht hat mittlerweile in Deutschland den der Wasserkraft überschritten, der 1990 noch der größte regenerative Energielieferant war. Die Technologie der Photovoltaik (PV) wandelt die hochenergetische Strahlung der Sonne in elektrischen Strom um und nutzt dabei häufig Glasplatten als tragende Struktur. Der Hauptanspruch dieser Arbeit liegt in der Entwicklung und Untersuchung eines Befestigungssystems mit einer höher- oder hochmoduligen Klebverbindung zum gläsernen PV-Modul sowie einer möglichst universell einsetzbaren Fügeverbindung zur Unterkonstrukion. Die systematische Enwicklung der Fügeverbindung zum PV-Modul basiert auf dem Ansatz eines flexiblen, stützenden \\hbox{Ringes} für das Fügeelement (Halter), um die durch eine mechanische Belastung der Module induzierten Zugspannungen im Glas über der Fügeelementkante zu reduzieren. Eine neuartige, kombinierte Klammer-Keil-Verbindung sichert die Befestigung auf einer von ihr unabhängigen Unterkonstruktion sowohl quer als auch längs zur Schienenrichtung. Experimentelle Arbeiten charakterisieren die eingesetzte Klebverbindung unter verschiedenen Beanspruchungsszenarien, um sowohl konstruktions- als auch klebstoffbedingte Möglichkeiten und Grenzen der Fügeverbindung für die vorliegende Anwendung zu identifizieren. Die Untersuchungen weisen zudem geeignete Vorbehandlungsmaßnahmen der Aluminiumoberflächen aus. Sowohl numerische Simulationen als auch die neuartig eingesetzte Nahbereichsphotogrammetrie bestätigen in Bauteiluntersuchungen die vorteilige Wirkung des flexiblen, höhermodulig geklebten Ringes. Die vorliegende Arbeit setzt sich hierbei auch kritisch mit unterschiedlichen Einflüssen auf die Ergebnisse auseinander, die einerseits durch verschiedene Prüfstände hervorgerufen werden können und andererseits auch den verwendeten Methoden zugrunde liegen. / Today much of technical advances are due to the usage of electricity. The contribution of solar power to the production of electricity in Germany currently surpasses water powered electricity which was in 1990 the almost exclusive renewable energy source. The technology of photovoltaic systems based on high-powered sun radiation, often utilizes glass plates as a supporting structure. This dissertation primarily focuses on the research and development of a mounting system with a higher or high modulus adhesively bonded joint to the PV-module as well as an all-purpose connection to the substructure. The systematical development process of the connection to the PV-module is based on the approach of a flexible supporting ring-shaped mounting element. This reduces the tension within the glass surface at the edge of the mounting element when mechanically loading the PV-module. A novel connection using a clamp-wedge combination ensures the ability to mount the PV-module horizontally or vertically to the rail substructure. Through the development process, the bonded joint is exposed to various scenarios where the construction as well as the adhesive possibilities and limitations under each scenario are analyzed. Research outcomes yield recommendations for appropriate pre-treatment of the aluminum surfaces. Numerical simulations as well as the novel use of the near-field photogrammetry method confirmed beneficial action of the flexible ring-shaped mounting element within assembly testing of large glass specimens. This dissertation discusses how different variables can have a considerable effect on results when introduced through the testing device and through monitoring methods.

Die Solarstromerzeugung mit Photovoltaikmodulen entwickelt sich zu einer wesentlichen Säule der Energieversorgung. Dabei kann die Integration der Module in die Gebäudehülle die Nachhaltigkeit der Systeme verbessern und neue Anwendungen in der Architektur erschließen. Die vorliegende Arbeit untersucht die bautechnischen Anforderungen, die sich bei der gebäudeintegrierten Verwendung von Photovoltaikmodulen im Hinblick auf die Sicherheit von Bauteilen aus Glas ergeben. Diese Anforderungen betreffen die materielle Zusammensetzung als Bauprodukt, die Konstruktionsweise und die zu erbringenden Nachweise. Die alleinige Produktqualifizierung nach der elektrotechnischen Normung und die üblichen Qualitätssicherungsmaßnahmen in der Modulproduktion bieten hierfür keine hinreichende Grundlage, da sie keine charakteristischen Materialkennwerte liefern. Infolgedessen bedarf die Integration von Photovoltaikmodulen in die Gebäudehülle in vielen Fällen gesonderter Zustimmungs- oder Zulassungsverfahren. Resttragfähigkeitsprüfungen an Glas-Glas-Photovoltaikmodulen verfolgten das Ziel, die mechanischen Sicherheitseigenschaften gängiger Modulaufbauten im Vergleich zu Verbund-Sicherherheitsglas zu ermitteln. Auf der Grundlage der Ergebnisse lassen sich die untersuchten Aufbauten als mindestens gleichwertig beurteilen. Mit einer bauaufsichtlichen Einstufung geeigneter Modulaufbauten als Verbund-Sicherherheitsglas könnte sich der zusätzliche Nachweisaufwand für gebäudeintegrierte Photovoltaik erheblich reduzieren. Im Vierpunkt-Biegeversuch wurde der Einfluss der Glasbeschichtung mit Dünnschichtsolarzellen auf die Festigkeit der verwendeten Gläser analysiert. Die für eine praktikable Qualitätssicherung durch die Hersteller wünschenswerte Prüfung im Fertigungsformat der Module erforderte eine Modifikation der Probengeometrie. Numerische Berechnungen konnten die Anwendbarkeit des Prüf- und Auswertungsverfahrens auf die vergrößerte Probenbreite nachweisen. Bei beiden untersuchten Dünnschichttechnologien ließ sich die Randentschichtung als Ursache für eine leichte Reduzierung der Biegezugfestigkeit identifizieren. Dabei blieben Mindestwerte für das Basisprodukt Floatglas eingehalten. Die Arbeit leistet einen Beitrag zum Nachweis der mechanischen Leistungseigenschaften von Photovoltaikmodulen, die für den Einsatz als Bauprodukt erforderlich sind. Darüber hinaus können die entwickelten Empfehlungen für die photovoltaikspezifischen Entwurfs- und Planungsaufgaben einen ganzheitlichen und interdisziplinären Planungs- und Bauablauf erleichtern. / Solar electricity produced by photovoltaic systems will play a major role in future energy supply systems. Integrating photovoltaic modules into the envelopes of buildings can improve the sustainability of these systems and stimulate new architectural applications. This thesis investigates the structural requirements related to building-integrated photovoltaic modules with regard to the structural safety of architectural glazing components. These requirements apply to the materials used, the structural design and the verification procedures. Neither type approval according to the electrical engineering standards nor customary quality control in module production provides characteristic material properties. Therefore, these standards are not sufficient to determine and declare the performance of a construction product. As a result, building-integrated photovoltaic modules require individual approval in many cases. Residual strength testing of glass-glass photovoltaic modules was carried out with the aim of determining the mechanical safety properties of common module configurations in comparison with laminated safety glass. Based on the results, the configurations tested can be evaluated to provide an equivalent safety level. The classification of suitable module configurations as laminated safety glass in the building codes could significantly reduce the need for additional testing and approval, and thus facilitate the use of building-integrated photovoltaics. The influence of photovoltaic thin-film coatings on the bending strength of the float glass used as a substrate or superstrate was analysed by applying four-point bending tests. As the direct use of full-size photovoltaic-coated glass sheets as samples would simplify quality control by the manufacturers, the dimensions of the specimens were modified with respect to the existing testing standard. Numerical calculations demonstrated the applicability of the test and evaluation procedures when the larger specimen width was used. For both types of investigated thin-film PV technology, edge ablation was determined to cause a slight reduction in the bending strength. The specimens tested still met the minimum values for float glass. The thesis contributes to knowledge on the mechanical performance of photovoltaic modules that are required for use as construction products. In addition, recommendations on the specific design and planning tasks for building-integrated photovoltaics were developed to promote a holistic and interdisciplinary planning and construction process.

Uppsatsen syftar till att studera intertextualiteten i Bjarne Moelvs Helgas offer – dagboksroman om ett brott och Hjalmar Söderbergs Doktor Glas. Tyngden i analysen ligger på Moelvs roman, under det att Doktor Glas tjänar som belysande jämförelsematerial. Analysen består av tre delar där den textuella strukturen, perspektivet och berättarstrukturen undersöks. Resultaten visar att romanerna uppvisar flera stilistiska likheter men även tydliga skillnader när det gäller jagberättarens framställning. Moelv distanserar sig från det kvinnliga berättarjaget genom att begränsa henne till en iakttagare. Detta ger uttryck för en framställning som konstrueras ur ett genussystem där manliga normer slår igenom i representationer av kvinnor.

Silber-Glas-Dispersionen werden in der Herstellung von Solarzellen zur Ausbildung des Vorderseitenkontaktes großtechnisch seit vielen Jahren eingesetzt. Nichtsdestotrotz ist der Kontaktbildungsmechanismus bis jetzt nicht vollständig verstanden. In dieser Arbeit wurden Lösungs-, Transport- und Ausscheidungsprozesse von silberhaltigen Glasschmelzen in Silber-Glas-Dispersionen während der thermischen Kontaktierung von multikristallinem Silicium untersucht. Hierfür wurden systematisch Änderungen in der Zusammensetzung der Silber-Glas-Dispersionen sowie der hierfür verwendeten Gläser durch geführt, um Einzeleffekte zu separieren. Die Gläser wurden mit Silber zu Modelldispersionen verarbeitet und auf Siliciumwafer zu Herstellung von Solarzellen mittels Siebdruck abgeschieden und eingebrannt. Sowohl die Einzelkomponenten als auch die hergestellten Dispersionen wurden hinsichtlich ihrer thermisch aktivierten, linearen Schwindung untersucht. Die hergestellten Solarzellen wurden elektrisch sowie mittels FESEM in ihrer Mikrostruktur charakterisiert. Es konnten Zusammenhänge zwischen diesen Untersuchungen hinsichtlich der Silberlösung im Glas unter Oxidation, dem Silbertransport im Glas mittels Diffusion oder Konvektion sowie der Silberausscheidung unter Reduktion an der Waferoberfläche hergestellt und Einzeleffekte für den Silbertransport während des Einbrandes von Solarzellen identifiziert werden.

This PhD thesis employed high energy synchrotron x-ray radiation to reveal atomic scale structural features occurring in plastically deformed Zr52.5Ti5Cu18Ni14.5Al10 (Vit105) bulk metallic glass (BMG). The study is divided into three parts: Strain evolution during in-situ compression, strain distribution maps in mechanically-imprinted BMG, and residual strain around a single shear band. 1. Strain evolution during in-situ compression The structural rearrangements occurring during compressive deformation of a plastically deformable BMG showed that the elastic and plastic deformation of the BMG is correlated to the structural changes at short- (SRO) and medium range order (MRO). In the elastic regime, the atomic distances at SRO vary linearly with macroscopic stress. Analysis of the area under radial distribution function indicates that a small fraction of bonds in the first shell is broken in the loading direction whereas some new bonds are formed in the transverse direction. Atomic bonds at SRO appeared significantly stiffer than the MRO shells. Compared to the macroscopic values of the elastic strain, Young’s modulus and Poisson's ratio, both SRO and MRO appeared significantly stiffer, implying that the elastic behavior of the BMG is not only ruled by simple compression of the atoms/clusters but also is aided by rearrangement of atoms/clusters. The deviation of MRO atomic strain-stress correlation from linearity at the onset of plastic deformation was attributed to the activation of irreversible shear transformation zones. It was demonstrated by a strong shear strain value at the onset of yielding. This value is in good agreement with the reported value of the critical shear strain needed for activation of an irreversible STZ. The length scale of 12.5 Å indicated the largest shear strain and is probably the most effective length scale in the formation of STZs. The atomic pairs at SRO with smallest shear strain have the least contribution to the STZs. It was also indicated that the typical fracture angle of this BMG can be explained by the orientation of maximum shear strain at the onset of catastrophic shear band formation. 2. Strain distribution map in mechanically-imprinted BMG In mechanical imprinting, the BMG plate is loaded between two tools with a regular array of linear teeth and, as a result, a regular pattern of linear imprints is created on the surface of the plate. Mechanically imprinting results in considerable tensile plasticity of brittle Vit105 BMG plate. The distribution of hardness and Young’s modulus values at the transverse cross section of imprinted plate probed via nanoindentation revealed oscillating soft and hard regions beneath the surface. Spatially-resolved strain maps obtained via high-energy nano-size beam X-ray diffraction exhibited that the plastic deformation during imprinting creates a spatially heterogeneous atomic arrangement, consisting of strong compressive and tensile strain fields as well as significant shear strain fields in the cross section. It was shown that the heat treatment diminishes the heterogeneous structure resulting in brittle behavior in tension. The analysis of strain tensor components based on changes in the first diffraction maximum of the structure function, q1, revealed that Ɛx, the strain perpendicular to the loading direction, changes from the compressive at near to the surface to the tensile mode at the center of the imprinted plate. In contrast, the strain component along the loading direction, Ɛy, changes from tensile near the surface to the compressive at the center. Beneath the surface, Ɛx reaches to values about 1.5% under the imprints where there is a negligible Ɛy. The distribution map of principal strains, Ɛ1 and Ɛ2, indicated that large regions with compressive Ɛ1 and Ɛ2 exist under the imprints which can result in blocking of the propagating shear bands in agreement with microstructural observations of shear banding after uniaxial tension. Moreover, the region beneath the border of the imprinted and un-imprinted parts has the highest residual shear strain. Microstructural observations indicated that such regions can nucleate new shear bands upon tensile loading of imprinted BMG plate. 3. Residual strain around a single shear band In order to probe structural changes in the shear-induced zone around a single shear band, the distribution of residual strains at short- and medium-range order around a single shear band was determined in cold-rolled BMG plate using the nano-focused high energy x-ray diffraction. Plastic deformation results in significant residual normal and shear strains at distances of more than 15 μm around the shear band. The residual normal strains exhibit an asymmetric distribution whereas the residual shear strain is distributed symmetrically around the shear band. The large amount of residual atomic shear strain magnitude at the vicinity of the shear band triggers the nucleation of the new shear bands. The coincidence of the direction of the nucleating secondary shear bands from the main shear band with the orientation of the residual shear strain at the vicinity of the mature shear band highlight the dominant role of the shear strain in determining further plastic deformation at regions near the shear band. / Im Rahmen dieser Arbeit wird hochenergetische Synchrotron Röntgenstrahlung zum Aufzeigen der strukturellen Veränderungen in plastisch verformtem Zr52.5Ti5Cu18Ni14.5Al10 metallischen Glas verwendet. Die Arbeit gliedert sich in drei Teile: Dehnungsentwicklung während in-situ Druckversuch, Dehnungsverteilung eines mechanisch geprägten massiven metallischen Glases, und Restdehnungen in der Umgebung eines einzenen Scherbandes. 1. Dehnungsentwicklung während in-situ Druckversuch Die während der Verformung auftretende strukturelle Neuordnung eines plastisch verformbaren metallischen Glases zeigt die Korrelation der elastischen und plastischen Verformung mit den strukturellen Änderungen in den Größenordnungen der Nah- (SRO) und mittelreichweitigen Ordnung (MRO). Im elastischen Bereich verändern sich die Atomabstände in der SRO linear mit der makroskopisch anliegenden Spannung. Die Untersuchung der Fläche unter der Radialen Verteilungsfunktion (RDF) deutet auf ein Aufbrechen eines geringen Anteils der Bindungen der ersten Schale in Druckspannungsrichtung und deren Neubildung quer dazu. Die atomaren Bindungen in der SRO erscheinen wesentlich steifer als in den MRO Schalen. Vergleicht man die Werte von elastischer Dehnung, E-Modul und Querkontraktionszahl mit ihren makroskopischen Gegenstücken erscheinen beide, SRO und MRO, wesentlich steifer. Dies zeigt, dass die elastische Verformung von metallischen Gläsern nicht nur von der einfachen Stauchung der Atome bzw. Atomgruppen bestimmt, sondern auch durch deren Neuanordnung unterstützt wird. Das Abweichen der Dehnungs-Spannungs-Korrelation vom linearen Verhalten in der MRO am Beginn der plastischen Verformung wird der irreversiblen Bildung von Schertransformations-zonen (STZ) zugeschrieben. Dies zeigt sich zudem in den erhöhten Scherdehnungswerten am Beginn der Dehngrenze, welche mit den in der Literatur berichteten Werten für die kritische Scherdehnung zum Bilden einer STZ übereinstimmen. Bei einem Atomabstand von 12,5 Å tritt der höchste Wert der Scherdehnung auf und markiert den effektivsten Längenbereich der STZ Bildung. Andererseits haben die atomaren Paare in der SRO mit der geringsten Scherdehnung den geringsten Beitrag an der STZ. Es zeigt sich außerdem, dass der typische Bruchwinkel dieses metallischen Glases über die Orientierung der maximalen Scherdehnung am Beginn der kritischen Scherbandbildung erklärt werden kann. 2. Dehnungsverteilung eines mechanisch geprägten massiven metallischen Glases Eine Prägung besteht darin, eine Platte metallischen Glases mit zwei Stempel, auf denen eine regelmäßige Anordnung von geradlinigen Kerben angebracht ist, zu belasten. Dadurch wird eine ebenso regelmäßige Anordnung von geradlinigen Kerben auf der Oberfläche des metallischen Glases erzeugt. Die plastische Verformbarkeit der Vit105 Platte im Zugversuch wird durch Prägung im Vergleich zur gegossenen Probe eindeutig verbessert. Die Untersuchung der Härte und des E-Moduls über den Querschnitt der geprägten Probe zeigt die Einbringung von Abwechselnd weichen und harten Regionen an der Oberfläche. Es wurden räumlich aufgelöste Dehnungskarten des geprägten metallischen Glases durch Beugung eines hochenergetischen nanometergroßen Röntgenstrahles erzeugt. Die Ergebnisse offenbaren, dass die durch Prägung eingebrachte plastische Verformung eine räumlich heterogene Atomanordnung erzeugt, welche aus starken Druck- und Zugdehnungsfeldern besteht. Zusätzlich wird eine signifikante Scherdehnung in die Probe eingebracht. Die Wärmebehandlung beseitigt diese heterogene Struktur und führt sie fast auf den Ausgangszustand zurück. Die Analyse der Dehnungstensorkomponenten basierend auf Änderungen im erstem Maximum des Strukturfaktors, q1, zeigt, dass sich Ɛx von der Oberfläche zur Mitte der Platte hin von einer Stauchung in eine Dehnung umwandelt. Im Gegensatz dazu wandelt sich die Komponente Ɛy von der Oberfläche zur Mitte der Platte hin von einer Dehnung in eine Stauchung um. An der Oberfläche unter den Eindrücken, wo Ɛy vernachlässigbar ist, erreicht Ɛx Werte von ca. 1.5 %. Die Verteilungskarten der Hauptdehnungen zeigt, dass beide e1 und e2 unterhalb der Kerben als Stauchungen vorhanden sind. Daraus resultiert das Blockieren und Ablenken der sich ausbreitenden Scherbänder, was an Zugproben im REM beobachtet werden kann. Weiterhin hat der Bereich an der Grenze der geprägten und nicht geprägten Regionen die höchste Restscherdehnung. Mikrostrukturelle Beobachtungen deuten darauf hin, dass solche Bereiche unter Zuglast Keimstellen für neue Scherbänder sind. 3. Restdehnungen in der Umgebung eines einzenen Scherbandes Es wurde ein einzelnes Scherband einer kaltgewalzte Platte mittels Beugung eines hochenergetischen nanometergroßen Röntgenstrahles untersucht. Die strukturellen Unterschiede in der scherinduzierten Zone um ein einzelnes Scherband werden durch die Verteilung der Restdehnungen in SRO und MRO bestimmt. Plastische Verformung führt zu signifikanten Restnormal- und Restscherdehnungen in Entfernungen von mehr als 15 µm um das Scherband. Die Restnormaldehnungen zeigen eine asymmetrische Verteilung, wohingegen die Restscherdehnungen auf beiden Seiten des Scherbandes symmetrisch verteilt sind. Der große Betrag der atomaren Restscherdehnung in der Nähe des Scherbandes führt zur Bildung von neuen Scherbändern. Das Zusammenfallen der Richtung des sich bildenden sekundären Scherbandes und der Orientierung der Restscherdehnung, in der Nähe des primären Scherbandes, demonstriert die dominierende Rolle der Scherdehnung bei weiterer plastischer Verformung in der Nähe des Scherbandes.

Glass production has historically occurred at around 50 glassworks in Sweden, in a region known as the Kingdom of Crystals (Glasriket). Today, most of these sites are no longer active and left behind is glass waste of different forms (both as fragments of finished glass as well as unrefined glass melts). Consequently, increased concentrations of different metals, especially arsenic, lead and cadmium, have been found around the sites, both in soil as well as in ground and surface water. Between 2016 and 2019, the Geological Survey of Sweden (SGU) assigned Golder Associates AB (Golder) to evaluate the environmental risks at three different glassworks: Flerohopp, Åryd and Alsterbro. The results, based on humidity cell tests (HCT) conducted on glass samples from each site, showed that glass itself leached to a surprisingly high extent. Based on this, the aim of this master thesis has been to explain trends in glass leaching by a thorough literature review and through the analysis of HCT data of glass samples. Additionally, the speciation of different metals in the leachate was investigated based on geochemical modelling using PHREEQC. Results from the literature review show that one of the possible mechanisms for the leaching of glass in contact with water is ion exchange, which occurs at the surface of the glass, namely between glass components and H+ ions in water. Additionally, the literature also argues that glass with higher silica content form a more resilient structure, in contrast to glass which contains a large amount of modifiers, such as Na and Ca. Researchers speculate that adding such modifiers to the glass mass opens up the structure, making it more vulnerable upon contact with water. Looking at the total concentration of elements from the three glassworks, the results show a variation in silica content in relation to other elements. In line with this hypothesis, the sample from Åryd, which contained a higher proportion of modifiers, showed a high leaching rate of both Na and Si. Furthermore, the result shows that the leaching of Na and As follows the same pattern over the HCT period for all glassworks. This is, to some extent, also the case for Pb although the correlation is not as significant. This could be explained by the result from geochemical modelling, showing that As tends to dissolve into the leachate while Pb is more prone to forming secondary minerals. Hence explaining their differences in leaching behavior. The result from this study showed no clear correlation between Ca and either As or Pb which could potentially be explained by the formation of precipitates. However, another approach to describe the difference in the behavior between Na and Ca is based on the glass structure itself as well as the hypothesis that Na+ participate in ion exchange to a larger extent than Ca2+. Consequently, the leaching of Na+ makes the surface structure more vulnerable, thereby promoting the leaching of other components such as As and Pb. / Produktion av glas har historiskt skett på cirka 50 glasbruk i Sverige i ett område som kallas Glasriket. I dag är produktionen vid majoriteten av dessa glasbruk avvecklad och kvar på platserna finns glasavfall i olika former, både som skärvor av färdigt glas och som ej färdigställd glasmassa. Som en konsekvens av detta har förhöjda halter av olika metaller, särskilt arsenik, bly och kadmium, påträffats i jorden såväl som i grund- och ytvattnet kring glasbruken. Mellan åren 2016 och 2019 gav Sveriges geologiska undersökning (SGU) i uppdrag till Golder Associates AB (Golder) att uträtta huvudstudier och bedömma risker vid tre olika glasbruk, Flerohopp, Åryd och Alsterbro. Resultaten, baserade på fuktkammarförsök på glassavfall, påvisade att glas lakade till en överraskande hög utsträckning. Detta resultat lade grunden till detta examensarbete med frågeställningar i syfte att förklara lakning av glas baserat på en genomgående litteraturstudie samt analys av resultat från fuktkammarförsöken. Vidare har även geokemisk modellering med programmet PHREEQC gjorts för att identifiera olika specifieringar av metaller som kan förväntas påträffas i lakvätskan. Resultat från litteraturstudien visar att en möjlig process som kan förklara lakning av glas vid kontakt med vatten är jonbyte mellan glasets beståndsdelar och H+-jonerna i vattnet. Tidigare studier påvisar att ett högre kiselinnehåll i glaset skapar en mer motståndskraftig struktur än glas som innehåller en förhållandevis hög andel modifierare, såom Na och Ca. Forskare spekularar kring huruvida tillsatsen av modifierare till glasmassan bidrar till att öppna upp glasstrukturen och som en konsekvens av detta göra strukturen mer sårbar. Vid analys av prover tagna vid de tre olika glasbruken påvisade resultaten ett varierat kiselinnehåll i förhållande till övriga ämnen. I linje med denna hypotes påvisade provet från Åryd den högsta andelen modifierare och samtidigt även den högsta lakningen av Na såväl som Si. Vidare påvisar resultatet att lakningen av Na och As följer samma mönster över hela fuktkammarförsöket. Detta kan delvis ses för Pb men korrelationen är inte lika signifikant som för As. En förklaring till detta baseras på resultat från geokemisk modellering, där As tenderar att gå i lösning medan Pb kan förväntas forma sekundära mineral vilket därmed kan antas kontrollera lakningen. Resultatet från denna studie visade ingen korrelation mellan varken Ca och As eller Ca och Pb vilket också skulle kunna förklaras av utfällningar i form av Ca-mineral i lakvätskan. En annan utgångspunkt för att beskriva den skillnad som kan ses mellan Na och Ca baseras på själva glasstrukturen och hur Na+ deltar i jonbyte till en högre grad än vad Ca2+ gör. Som en konsekvens av detta bidrar lakningen av Na+ till att ytan på glaset blir mer sårbar och på så sätt gör att ämnen som As och Pb blir mer lättåtkomliga. Detta resulterar i en större möjlighet för dessa att delta i reaktioner på ytan och därmed laka ut från strukturen.