While in conventional superconductors coupling between electrons and phonons is known to be responsible for the electron pairing, for the high temperature superconductors the pairing media remains under debates. Since the interactions of electrons with other degrees of freedom (phonons, magnetic excitations, etc) manifest themselves by an additional renormalization in the electronic dispersion, they can be investigated by means of Angle Resolved Photoelectron Spectroscopy. In the work renormalization in two families of high Tc cuprates have been studied. Along the diagonal of the two-dimensional BZ, the renormalization effects are represented by an unusual band dispersion that develops a so-called ‘‘kink’’. In the vicinity of the (pi, 0) point of the BZ, where the order parameter reaches its maximum, the renormalization is noticeably stronger and makes itself evident even in the shape of a single spectral line measured for a fixed momentum. It was shown that for the Bi-2212 samples substitution of Cu atoms in Cu-O plane changes renormalization features in ARPES spectra both in nodal and antinodal parts of the Brillouin zone. The smearing of the dip in the in the spectral line shape measured at (pi; 0) point can be well explained by coupling of electrons to the magnetic resonance mode. The effect of Zn and Ni substitution on the antinodal ARPES spectra was shown to be in good agreement with the influence of these impurities on magnetic resonance mode seen in inelastic neutron scattering experiments. This, in addition to the previous ARPES studies of temperature and doping dependence of peak-dip-hump structure, mass renormalization near antinodal region and a kink in the nodal part of Brillouin zone, provides further evidence that the coupling to magnetic excitations, rather than to phonons, is responsible for the observed unusual renormalization. Unlike the well studied Bi-2212 family of cuprates, photoemission on YBCO-123 turns out to be much more complicated. The observed spectra have a strong contribution from a heavily overdoped surface component with the hole doping level of about x~0.30, which is weakly dependent on the sample stochiometry. Absence of any signs of superconductivity in the spectra of the overdoped component was argued to result from the unusually high doping level. This conclusion is supported by the fact that the overdoped bands give rise to the Fermi surface and band structure consistent with the predictions of the LDA calculations, as well as, by the dependence of the photoemission matrix element on the excitation energy, which closely follows that of the superconducting bulk component. Specific experimental geometry was used to enhance the signal coming from the superconducting component. In particular, experiments with circularly polarized light bundled with simple theoretical considerations enabled better separation of the surface and the bulk components. This type of experiments also suggests that the overdoped component is mainly localized in the topmost CuO2 bilayer, while the next bilayers in the YBCO-123 structure already represent bulk properties and retain superconductivity. Using partially Ca substituted samples it was possible to obtain spectra with a suppressed overdoped component. The likely reason for the suppression is a shift of the most probable cleavage plane from the Ba–O interface to the Y layer. Spectra from the Ca substituted sample clearly reveal a sizable superconducting gap, and strong renormalization effects in the vicinity of the antinodal point. The fact that the renormalization vanishes above Tc and has strong momentum dependence, diminishing away from the (pi; 0)/(0; pi) point, strongly suggests that the reason for this renormalization in YBCO-123 is coupling of the electronic subsystem to spin resonance, similar to the case of Bi-2212.

Für die theoretische Beschreibung verschiedener Substanzen, so z.B. für diverse Kuprate die Anwendungen als Hochtemperatur-Supraleiter finden, spielt das t-J-Modell eine wichtige Rolle. In vielen Fällen kann man Abweichungen der Verbindungen vom idealen translationsinvarianten Festkörper vernachlässigen, für bestimmte Eigenschaften ist jedoch der Einfluß von Störstellen,z.B. Dotieratomen, bedeutsam. Um solche Verunreinigungen einzubeziehen, behandelt die vorliegende Arbeit das t-J-Modell mit einer zusätzlichen on-site-Energie mit über die Gitterpläte zufallsverteilten Werten. Um für dieses Modell die Einteilchen-Greensfunktion zu bestimmen, wird ein Verfahren entwickelt, welches auf der Projektionstechnik basiert und die Einbeziehung des Unordnungsterms ermöglicht. Die notwendige Mittelung über die möglichen Unordnungskonfigurationen erfolgt näherungsweise durch Faktorisierung und ist verwandt mit der sogenannten average T-matrix approximation, wird hier jedoch auf ein stark korreliertes System erweitert. Zur Illustration wird der Grundzustand von La2−xSrxCuO4 und Nd2−xCexCuO4 bei einem zusätzlichen Ladungsträger über Halbfüllung untersucht. Wie Bandstrukturrechnungen zeigen, ruft die Dotierung der elektronendotierten Substanz gerade einen solchen Zufallsterm hervor. Dies wurde in der bisherigen Literatur meist vernachlässigt. Bei der Übertragung der Bandstrukturergebnisse in die Modellparameter des t-t′-t′′-J-Modells zeigt sich, daß der Einfluß der Dotieratome bei La2−xSrxCuO4 um etwa eine Größenordnung geringer ist als in Nd2−xCexCuO4 . Als wichtige Ursache hierfür wird der Einfluß der Apex-Sauerstoffatome angesehen, die im Fall von La2−xSrxCuO4 die Seltenerd- Dotieratome gegenüber der Kupferoxidebene abschirmen. Für das mit diesen Parametern belegte Modell wird anschließend die Einteilchen- Greensfunktion berechnet, die Ausgangspunkt der Berechnung verschiedener Observablen ist. Die für die elektronendotierte Substanz auftretende lokale Mode gibt zu dem Vorschlag Anlaß, daß die unterschiedliche Stabilität der antiferromagnetischen Phase für die beiden betrachteten Substanzen nicht nur auf die Art der Ladungsträger zurückzuführen ist, sondern auch auf die Struktur der Elementarzelle. / The t-J-Modell can be applied to several classes of materials, e.g. high-Tc cuprate superconductors. Often translational invariance can be assumed, but sometimes it is necessary to take into account the effects of the doping atoms at randomly distributed sites. Therefore a t-J-Modell with an additional randomly distributed on-site energy is investigated. To calculate the one-particle Green’s function considering this term of disorder, a method is developed which bases on projection technique. The average over the possible configurations of the dopand atoms is approximated by factorization and is similar to the so-called average T-matrix approximation. Here it is extended to a model with strong correlations. In order to illustrate the methode the single-particle ground state of La2−xSrxCuO4 and Nd2−xCexCuO4 is analyzed. Band-structure calculations exhibit that for the electron-doped case the doping atoms (in first approximation) induce indeed a term of disordered on-site energies. The transformation of the values of this energies at the copper sites into the parameters in the t − t′ − t′′ − J-model shows that the influence of doping in La2−xSrxCuO4 is by about an order of magnitude smaller than in Nd2−xCexCuO4 . The existence of apex oxygen atoms between the rare-earth plane and the copper-oxygen plane in La2−xSrxCuO4 is one important reason for that effect. The single-particle Greens function for the t-t′-t′′-J-model with these parameters is calculated. A local mode appears in the electron-doped case, which suggests that the differences of the stability of the antiferromagnetic phases in both compounds are not only due to the type of charge carriers but also due to the structure of the unit cell.

In this thesis, an extended periodic Anderson model with an additional local Coulomb repulsion U f c between localized f electrons and conduction electrons is investigated by use of the projector-based renormalization method (PRM). First, it is shown that the model in one dimension shows a valence transition, which becomes sharper, when the energy of the f level approaches the Fermi level. The transition becomes also enhanced, when the hybridization V between the localized and conduction electrons decreases, for the case that the total number of electrons is fixed. In the two-dimensional case, one finds a similar valence transition behavior. However, in the valence transition regime also a superconducting phase may occur. To investigate this phase, we start from an Hamiltonian which includes small gauge symmetry breaking fields. We derive renormalization equations, from which the superconducting pairing functions are self-consistently determined. Our analytical and numerical results show that d- wave superconductivity becomes dominant in the valence transition regime. This confirms the suggestion by Miyake that valence fluctuations may lead to superconductivity in the Ce based heavy-fermion systems under high pressure. / In dieser Arbeit wird mit Hilfe der projektiven Renormierungsmethode (PRM) ein erweitertes periodische Anderson Modell untersucht, das zusätzlich eine Coulomb-Abstoßung zwischen den lokalisierten f-Elektronen und den Leitungselektronen enthält. In einer Dimension zeigt das Modell einen Valenzübergang, wenn sich die Energie des f-Niveaus der Fermienergie nähert. Der Übergang wird ebenfalls schärfer, wenn bei festgehaltener Gesamtelektronenzahl die Hybridisierung V zwischen den lokalisierten und den Leitungselekronen abnimmt. In zwei Dimensionen findet man ein ähnliches Valenzübergangsverhalten. Allerdings kann zusätzlich eine supraleitende Phase im Valenzübergangsgebiet auftreten. Um die supraleitende Phase zu untersuchen, betrachten wir einen Hamiltonoperator mit kleinen zusätzlichen Feldern, die die Eichsymmetrie brechen. Wir leiten Renormierungsgleichungen her, aus denen sich die supraleitenden Paarfunktionen selbstkonsistent bestimmen lassen. Unsere analytischen und numerischen Resultate zeigen, dass im Valenzübergangsgebiet d-Wellen-Supraleitung dominiert. Dies bestätigt eine Vermutung von Miyake, dass Valenzfluktuationen in Ce-basierten Schwerfermionensystemen bei hohen Drücken zur Supraleitung führen können.

Die vorliegende Arbeit befaßt sich mit der TEM-Untersuchungen der Realstruktur der intermetallischen Seltenerd-Borokarbid Supraleiter. Ziel war es, die Korrelation zwischen der Realstruktur und der supraleitenden Sprungtemperatur Tc zu untersuchen. Um die Realstruktur zu beeinflussen, wurden drei Probentypen mit unterschiedlicher thermischer Vorgeschichte ausgewählt. Das Seltenerd-Ion wurde entweder komplett in SENi2B2C (SE = Y, Er, Ho, Ce und Tb) oder teilweise in SE1xSE21-xNi2B2C (SE1 = Tb; SE2=Y und Er) ausgetauscht. Schließlich erfolgte ein gekoppelter Austausch von Ni und Bor im gleichen Verhältnis in YNi2-xB2-xC. Es wurde ein Einfluß der Glühbehandlung auf die Realstruktur unabhängig von der Zusammensetzung festgestellt. Das Auftreten von dicht liegenden Stapelfehlern und der Bevorzugung der <110]-Versetzungen wurden in "inhomogenen" Proben (bei 1100°C geglühten Polykristalle bzw. rasch abgeschreckter Einkristall) beobachtet. Hingegen heilen die Stapelfehler und Versetzungen durch eine Glühung bis 1450°C bzw. durch langsames Abkühlen aus. Die Versetzungsdichte ist dabei um zwei Größenordnungen niedriger. Hier kommen überwiegend die <100]-Versetzungen vor. Die Bestimmung der Gleitsysteme liefert Aussagen über die Bindungsfestigkeit in der SENi2B2C-Struktur. Die {011)-Gleitebene ist durch ihre geringste Flächendichte aufzubrechender Ni-B-Bindung (1.27/a2) ausgezeichnet. Bei Gleitung auf (001) ist das Aufbrechen einer B=C-Bindung wahrscheinlicher als das Aufbrechen von vier Ni-B-Bindungen. Eine Reihe der [010]-Helixversetzungen deutet auf einen Klettervorgang hin. In der Probenserie YNi2-xB2-xC mit x = 0.2, 0.35 und 0.5 konnten hohe Stapelfehlerdichten und auch neue Phasen der homologen Reihe (YC)n(NiB)m erzeugt werden. Die Existenz der YNiBC-, Y3Ni4B4C3-, und YNi2B2C-Phasen wurden eindeutig durch röntgendiffraktometrische, WDX-, EDX- und TEM-Untersuchungsmethoden nachgewiesen. Die Y5Ni8B8C5- und Y5Ni6B6C5-Strukturen wurden erstmalig durch TEM-Untersuchungen gefunden und bezüglich ihrer Zusammensetzung durch EDX-Analyse bestätigt. Eine hohe chemische Stapelfehlerdichte tritt in YNiBC, YNi2B2C, Y3Ni4B4C3 und Y5Ni8B8C5 auf. Die durch die Kontrastanalyse ermittelten Fehlervektoren 1/3c1111, 1/4 c1221, 1/10c3443 und 1/18c5885 entsprechen nur einer Schichtänderung in der jeweiligen Phase. Für alle Phasen wird das Einfügen zusätzlicher YC-Schichten und Ni2B-Schichten betrachtet. Bei den Phasen mit zwei aufeinander folgenden YC-Schichten ist das Entfernen einer YC-Schicht möglich. Es wurde festgestellt, daß für alle untersuchten Systeme die Supraleitung nicht von der Stapelfehlerdichte abhängt, sondern hauptsächlich durch Punktdefekte bestimmt ist. Die Unterschiede in Tc und DeltaTc der YNi2-xB2-xC-Probenserie sind besonders bei den ungeglühten Proben bemerkbar, die auf die unterschiedliche Stöchiometrie der YNi2B2C-Phase zurückzuführen ist. Die Tatsache einer vergleichbaren Erhöhung von Tc bei der 1100°C- bzw. 1450°C-Glühung spricht für die Ausheilung der Punktdefekten, die bereits bei 1100°C erfolgt, da erst die 1450°C-Glühung zur Ausheilung von Versetzungen und Stapelfehlern führt. Dieser Befund läßt sich auch bei den Proben mit und ohne Stapelfehler in YNi2B2C und Tb0.4Y0.6Ni2B2C bestätigen.

The aim of the present work is to clarify the interplay between the complex technological chain of crystal preparation, chemical and structural perfection of grown crystals of intermetallic compounds and oxides and their physical properties. This technological chain includes detailed studies of unknown or insufficiently known phase diagrams, their correlation with growth conditions and optimisation of process parameters for obtaining single crystals with high chemical and physical perfection. The measurements of the physical properties of the grown crystals such as superconductivity, thermoelectric or dielectric properties not only show new features and properties for application of the materials obtained, but also allow conclusions of the crystal perfection. The studies are focused on the following systems: RENi2B2C borocarbides (RE=Y, Tb or Ho) displaying superconductivity, magnetic order and a strong interplay between magnetic and superconducting properties for YNi2B2C, TbNi2B2C, HoNi2B2C, respectively; CeSi2-?Ô and Ru2Si3 as examples of systems with magnetic and promising thermoelectric properties, respectively; MgB2 and LiBC to test of theoretical predictions of the new superconducting intermetallic compounds discovered in the last years; SrTiO3 and SrZrO3 oxide compounds with special dielectric and optical properties. For this wide spectrum of substances necessarily different growth techniques were applied. That is mainly the floating zone (FZ) or travelling solvent floating zone (TSFZ) techniques with optical heating. Flux techniques were used if the vapour pressure of composing elements is high such as for Mg and Li. The crucible free FZ technique is very attractive for the crystal growth of these intermetallic and oxide compounds to avoid contamination with the crucible material, if the melts have very high chemical reactivity, high melting temperatures and if a large crystal size (at least 3-5 mm) is desired for corresponding physical measurements. One special aim in the presented work is the optimisation of the preparation and growth process features with respect to crystal perfection, establishing new relationships between process parameters, crystal perfection, crystallographic structure, composition of grown crystals and the related physical properties. Optimisation of crystal growth process requires own constitutional studies of growth relevant parts of corresponding multicomponent phase diagrams. Therefore, parts of the phase diagrams were experimentally revealed by differential thermal analysis (DTA), optical metallography and EPMA and partially combined with CALPHAD calculations.

The physics of transition metal oxides is controlled by the combination and competition of several degrees of freedom, in particular the charge, the spin and the orbital state of the electrons. One important parameter responsible for the physical properties is the density of charge carriers which determines the oxidization state of the transition metal ions. The central objective in this work is the study of transition metal oxides in which the charge carrier density is adjusted and controlled via lithium intercalation/deintercalation using electrochemical methods. Lithium exchange can be achieved with a high degree of accuracy by electrochemical methods. The magnetic properties of various intermediate compounds are studied. Among the materials under study the mixed valent vanadium-oxide multiwall nanotubes represent a potentially technologically relevant material for lithium-ion batteries. Upon electron doping of VOx-NTs, the data confirm a higher number of magnetic V4+ sites. Interestingly, room temperature ferromagnetism evolves after electrochemical intercalation of Li, making VOx-NTs a novel type of self-assembled nanoscaled ferromagnets. The high temperature ferromagnetism was attributed to formation of nanosize interacting ferromagnetic spin clusters around the intercalated Li ions. This behavior was established by a complex experimental study with three different local spin probe techniques, namely, electron spin resonance (ESR), nuclear magnetic resonance (NMR) and muon spin relaxation spectroscopies. Sr2CuO2Br2 was another compound studied in this work. The material exhibits CuO4 layers isostructural to the hole-doped high-Tc superconductor La2-xSr2CuO4. Electron doping is realized by Li-intercalation and superconductivity was found below 9K. Electrochemical treatment hence allows the possibility of studying the electronic phase diagram of LixSr2CuO2Br2, a new electron doped superconductor. The effect of electrochemical lithium doping on the magnetic properties was also studied in tunnel-like alpha-MnO2 nanostructures. Upon lithium intercalation, Mn4+ present in alpha-MnO2 will be reduced to Mn3+, resulting in a Mn mixed valency in this compound. The mixed valency and different possible interactions arising between magnetic spins give a complexity to the magnetic properties of doped alpha-MnO2.

Das Auftreten von Supraleitung in Systemen mit schweren Fermionen, erstmals entdeckt in CeCu_2Si_2, wird mit der Nähe zu einem quantenkritischen Punkt in Verbindung gebracht. Daraus ergibt sich ein komplexes Zusammenspiel von Magnetismus und Supraleitung, das in der vorliegenden Arbeit durch Messungen der spezifischen Wärme, der Wechselfeldsuszeptibilität und durch inelastische Neutronenstreuexperimente an verschiedenen Einkristallen von CeCu_2(Si_{1-x}Ge_x)_2 untersucht wird. Der Schwerpunkt liegt auf der genauen Charakterisierung des magnetischen Anregungsspektrums von CeCu_2Si_2 des S-Typs. Die Ergebnisse der Neutronenstreumessungen implizieren stark, dass die Kopplung der supraleitenden Cooper-Paare durch überdämpfte Spinfluktuationen vermittelt wird, die in der Umgebung eines Quantenphasenübergangs gehäuft auftreten. Unter Substitution einiger Si- durch Ge-Atome in CeCu_2Si_2 stabilisiert sich die magnetische Ordnung, und die Supraleitung wird zunehmend unterdrückt. Neutronenstreumessungen ergeben, dass dies bei 2 % Ge-Substitution dazu führt, dass sich Magnetismus und Supraleitung gegenseitig verdrängen, während sie bei 10 % Ge-Substitution mikroskopisch koexistieren. - (Die Dissertation ist veröffentlicht im Logos Verlag Berlin GmbH, Berlin, Deutschland, http://www.logos-verlag.de, ISBN: 978-3-8325-2456-2) / The occurrence of superconductivity in systems with heavy fermions, discovered for the first time in CeCu_2Si_2, is often linked to the vicinity of a quantum critical point. This results in a complex interplay of magnetism and superconductivity, which is studied by means of specific heat and ac susceptibility measurements as well as neutron scattering experiments on different single crystals of CeCu_2(Si_{1-x}Ge_x)_2 in the present thesis. The focus is put on the detailed characterisation of the magnetic excitation spectrum in S-type CeCu_2Si_2. Neutron scattering results strongly imply that the coupling of superconducting Cooper pairs is mediated by overdamped spin fluctuations, which accumulate in the vicinity of a quantum phase transition. By substituting Si by Ge atoms in CeCu_2Si_2 magnetic order is stabilised and superconductivity successively suppressed. Neutron scattering experiments demonstrate that 2 % Ge substitution leads to magnetic order being displaced by superconductivity on decreasing temperature, whereas both coexist microscopically in the case of 10 % Ge substitution.

The structure and magnetism of selected compounds of the pnictides iron based superconductors with chemical formula LnO{1-x}FeAsFx (Ln = La,Sm and Ce), commonly known as 1111, and of rare earth iron borates RFe3(BO3)4 (R = Tb, Gd, Nd and Y), were studied by means of hard x-ray diffraction. For the 1111 pnictides compounds, Rietveld refinement of powder x-ray diffraction measurements at room temperature reveals, that the ionic substitution of O by F has no effect on the structure of the FeAs layers of tetrahedra, whereas the major changes takes place in the LnO layer. These changes are reflected as a shrinkage of the crystal lattice, specially in the c direction. Additionally, a study of the temperature dependent structure of the Sm and Ce-1111 compounds was performed and an estimation of the the structural transition temperature was obtained. The results of the structural measurements, combined with electrical resistivity and µSR, were used to construct the Sm and Ce-1111 phase diagrams. These phase diagrams are characterized by two regions, consisting of a spin density wave (SDW) state and a superconducting state, which are sharply separated upon doping. Considering the different Ln ion, upon F doping the transition temperatures are more efficiently suppressed in Ce-1111 as compared to Sm-1111. More intriguingly, for the Ce case, a coexistence region between static magnetism and superconductivity without an orthorhombic distortion has been observed. Further analysis of the width of the Bragg peaks reveals strong lattice fluctuations towards phase transitions, which are reflected in magnetic and transport properties. Moreover, a strong damping of the lattice fluctuations is observed at Tc for superconducting Sm-1111 samples, giving experimental evidence of competing orders towards phase transitions in the iron pnictides. Regarding the iron borates, non-resonant x-ray scattering studies have shown several new diffraction features, from the appearance of additional reflections that violate the reflection conditions for the low temperature crystal structure, to the emerging of commensurate superlattice peaks that appear below TN. A detailed analysis of the structure factors and q dependencies of the earlier reflections, demonstrate their magnetic nature. Additional resonant x-ray magnetic scattering experiments on NdFe3(BO3)4 were performed at the Nd L2,3 and Fe K edges. The results show that the magnetization behavior is different for the Nd and for the Fe sublattices. Moreover, we find that the magnetization of the Nd sublattice is induced by the Fe magnetization. The temperature dependent measurements also show a commensurate to incommensurate transition where the magnetic structure changes from a commensurate collinear structure, where both Nd and Fe moments align in the hexagonal basal plane, to an incommensurate spin helix structure that propagates along c. When a magnetic field is applied, the spin helix is destroyed and a collinear structure is formed where the moments align in a direction perpendicular to the applied magnetic field. Moreover, the critical field at which the spin helix is destroyed is the same field at which the magnetic induced electric polarization is maximum, thus, showing that the spin helix is not at the origin of the electric polarization.

The recent discovery of high-temperature superconductivity in Fe-based materials triggered worldwide efforts to investigate their fundamental properties. Despite a lot of similarities to cuprates and MgB2, important differences like near isotropic behaviour in contrast to cuprates and the peculiar pairing symmetry of the order parameter (OP) have been reported. The OP symmetry of Fe-based superconductors (FBS) was theoretically predicted to be of so-called s± state prior to various experimental works. Still, most of the experimental results favour the s± scenario; however, definitive evidence has not yet been reported. Although no clear understanding of the superconducting mechanisms yet exists, potential applications such as high-field magnets and Josephson devices have been explored. Indeed, a lot of reports about FBS tapes, wires, and even SQUIDs have been published to this date. In this thesis, the feasibility of high-field magnet applications of FBS is addressed by studying their transport properties, involving doped BaFe2As2 (Ba-122) and LnFeAs(O,F) [Ln=Sm and Nd]. Particularly, it is important to study physical properties in a sample form (i.e. thin films) that is close to the conditions found in applications. However, the realisation of epitaxial FBS thin films is not an easy undertaking. Recent success in growing epitaxial FBS thin films opens a new avenue to delve into transport critical current measurements. The information obtained through this research will be useful for exploring high-field magnet applications. This thesis consists of 7 chapters: Chapter 1 describes the motivation of this study, the basic background of superconductivity, and a brief summary of the thin film growth of FBS. Chapter 2 describes experimental methods employed in this study. Chapter 3 reports on the fabrication of Co-doped Ba-122 thin films on various substrates. Particular emphasis lies on the discovery of fluoride substrates to be beneficial for epitaxy without compromising superconducting properties. It is worth mentioning, that a world record Tc of 28 K for Co-doped Ba-122 thin films is reported here. Chapter 4 describes high-field transport properties (up to dc 35 T) of epitaxial P-doped Ba-122 thin films prepared by MBE. Among the FBS, P-doped Ba-122 shows very high transport critical current densities, although the Tc is lower than for LnFeAs(O,F)[Ln=Sm and Nd]. Additionally, the film is microstructurally clean. These high Jc values are due to a high vortex line energy. Chapter 5 deals with transport properties of epitaxial SmFeAs(O,F) thin films. In the course of this work, a dc 45 T magnet has been used within collaboration with the National High Magnetic Field Laboratory at Tallahassee, FL, USA. SmFeAs(O,F) thin films have been prepared by molecular beam epitaxy (MBE). The investigated film shows a very high transport critical current density (Jc) of over 105 A/cm2 at 45T and 4.2K for both main crystallographic directions, which features favourable for high-field magnet applications. Additionally, by investigating the pinning properties, a dimensional crossover between the superconducting coherence length and the FeAs interlayer distance at 30-40K was observed. Chapter 6 reports on high-field transport properties of NdFeAs(O,F) thin films prepared by MBE. In this case, the transition from Abrikosov to Josephson vortices was observed around 20-30K. Additionally, the angular Jc data were scaled with the anisotropic GinzburgLandau approach. The obtained parameters at given temperature are observed to increase with decreasing temperature, which is different from Co-doped Ba-122. Chapter 7 summarises this work. / Die kürzliche Entdeckung von Hochtemperatur-Supraleitung in Fe-basierten Materialien löste weltweite Bemühungen aus, deren grundlegende Eigenschaften zu untersuchen. Neben vielen Gemeinsamkeiten mit den Kupraten und MgB2 sind wichtige Unterschiede wie nahezu isotropes Verhalten (im Gegensatz zu den Kupraten) und eine auffällige Paarungssymmetrie des Ordnungsparameters (OP) berichtet worden. Die OP-Symmetrie der Fe-basierten Supraleiter (FBS) wurde theoretisch als s± berechnet, noch bevor experimentelle Versuche unternommen wurden. Derzeit favorisieren experimentelle Ergebnisse das s±-Szenario, dennoch gibt es noch keine definitiven Nachweise. Obwohl noch kein komplettes Verständnis des supraleitenden Mechanismus existiert, wurden schon potentielle Anwendungen wie Josephson-Elemente und Hochfeldmagnete erforscht. In der Tat erschienen zahlreiche Veröffentlichungen über supraleitende Kabel, Bänder und auch SQUIDs. Diese Arbeit befasst sich mit der Durchführbarkeit von Hochfeld-Anwendungen durch die Untersuchung der Transporteigenschaften von FBS, namentlich Ba-122 und LnFeAs(O,F)[Ln=Sm und Nd]. Es ist von großer Wichtigkeit, die physikalischen Eigenschaften in einer Probenform zu untersuchen, die der Form in Anwendungen nahekommt (z.B. Dünnschichten), um dieselben Rahmenbedingungen vorgeben zu können. Es ist jedoch nicht einfach, epitaktische FBS Dünnschichten zu realisieren. Kürzlich gewonnene Erkenntnisse in der Herstellung von epitaktischen FBS-Dünnschichten ermöglichen nun ein tieferes Eindringen in die Transporteigenschaften. Die in diesen Untersuchungen gewonnenen Informationen stellen somit wichtige Argumente in der Diskussion um Hochfeld Anwendungen dar. Diese Arbeit besteht aus sieben Kapiteln: Kapitel 1 beinhaltet die Motivation dieser Arbeit, die Grundlagen der Supraleitung und eine kurze Zusammenstellung der bisherigen Arbeiten zur Dünnschichtherstellung von FBS. Kapitel 2 beschreibt experimentelle Methoden, die im Zuge dieser Arbeit verwendet wurden. Kapitel 3 berichtet von der Herstellung Co-dotierter Ba-122 Dünnschichten (Co-Ba-122) auf verschiedenen Fluoridsubstraten. Dabei wurde Augenmerk darauf gelegt, neben einem verbesserten epitaktischen Wachstum der Dünnschichten die supraleitenden Eigenschaften nicht zu beeinträchtigen. Anzumerken ist, dass in diesem Rahmen Tc-Rekord-Werte von 28 K in Co-Ba-122 erzielt werden konnten. Kapitel 4 beschreibt die Hochfeld-Transporteigenschaften epitaktisch gewachsener P-dotierter Ba-122 Dünnschichten, die durch MBE hergestellt wurden. Unter den FBS zeigt P-dotiertes Ba-122 enorm hohe kritische Transport-Stromdichten, obwohl das Tc niedriger ist als bei LnFeAs(O,F)[Ln=Sm und Nd]. Der Grund dafür konnte in der hohen Flusslinienkern-Energie des P-dotierten Ba-122 ermittelt werden. Kapitel 5 behandelt Transporteigenschaften von epitaktisch gewachsenen SmFeAs(O,F)-Dünnschichten. In diesem Zusammenhang wurde ein dc-45 T-Hochfeldmagnet in Zusammenarbeit mit dem National High Magnetic Field Laboratory in Tallahassee, Florida, USA, genutzt. SmFeAs(O,F)-Dünnschichten wurden mit dem Molekularstrahl-Verfahren (MBE) hergestellt. Die Schichten zeigen sehr hohe kritische Transport-Stromdichten (Jc) von über 105 A/cm2 bei 45 T und 4.2 K für beide kristallographische Hauptrichtungen, parallel zur c-Achse und in der ab-Ebene. Diese Ergebnisse sehen sehr verheißungsvoll für eine Verwendung in Hochfeld-Anwendungen aus. Zusätzlich konnte durch die Untersuchung der Pinning-Eigenschaften ein Dimensionsübergang zwischen supraleitender Kohärenzlänge und FeAs-Ebenenabstand im Bereich 30-40 K beobachtet werden. Kapitel 6 berichtet über die Hochfeld-Transporteigenschaften von NdFeAs(O,F)-Dünnschichten, die mithilfe des MBE-Verfahrens hergestellt wurden. In diesem Falle konnte ein Ubergang von Abrikosov- zu Josephson-Flusslinien im Temperaturbereich 20-30 K beobachtet werden. Zusätzlich konnte die winkelabhängige kritische Stromdichte mit dem anisotropen Ginzburg-Landau-Ansatz skaliert werden. Die erhaltenen Parameter für verschiedene Temperaturen steigen mit fallender Temperatur. Dieses Verhalten ist gegensätzlich zu dem in Co-dotiertem Ba-122 gefundenen. Kapitel 7 gibt eine Zusammenfassung dieser Arbeit.

In dieser Arbeit werden Messungen der elektrischen und thermischen Transportkoeffizienten an einem antiferromagnetisch ordnenden Iridat und FeAs-basierten Hochtemperatursupraleitern vorgestellt und analysiert. Iridate sind Materialien mit starker Spin-Bahn-Kopplung. In dem zweidimensionalen Vertreter Sr_2IrO_4 führt diese Kopplung zu isolierendem Mott-Verhalten mit gleichzeitiger antiferromagnetischer Ordnung der gekoppelten Spin-Bahn-Momente. Somit stellt Sr2IrO4 ein Modellsystem für die Untersuchung magnetischer Anregungen dieser Momente in Iridaten dar. Die Analyse der Wärmeleitfähigkeit von Sr_2IrO_4 liefert erstmals klare Hinweise auf magnetische Wärmeleitung in den Iridaten. Die extrahierte magnetische freie Weglänge gibt Aufschluss über die Streuprozesse der zum Wärmetransport beitragenden Magnonen und lässt Schlüsse über die Anregungen des gekoppelten Spin-Bahnsystems zu. Die FeAs-Hochtemperatursupraleiter haben aufgrund ihrer geschichteten Kristallstruktur einen hauptsächlich zweidimensionalen Ladungstransport. Die Phasendiagramme dieser Materialien setzen sich aus Ordnungsphänomenen zusammen, die Magnetismus, Supraleitung und eine Strukturverzerrung umfassen. Das Hauptaugenmerk richtet sich auf die Reaktion der Transportkoeffizienten mit den sich ausbildenden Phasen in Vertretern der 111- und 122-Familien unter chemischer Dotierung innerhalb und außerhalb der Schichtstruktur. Mithilfe von Widerstand und magnetischer Suszeptibilität lassen sich Phasendiagramme der verschiedenen Supraleiterfamilien konstruieren. In ausgewählten Fällen werden der Hall-Koeffizient und elektrothermische Transporteffekte genutzt, um das Phasendiagramm näher zu erforschen. Der Großteil der Untersuchungen zeigt omnipräsente elektrische Ordnungsphänomene, die als nematische Phase bezeichnet werden. Die Messdaten zeigen, dass die Wärmeleitfähigkeit und der Nernst-Koeffizient dominant von Fluktuationen, die der nematischen Phase vorausgehen, beeinflusst werden. Aus den Ergebnissen der Nernst-Daten an dotiertem BaFe_2As_2 werden Schlüsse über die der nematischen Phase zugrunde liegenden Mechanismen des korrelierten Elektronensystems gezogen.