The vision of this thesis is to study how it is possible to obtain optimised workpieces during metal cutting processes in industry. Specifically, the work is aimed to increase the understanding between the steel characteristics and their link to the chip breaking and tool wear during metal cutting. The emphasis is on the influence of the cleanliness and the characteristics of non-metallic inclusions in the workpiece on the machinability of carburising steel grades. The machinability of a case hardening steel is improved by a M-treatment (additions of Ca). Also, the improved machinability of the M-steels offers an attractive potential to save money which makes it possible to reduce the tooling costs with up to 50%. The improved machinability of Ca-treated steels is correlated to the formation of lubricating slag layers consisting of Ca-enriched sulfide inclusions and oxy-sulfide inclusions, which are formed on the rake face during the machining operation. It is proposed that the formations of slag layers from the workpiece constituents are essential to minimise the chemical degradation of the tool edge due to a contact with the chip. During this process, sulfur minimises the material transfer from the chip flow, whilst Ca-treated impurities have a stabilising effect on the protective deposits made of slag layers. Since there is a remaining industrial need to increase the production rate, whilst maintaining a high quality of the finished parts, the future production will continue to require extreme demands on the quality of workpieces. If the emphasis is focused on the workpiece, it should be possible to obtain a robust manufacturing process. Therefore, the challenge for future steel metallurgists is to develop high performance grades with optimised combined properties. / Syftet med denna avhandling är att studera hur det är möjligt att framställa optimala ämnen för skärande bearbetning i industriell skala. Målsättningen med arbetet är att öka förståelsen för ståls egenskaper och dess inverkan på spånbrytning och slitage av verktyg vid skärande bearbetning. Avhandlingen fokuserar på kopplingen mellan arbetsstyckets renhet och inneslutningskarakteristik och dess inverkan på skärbarhet hos sätthärdningsstål. Skärbarheten hos vanligt sätthärdningsstål kan förbättras markant genom en Ca-behandling, dvs. en så kallad M-behandling. Den förbättrade skärbarheten hos M-stål möjliggör stora kostnadsbesparingar, som uppskattas kunna reducera verktygskostnader med upp till 50%. Den förbättrade skärbarheten hos M-stål beror på bildningen utav tribologiska skikt som är anrikade med (Mn,Ca)S- och (CaO)x-Al2O3-S-slagg. Dessa tribologiska skikt bildas på skärverktygets spånsida under ingrepp vid skärande bearbetning och består utav vissa atomer som överförts från det bearbetade ämnet till skäret. Bildandet av ett skyddande skikt anses nödvändigt för att undvika att verktygets skäregg utsätts för ett kemiskt angrepp i kontaktytan med spånflödet. Svavel anses minimera att rent arbetsmaterial överförs till skärverktyget medans kalcium-berikade inneslutningar hjälper till att bilda ett stabilt och skyddande tribologiskt skikt. Det eviga behovet att öka produktionstakten, utan att för dess skull riskera slutproduktens kvalité ställer stora krav på framtidens material. Med utgångspunkt från arbetsstycken så ska det vara möjligt att uppnå en robust industriell produktion. Utmaningen är därför att utveckla högpresterande stål med en förhöjd kombinerad funktionsegenskap.

In a multi-year project at Swerea Swecast AB studies on influence of dissolved gas on inclusions have been made. The knowledge about these parameters could be used to increase the quality of the final steel casting. The purpose of this thesis was to closer examine the impact of the oxygen level on inclusions. The questions asked were:  What was the amount of inclusions at different levels of oxygen?  What was the size of these inclusions at different levels of oxygen?  What does the inclusions consist of at different levels of oxygen? This was studied by measuring and sampling, sample preparation and microscopic analysis using an optical microscope and a scanning electron microscope (SEM). Measurements and sampling was performed at Smålands Stålgjuteri AB in Eksjö and at Swerea Swecast AB in Jönköping. At Smålands Stålgjuteri AB the measurements were performed in production while at Swerea Swecast AB the measurements were made in a way that the oxygen levels were provoked. The sample preparations were made at Swerea Swecast AB’s workshop and lab. Scanning electron microscopy (SEM) and light optic microscopy was used for the analysis. The data from these analyses were processed and charts and tables were prepared. The results from the light microscopy shows a difference in microstructure between the two samplings. The charts and tables that were obtained indicated that the number of inclusions correlated with the oxygen level. However, only to a certain extent because other parameters such as time and amount of deoxidizer have a greater effect. The size of the inclusions decreased with decreased oxygen level during deoxidation. As mentioned in the pre-study, oxides are the most common type of inclusions in steel. This was also the case in the current study. The results showed that the oxygen level can be used as an indicator of the necessary addition of deoxidiser. / I ett flerårigt projekt på Swerea Swecast AB har undersökningar kring gasers inverkan på mängden inneslutningar i gjutstål genomförts. Kunskap kring hur parametrarna ser ut skulle användas för att höja kvaliteten på gjutgods. Syftet med det här arbetet var att noggrannare undersöka den fria syrehaltens påverkan på inneslutningar. Frågeställningarna var:  Hur stort antal inneslutningar fanns vid olika syrehalter?  Hur stora var dessa inneslutningar vid olika syrehalter?  Vad innehöll dessa inneslutningar vid olika syrehalter? Detta undersöktes genom mätning och provtagning, provberedning och analys. Mätning och provtagning utfördes på Smålands Stålgjuteri AB i Eksjö och på Swerea Swecast AB i Jönköping. Vid Smålands Stålgjuteri AB utfördes mätningar under ordinarie produktion medan mätningarna på Swerea Swecast AB gjordes så att olika syrehalter provocerades fram. Provberedningen och analysen gjordes i Swerea Swecast ABs verkstad och labb. Analysen gjordes med hjälp av svepelektronmikroskop (SEM) och ljusmikroskop. Data från dessa analyser bearbetades i Excel och diagram samt tabeller togs fram. Resultatet från ljusmikroskopbilderna visar en skillnad i mikrostrukturer mellan de två gjutförsöken. Ur diagram och tabeller kan utläsas att antalet inneslutningar korrelerar med syrehalten. Dock bara till viss del eftersom andra parametrar såsom tid och mängd desoxidationsmedel har större påverkan. Storleken på inneslutningarna minskade tillsammans med syrehalten vid desoxidation. Vid en överdriven desoxidation kunde inneslutningar ansamlas i korngränserna vilket kraftigt försämrar de mekaniska egenskaperna. I förundersökningen nämndes att oxider var de vanligaste inneslutningarna i stål. Så var fallet även här. Resultatet visar tydligt att syrehalten kan användas som indikator för hur stor tillsats av desoxidationsmedel som behövs.

SÄBO AB will construct a sports Centre in Säffle municipality, the sports Centre will be used for football practice and the outer dimension of the sports Centre was determined to be 40x70 m.   The purpose was to demonstrate price and carbon dioxide emissions for the production of glulam and steel frames, the cross-laminated timber, CLT, and Paroc curtain wall. This was done by dimensioning the frames according to the Eurocodes and generate producing prices for the materials, also a calculation was made for carbon dioxide emissions for the alternatives in terms of transport and production. To calculate a key figure for earned carbon dioxide per invested capital, the differences could be more clearly demonstrated. Another aim was to produce a design proposal.   The glulam frame consists of glulam columns with three-joint truss in glulam, drawstick and windstrut in round steel. The roof trusses have a span of 40 m and the ceiling height indoors is 7.5 m. This frame became the most expensive but more beneficial in terms of carbon dioxide emissions for production.   The steel frame consists of HEA columns and saddle framework as roof, the roof trusses have a span of 40 m and the ceiling height indoors is 7.5 m. This frame was the cheapest but has the largest emissions of carbon dioxide from the production.   The curtain wall of CLT released the least carbon dioxide but became the most expensive alternative, the curtain wall of Paroc became the cheapest option but released most carbon dioxide from these two alternatives. / SÄBO AB skall uppföra en hallbyggnad i Säffle kommun, hallbyggnaden ska användas till fotbollsutövning och storleken på fotbollsplanen kommer vara en 7-mannaplan. Yttermåttet på bollhallen bestämdes till 70 x 40 meter.    Målet var att påvisa pris och koldioxidutsläpp för framställning av limträ- och stålstomme, och utfackningsvägg av KL-trä samt av Paroc. Detta gjordes genom dimensionering av stommarna enligt eurokoderna och genom att priser togs fram för materialen, även en beräkning gjordes för koldioxidutsläpp för alternativen vad gäller transport och framställning. Genom att ett nyckeltal för tjänad koldioxid per investerat kapital togs fram kunde skillnaderna påvisas på ett tydligare sätt. Ett ytterligare mål var att ta fram ett gestaltningsförslag.    Limträstommen består av limträpelare med treledstaktolar i limträ, dragband och vindstag i rundstål. Takstolarna har en spännvidd på 40 m och den fria takhöjden inomhus är 7,5 m. Denna stomme blev dyrast men mer fördelaktig vad gäller koldioxidutsläpp för framställning.    Stålstommen består av HEA-pelare och sadelfackverkstakstolar, takstolarna har spännvidden 40 m och den fria takhöjden inomhus är 7,5 m. Denna stomme blev billigast men har det största utsläppen av koldioxid från framställningen.    Utfackningsväggen av KL-trä släppte ut minst koldioxid men blev det dyraste alternativet, utfackningsväggen av Paroc blev således det billigaste alternativet men släppte ut mest koldioxid av dessa två alternativ.

Det finns många olika varianter av uppbyggnader för ett stomsystem. Skoglunds Bygg har genom åren använt sig av många olika stomsystem och de vill nu ha dessa utvärderade och jämförda för att få ett resultat på vad som varit de mest lönsamma och tidseffektiva konstruktionerna. Genom att använda ett referenshus är målsättningen att studera och jämföra olika stomsystem som Skoglunds Bygg har använt sig av i tidigare projekt, men även att jämföra några nya lösningar som de är intresserade av. Som avslutning av denna jämförelse vill Skoglunds Bygg få ut en ”Skoglunds modell”, som består av de mest lönsamma och tidseffektiva konstruktionslösningarna.    För att kunna genomföra denna jämförelse genomfördes först en litteraturstudie för att få en djupare förståelse för de olika konstruktionerna och datorprogrammet som ska användas. Därefter redovisade Skoglunds Bygg vilka konstruktioner de ville ha jämförda. När detta var gjort användes datorprogrammet BidCon för att jämföra dessa konstruktioner med hänsyn till tidsåtgång och kostnader. Detta resulterade slutligen i en ”Skoglunds modell”.   Studien resulterade i att träregelstomme med en fasad av trä var den billigaste konstruktionen medans den snabbaste konstruktionen var utfackningsväggar i trä.  För bärande lägenhetsavskiljande väggar var resultatet att skalväggen var den billigaste och snabbaste konstruktionen.  För bjälklag var resultatet att betongbjälklaget DalaDekk var den billigaste konstruktionen medans hålbjälklaget i betong var den snabbaste konstruktionen att producera.    ”Skoglundsmodellen” består av följande konstruktioner:    Ytterväggar – Träregelstommme med en fasad av trä Lägenhetsavskiljande bärande väggar – Skalväggar i betong Bjälklag – DalaDekk betongelement / There are many different variants of structures for a framework system. Skoglunds Bygg has used many different frame systems over the years and they now want these evaluated and compared to get a result on what has been the most profitable and time-efficient designs. By using a reference house, the goal is to study and compare different frame systems that Skoglunds Bygg has used in previous projects, but also to compare some new solutions that they are interested in. As a conclusion to this comparison, Skoglunds Bygg wants to get a "Skoglund model", which consists of the most profitable and time-efficient design solutions.   To be able to carry out this comparison, a literature study was first carried out in order to gain a deeper understanding of the various designs and the computer program to be used. Then Skoglunds Bygg reported which designs they wanted to compare. When this was done, the computer program BidCon was used to compare these constructions with regard to time and costs. This eventually resulted in a "Skoglund model".   The result shows that the wooden timber frame with a wooden facade are the cheapest construction, while the fastest construction is curtain walls with wood façade. For load-bearing partition walls, the result shows that the concrete shell wall is the cheapest and fastest alternative in this particular study. For the framing of joists floor, the result shows that the concrete flooring DalaDekk is the cheapest alternative, while the hollow core flooring in concrete is the fastest construction to produce.    “The Skoglundsmodel” consists of the following: Load-bearing external walls - Curtain walls with a wood facade Load-bearing partition walls - Concrete shell walls Floor layers – Flat concrete base

<p>This doctoral thesis is concerned with pitting corrosion in super martensitic stainless steel (SMSS) weldments in slightly sour service. Thee main objective with the present thesis has been to find out why pitting corrosion occurs in the heat affected zone (HAZ) at ambient rather than at elevated temperatures and how the corrosion mechanism depends on the welding process.</p><p>The thesis is divided into six parts. Part I gives a general introduction to martensitic stainless steels, focusing on the metallurgical and corrosion properties.</p><p>Part II is concerned with the conditions for initiating of pitting corrosion in two SMSS weldments. Optical microscopy in combination with sputtered neutral mass spectrometry has been used to examine the conditions, and it is shown that the corrosion resistance depends mainly on the nature of the surface oxide and less on the underlying microstructure. In the absence of H₂S the initiation is associated with spalling of the iron-enriched chromium oxide within a narrow region approximately 6mm from the fusion boundary, where the contaminated oxide layer is thinnest. As H₂S is introduced, the region close to the fusion boundary become susceptible to localised corrosion because of the more extensive metal oxidation. Thus, the high temperature oxidation and iron oxide scale formation accompanying the welding operation appears to be the main factor affecting the pitting corrosion initiation in SMSS weldments.</p><p>In Part III, a comparative study of the dissolution and repassivation behaviour of a Fe-12.3Cr-6.5Ni-2.6Mo SMSS alloy and other stainless grades has been carried out. The SMSS alloy is characterised by means of the so-called “artificial pit technique”, and a diffusion model has been developed and employed for calculation of the pit surface concentration of dissolved species during the potential step experiments. For concentrations close to the saturation level, the dissolution kinetics are adequately described by a Tafel slope of approximately 57mV/dec and a current density of 0.5mA/cm2 at –300mV SCE. On the other hand, repassivation of the active pit surface occurs when the concentration of the dissolved species drops below 30% of the saturation value. Based on a comparison with relevant literature data it is concluded that the observed response of the SMSS to localised corrosion is similar to that reported for other high-alloyed steels. This result is to be expected if the dissolution and repassivation kinetics are controlled by the content of Cr, Ni and Mo in the parent material.</p><p>In Part IV, the specific effects of H₂S on the pitting corrosion behaviour of a Fe-12.3Cr-6.5Ni-2.6Mo SMSS alloy have been examined by means of the “artificial pit technique”. Addition of a critical amount of H₂S is found to hinder repassivation and accelerate active dissolution in the SMSS pit within the stability domain of the adsorbed sulphur. Above the redox potential of H₂S/S, the effect of H₂S is found to cease, whereby dissolution and repassivation kinetics similar to H₂S-free solutions are observed. Activated pits show no signs of repassivation, not even at low surface concentration of dissolved species. It is concluded that the resistance to pitting corrosion depends both on the potential and the H2S concentration and the effect of H₂S is most significant at low potentials.</p><p>Part V is concerned with the occurrence and appearance of pitting corrosion in SMSS girth welds in the presence of H₂S. Galvanostatic and potentiodynamic measurements were carried out at ambient temperature and pressure, using both a deaerated solution and a 1mM H2S solution. In conjunction with this study, a descriptive pitting corrosion model is proposed to explain the effect of the root surface condition and the role of H₂S. The oxidized pipe surface close to the fusion boundary is found to be extremely vulnerable to pitting corrosion in the presence of H₂S, while the same zone appears to behave inert in the deaerated solution. In the latter case the oxidised surfaces were found to repassivate. In the H₂S solution, localized corrosion occurred in the most oxidized region of the HAZ, about 0 to 3mm from the fusion boundary. Moreover, it was found that a modification of the as-welded root surface by grinding hindered any initiation of pitting corrosion in this region, again highlighting the important role which high temperature oxidation and oxide scale formation play in controlling the corrosion properties of SMSS weldments. </p><p>Finally, in Part VI of the thesis, the practical implications of the above findings for choice and development of relevant corrosion test procedures have been considered. A key issue here is the effect of pre-exposure on the corrosion resistance of SMSS weldments in the presence of H₂S. Pre-exposures have been simulated in test solutions resembling the conditions in a flowline. It is shown that the quality (i.e. passivity) of SMSS root surfaces can be largely improved by the use of an appropriate pre-exposure procedure. It is therefore recommended that all samples in the future are pre-exposed to an H₂S-free solution before they are subjected to actual corrosion testing in solutions containing H₂S to avoid pitting corrosion in the oxidized part of HAZ. This is deemed to be important in order to achieve realistic results.</p>

This doctoral thesis is concerned with pitting corrosion in super martensitic stainless steel (SMSS) weldments in slightly sour service. Thee main objective with the present thesis has been to find out why pitting corrosion occurs in the heat affected zone (HAZ) at ambient rather than at elevated temperatures and how the corrosion mechanism depends on the welding process. The thesis is divided into six parts. Part I gives a general introduction to martensitic stainless steels, focusing on the metallurgical and corrosion properties. Part II is concerned with the conditions for initiating of pitting corrosion in two SMSS weldments. Optical microscopy in combination with sputtered neutral mass spectrometry has been used to examine the conditions, and it is shown that the corrosion resistance depends mainly on the nature of the surface oxide and less on the underlying microstructure. In the absence of H2S the initiation is associated with spalling of the iron-enriched chromium oxide within a narrow region approximately 6mm from the fusion boundary, where the contaminated oxide layer is thinnest. As H2S is introduced, the region close to the fusion boundary become susceptible to localised corrosion because of the more extensive metal oxidation. Thus, the high temperature oxidation and iron oxide scale formation accompanying the welding operation appears to be the main factor affecting the pitting corrosion initiation in SMSS weldments. In Part III, a comparative study of the dissolution and repassivation behaviour of a Fe-12.3Cr-6.5Ni-2.6Mo SMSS alloy and other stainless grades has been carried out. The SMSS alloy is characterised by means of the so-called “artificial pit technique”, and a diffusion model has been developed and employed for calculation of the pit surface concentration of dissolved species during the potential step experiments. For concentrations close to the saturation level, the dissolution kinetics are adequately described by a Tafel slope of approximately 57mV/dec and a current density of 0.5mA/cm2 at –300mV SCE. On the other hand, repassivation of the active pit surface occurs when the concentration of the dissolved species drops below 30% of the saturation value. Based on a comparison with relevant literature data it is concluded that the observed response of the SMSS to localised corrosion is similar to that reported for other high-alloyed steels. This result is to be expected if the dissolution and repassivation kinetics are controlled by the content of Cr, Ni and Mo in the parent material. In Part IV, the specific effects of H2S on the pitting corrosion behaviour of a Fe-12.3Cr-6.5Ni-2.6Mo SMSS alloy have been examined by means of the “artificial pit technique”. Addition of a critical amount of H2S is found to hinder repassivation and accelerate active dissolution in the SMSS pit within the stability domain of the adsorbed sulphur. Above the redox potential of H2S/S, the effect of H2S is found to cease, whereby dissolution and repassivation kinetics similar to H2S-free solutions are observed. Activated pits show no signs of repassivation, not even at low surface concentration of dissolved species. It is concluded that the resistance to pitting corrosion depends both on the potential and the H2S concentration and the effect of H2S is most significant at low potentials. Part V is concerned with the occurrence and appearance of pitting corrosion in SMSS girth welds in the presence of H2S. Galvanostatic and potentiodynamic measurements were carried out at ambient temperature and pressure, using both a deaerated solution and a 1mM H2S solution. In conjunction with this study, a descriptive pitting corrosion model is proposed to explain the effect of the root surface condition and the role of H2S. The oxidized pipe surface close to the fusion boundary is found to be extremely vulnerable to pitting corrosion in the presence of H2S, while the same zone appears to behave inert in the deaerated solution. In the latter case the oxidised surfaces were found to repassivate. In the H2S solution, localized corrosion occurred in the most oxidized region of the HAZ, about 0 to 3mm from the fusion boundary. Moreover, it was found that a modification of the as-welded root surface by grinding hindered any initiation of pitting corrosion in this region, again highlighting the important role which high temperature oxidation and oxide scale formation play in controlling the corrosion properties of SMSS weldments. Finally, in Part VI of the thesis, the practical implications of the above findings for choice and development of relevant corrosion test procedures have been considered. A key issue here is the effect of pre-exposure on the corrosion resistance of SMSS weldments in the presence of H2S. Pre-exposures have been simulated in test solutions resembling the conditions in a flowline. It is shown that the quality (i.e. passivity) of SMSS root surfaces can be largely improved by the use of an appropriate pre-exposure procedure. It is therefore recommended that all samples in the future are pre-exposed to an H2S-free solution before they are subjected to actual corrosion testing in solutions containing H2S to avoid pitting corrosion in the oxidized part of HAZ. This is deemed to be important in order to achieve realistic results.

Denna rapport behandlar ett examensarbete som bedrivits mot AB IDESTA Kök i Eskilstuna av två studenter på Mälardalens högskola. Examensarbetet ligger på D-nivå och innefattar 30 högskolepoäng.   Uppdraget från IDESTA innefattade att ta fram en ny vattenkanna i rostfritt stål för konsumentmarknaden för design produkter.   Syftet med vattenkannan var att göra en marknadsintroduktion för en större produktserie bestående av kannor och kantiner. Vid utformning av vattenkannan var det viktigt att ta hänsyn till krav både från produktion och från användare. IDESTA sökte en vattenkanna med ett estetiskt vackert utseende, problemfri användning och låg produktionskostnad. Den skulle dessutom urskilja sig på från konkurrenter och äga en samhörighet med kannor och kantiner.   Målet med examensarbete var att ritningar skulle tas fram för att företaget skulle kunna bygga en fullskalig prototyp.   För att fastställa riktlinjer för vattenkannans design genomfördes först en informationsinsamling bestående av kundintervjuer, litteraturstudier, konkurrentanalyser, besök av IDESTA och besök på mässor. Denna information analyserades sedan via olika verktyg för att identifiera krav på vattenkannans design. En lång iterativ konceptgenerering genomfördes i ett tätt samarbete med IDESTAs produktion. Detta ledde till att vattenkannan som togs fram återspeglade både marknadens krav och IDESTAs produktion.   Vattenkannan förbereddes för prototyptillverkning genom att ritningar skickades till IDESTA och de leverantörer som skulle tillverka komponenter. Vattenkannan gick igenom nya förändringar då den anpassades till leverantörernas produktion.   Resultat av arbetet är en cylindrisk vattenkanna i rostfritt stål. Dess utmärkande drag är ett ergonomiskt utformat trähandtag och en bra åtkomst för tvättning av insidan.  Utseendemässigt särskiljer sig vattenkannan från konkurrenter samtidigt som den äger samhörighet med kärl och kannor. En stålram går runt vattenkannan och trähandtaget. Denna stålram skänker vattenkannan ett utseende som inte går att hitta hos någon annan vattenkanna på marknaden.   Med hjälp av de ritningar, 3D modeller och bilder som skickades till IDESTA kunde en prototyp tas fram. Prototypen uppfyller de riktlinjer IDESTA lagt för examensarbetet och huvuddelen av kraven i kravspecifikationen.   Arbete som kvarstår är att hitta ett bra lim för montering av handtaget, utföra noggranna prototyptester, och ge vattenkannan ett bra namn.

Varmvalsade HSLA-stål (high strength low alloy) uppvisar normalt en lägre hållfasthet i sista änden av bandet. Denna s.k. ändeffekt har länge varit känd och flera undersökningar har genomförts för att utvärdera hur mycket de sistametrarna minskar i hållfasthet. Materialet som undersökts i detta examensarbete är Domex 700MC. DX 700MC är ett extra höghållfast kallformningsstål och dess typiska egenskaper är: • Utmärkt formbarhet i förhållande till sin höga hållfasthet. • God svetsbarhet • God slagseghet vid låg temperatur Materialet är varmvalsat och har en minsta sträckgräns längs valsriktningen på 700 MPa. Syfte och problemformulering är: • Bestämma ändeffektens utbredning med hjälp av hållfasthetsprovning • Litteraturstudie om materialmekanismer som inverkar på ändeffekten • Påverkan av värmebehandling • Inverkande tillverkningsfaktorer Examensarbetet är avgränsat till ett material med samma ämnesspecifikation, ÄS, vilket betyder att legeringshalterna i materialet är samma. Dessutom undersöks två olika tjocklekar av färdiga band.

Världens stadsbefolkning ökar stadigt. År 2050 förväntas världens stadsbefolkning ha ökat med 2,4 miljarder. Ytan som krävs för alla dessa människor är lika stor som Indien. För att kunna förtäta städer utan att de ska expandera ytmässigt krävs påbyggnation alternativt rivning av befintliga byggnader med efterföljande nybyggnation. I denna rapport har beräkningar gjorts på en befintlig trevåningsbyggnad för att kontrollera att utvalda särskilt viktiga element klarar en påbyggnation av två ytterligare våningar. Efter beräkningarna genomförs en jämförelse mellan den befintliga dimensionen och eventuell större dimension som kan krävas efter den tänkta påbyggnationen. Jämförelsen visar att en mindre förstärkning gör att de utvalda elementen klarar en påbyggnad i ett senare skede.

This project is the result of a cooperation between HalmstadUniversity and EABAB. The aim of the project was to create a macro that would help EABAB automate the process of designing steel trusses. When run in Microsoft Excel, the macro imports and processes coordinates from a calculator program. The data is then imported into the Building Information Modelling software Tekla Structures, which creates a 3D structural model of the steel truss. The macro saves much time in the project planning process and also helps minimize the risk of design flaws caused by human error.