Submitted by Setor de Tratamento da Informa??o - BC/PUCRS (tede2@pucrs.br) on 2016-09-26T11:23:37Z No. of bitstreams: 1 DIS_LUCAS_DA_SILVA_MEIRELLES_PARCIAL.pdf: 243991 bytes, checksum: d72682f62c8b046220c35b86e91ffff1 (MD5) / Made available in DSpace on 2016-09-26T11:23:38Z (GMT). No. of bitstreams: 1 DIS_LUCAS_DA_SILVA_MEIRELLES_PARCIAL.pdf: 243991 bytes, checksum: d72682f62c8b046220c35b86e91ffff1 (MD5) Previous issue date: 2016-01-27 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior - CAPES / Conselho Nacional de Pesquisa e Desenvolvimento Cient?fico e Tecnol?gico - CNPq / Most anchorage miniplates that are currently used do not present orthodontic devices. Thus, orthodontists resort to creativity and utilize adaptations such as buttons, brackets or tubes bonded directly to miniplates, which makes them more versatile in terms of dental movement possibilities. The goal of this paper was to determine, in Megapascals (MPa), the strength that can be attributed to the bond between an anchorage miniplate and an orthodontic accessory united by different materials. The bond between the accessory and the miniplates was divided into two groups: Group 1 resin (Transbond XT?, 3M ESPE), 20 specimens; Group 2 Cyanoacrylate (Scoth Bond?, 3M ESPE), 20 specimens. The shearing strength test (Rcp) was performed on a universal testing machine EMIC DL-2000. The result was 2.28 ? 0.44 MPa for Group 1 and 4.90 ? 0.76 MPa for Group 2. Sample normality was verified through the Kolmogorov-Smirnov test. The comparison between the means for the variable response was carried out using the Student T test. There was a significant statistical difference between the groups; however, both materials showed higher strength than that needed for dental movement. / A maioria das miniplacas de ancoragem utilizadas atualmente, n?o apresentam dispositivos ortod?nticos. Dessa forma, ortodontistas lan?am m?o da criatividade e utilizam adapta??es como a colagem de bot?es, br?quetes ou tubos diretamente nas miniplacas, tornando-as mais vers?teis em termos de possibilidades de movimenta??es dent?rias. O objetivo do trabalho foi determinar, em Mega Pascal (MPa), a for?a que pode ser atribu?da a essa uni?o entre a miniplaca de ancoragem e o acess?rio ortod?ntico unidos por diferentes materiais. A uni?o do acess?rio ?s miniplacas, foi dividida em dois grupos: Grupo 1 resina (Transbond XT?, 3M ESPE ), 20 corpo de prova; Grupo 2 Cianoacrilato ( Scoth Bond?, 3M ESPE), 20 corpos de prova. O teste de resist?ncia ao cisalhamento (Rcp) foi realizado na m?quina de ensaio universal EMIC DL-2000. O resultado obtido foi de 2,28 ? 0,44 MP para o Grupo 1 e 4,90 ? 0,76 MPa para o Grupo 2. A normalidade da amostra foi verificada atrav?s do teste Kolmogorov-Smirnov. A compara??o entre as m?dias da vari?vel-resposta foi realizada atrav?s do Teste T de Student. Houve diferen?a estat?stica significante entre os grupos, por?m ambos materiais apresentaram for?a superior a necess?ria para movimenta??o dent?ria.

Orientador: Ary dos Santos Pinto / Resumo: O objetivo de evitar a progressão da má oclusão e propiciar um crescimento craniofacial mais harmonioso. Os ativadores monoblocos e elásticos induzem o posicionamento terapêutico anterior da mandíbula para correção da má oclusão de Classe II podendo expandir ou não as arcadas dentárias para melhorar a forma dos arcos e promover o alinhamento dentário. O objetivo deste estudo foi avaliar os efeitos do tratamento ortopédico funcional, sobre as relações anteroposteriores e transversais dos arcos dentários no tratamento da má oclusão de classe II com dois tipos de aparelhos ortopédicos funcionais, o Bionator de Balters e o Ativador elástico de Klammt utilizando modelos de estudo digitais. Foram coletadas as documentações ortodônticas de 15 indivíduos com má oclusão de Classe II divisão 1 acompanhados pelo período de 1 ano sem tratamento (grupo controle) e de 30 indivíduos com má oclusão de Classe II divisão 1 tratados com os dois tipos de aparelhos ortopédicos funcionais e acompanhados pelo período de 1 ano (grupo tratado). Modelos em gesso iniciais e após 1 ano de controle ou tratamento foram digitalizados no Scanner 3D R700 e obtidas as medidas de relação oclusal interarcos e das dimensões dos arcos com auxílio do software 3Shape's OrthoAnalyzer™ Advanced Orthodontic Diagnosis and Treatment Planning. As medidas obtidas foram transferidas para o programa SPSS (versão16, SPSS, Chicago, Ill) para análise estatística. Trabalho 1: O tratamento com o aparelho Bionator pode promover r... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The objective to avoid the progression of the malocclusion and enable a more harmonious craniofacial growth. The monobloc and the elastic activator induce the mandible to an anterior therapeutic positioning to treat the Class II malocclusion and have different capabilities to expand or not the dental arches to improve the arch form and to promote the dental aligns. The aim of this study was to evaluate the differences in the antero-posterior and transverse dental arch relationship after orthopedic treatment of the Class II malocclusion two types of functional orthopedic appliances (Bionator of Balters and Elastic activator of Klammt) using digital study models. Orthodontic dental records of 15 individuals Class II division 1 malocclusion followed for one year without treatment (control group) and 30 individuals with Class II division 1 malocclusion treated with the two functional orthopedic appliances (Bionator of Balters and Elastic activator of Klammt) and followed for one year (treated group). Initial and final dental casts of these individuals will be digitalized in the 3D R700 Scanner and measurements of the interarch occlusal relationship and of the dimensions of arches were evaluated. The data was assessed through Descriptive Statistic and t test and analysis of variance (anova) statistical analysis. Paper 1: The treatment with the Bionator device can promote a significant reduction in the lower arch perimeter, with an increase in the lower incisor irregularity (increa... (Complete abstract click electronic access below) / Mestre

A proposta deste estudo foi comparar cefalometricamente os efeitos esqueléticos e dentoalveolares no tratamento da má oclusão de Classe II com os distalizadores Pendulum e Jones jig, seguidos do aparelho fixo corretivo e compará-los ao grupo controle. O grupo 1 foi composto de 23 pacientes com Classe II tratados com o distalizador Pendulum seguido do aparelho fixo corretivo, sendo que do número total de pacientes, 19 foram comparados ao grupo Jones jig, apresentando média de idade inicial de 13,86 anos; 18 pacientes foram comparados com os grupos Jones jig e controle, com média de idade inicial de 13,92 anos. O grupo 2 compreendeu 25 pacientes com Classe II tratados com o distalizador Jones jig seguido do aparelho fixo corretivo, com média de idade inicial de 12,90 comparados aos grupos Pendulum e controle; porém, somente 21 pacientes foram comparados com o grupo Pendulum, com média de idade inicial de 13,08 anos. Os pacientes foram dessa forma divididos a fim de compatibilizar média de idade inicial e tempo de tratamento, conferindo confiabilidade ao estudo comparativo. O grupo 3 compreendeu 19 jovens com má oclusão de Classe II não tratada e média de idade inicial de 12,88 anos. Os dois grupos experimentais foram avaliados individualmente por meio do teste ANOVA dependente e teste de Tukey, a fim de verificar as alterações intragrupos nos tempos inicial (T1), pós-distalização (T2) e final do aparelho fixo (T3). Os grupos experimentais foram também comparados por meio do teste t de Student nos três tempos avaliados e nas alterações entre as fases T2-T1 e T3-T2. Por fim, os grupos experimentais foram comparados ao grupo controle por meio do teste ANOVA a um critério e teste de Tukey, com o intuito de diferenciar as alterações do tratamento das alterações ocorridas pelo crescimento craniofacial. Os resultados demonstraram que os distalizadores não interferem no componente maxilar e mandibular, ou seja, não promovem alterações na relação maxilomandibular. Quanto à correção da Classe II, ambos os aparelhos promovem uma distalização eficiente dos primeiros molares, contudo o grupo Jones jig demonstrou maior perda de ancoragem, representada pela mesialização e extrusão significante dos primeiros e segundos pré-molares, provavelmente em virtude das diferenças no reforço de ancoragem e que resultou um maior aumento da AFAI ao final do tratamento. Os segundos molares superiores, após a distalização apresentaram maior distalização angular e linear e maior intrusão quando comparados ao grupo Jones jig. Comprovou-se que os efeitos adversos ocorridos na fase de distalização intrabucal são posteriormente corrigidos durante a mecânica corretiva. Em comparação ao grupo controle, ao final do tratamento ortodôntico, observou-se que o grupo Pendulum apresentou um crescimento maior da maxila e mandíbula, justificada provavelmente pela diferença significante na idade final entre os grupos. Verificou-se uma vestibularização significantemente maior dos incisivos inferiores nos grupos experimentais, ocorrido provavelmente pelo uso de elásticos de Classe II. Ao final do tratamento, foi observada a correção do trespasse horizontal e vertical nos grupos experimentais, alterações já esperadas na mecânica corretiva, contudo a distalização dos molares superiores seguida do aparelho fixo corretivo não promoveu alterações significantes no componente tegumentar. / The purpose of this study was to compare cephalometric skeletal and dentoalveolar effects in the treatment of Class II malocclusion with Pendulum and Jones jig appliances, followed by fixed orthodontic appliances, and to compare it to a control group. Group 1 comprised 23 Class II patients treated with the Pendulum and fixed appliances; being that the total number of patients,19 were compared to the Jones jig group, at a mean initial age of 13.86 years; 18 patients were compared with the Jones jig and control groups, at a mean initial age of 13.92 years. Group 2 comprised 25 Class II patients treated with the Jones jig and fixed appliances, at a mean initial age of 12.90 years, compared to Pendulum and control groups; however, only 21 patients were compared only to the Pendulum group, at a mean initial age of 13.08 years. Patients were divided in this way in order to match average initial age and length of treatment, giving reliability to the comparative study. Group 3 comprised 19 young subjects with untreated Class II malocclusions. The two experimental groups were individually evaluated by dependent ANOVA and Tukey tests, to verify the intragroup changes among the initial (T1), postdistalization (T2) and end of fixed appliance (T3) stages. The experimental groups were also compared with t tests in the three times evaluated and the changes between T2-T1 and T3-T2. Finally, the experimental groups were compared to the control group by one-way ANOVA and Tukey tests in order to differentiate treatment changes from the craniofacial growth normal changes. Results showed that the appliances did not interfere in the maxillary and mandibular components, i.e., did not promote changes in the maxillomandibular relationship. Regarding the correction of the Class II, both devices promoted an efficient distalization of the maxillary first molars, but Jones jig group showed greater anchorage loss, represented by significant mesial movement and extrusion of the first and second premolars, probably due to differences in anchorage reinforcement and resulting in a greater increase in the LAFH at the end of treatment. The maxillary second molars after distalization were more angularly and linearly distalized and intruded than the Jones jig group. It was proved that the adverse effects that occurred during the intraoral distalization are subsequently corrected during the corrective mechanics. Compared to the control group at the end of orthodontic treatment, we observed that the Pendulum group had a greater maxillomandibular growth, probably justified by significant differences in the final ages between the groups. There was a significantly greater tipping of mandibular incisors and first molars in the experimental groups, probably due to the use of Class II elastics. At the end of treatment, it was observed the correction of the overjet and overbite in the experimental groups, changes already expected in the mechanical correction, however the distalization of maxillary molars followed by fixed corrective orthodontics did not promote significant changes in the soft tissue.

A estabilidade da má oclusão de Classe II já foi vastamente estudada, porém, são mínimos os estudos que avaliaram a recidiva e a estabilidade da relação molar de Classe II. Sendo assim, o objetivo deste estudo foi avaliar a estabilidade da relação molar em casos com má oclusão de Classe II inicial, tratados ortodonticamente sem extrações, visando quantificar a recidiva e correlacioná-la com alguns fatores como a severidade da relação molar de Classe II inicial, o tempo de tratamento, tempo de contenção e de avaliação pós-contenção. A amostra consistiu de 39 indivíduos (16 do sexo feminino e 23 do masculino) com má oclusão de Classe II inicial tratada ortodonticamente sem extrações, com aparelhos fixos. A média de idade ao início do tratamento foi de 12,94 ± 1,21 anos, ao final do tratamento foi de 15,14 ± 1,38 anos e no estágio pós-contenção foi de 21,18 ± 2,65 anos. A média do tempo de tratamento foi de 2,19 ± 0,83 anos e do tempo de avaliação pós-tratamento foi de 6,12 ± 2,23 anos. Para verificar a influência da severidade da relação molar de Classe II inicial na estabilidade da relação molar, a amostra foi dividida em dois grupos, um apresentando relação molar inicial de meia Classe II ou de três quartos de Classe II e outro apresentando relação molar de Classe II completa. Nos modelos de estudo das fases inicial, final e pós-contenção, foram medidas a relação molar, as relações de primeiros e segundos pré-molares e a relação de caninos. Os dados obtidos foram analisados pelos testes ANOVA dependente, Tukey e correlação de Pearson, além do teste t independente entre os dois grupos divididos de acordo com a severidade da relação molar inicial. Houve uma pequena recidiva não significante da relação molar de 0,12mm. A severidade inicial da relação molar de Classe II não se correlacionou com a sua recidiva no período pós-contenção. Quando a amostra foi dividida em dois grupos, com meia e 3/4 de Classe II e com Classe II completa ao início do tratamento, nenhuma diferença na recidiva da relação molar foi encontrada entre os grupos. Concluiu-se que a correção da relação molar de Classe II é estável e a severidade inicial não exerce influência sobre a recidiva da relação molar. / The stability of Class II malocclusion was widely studied, however, few studies evaluated relapse and stability of Class II molar relationship. This way, this study aimed to evaluate stability of molar relationship after nonextraction treatment of Class II malocclusion, in order to quantify the relapse and correlates it to some factors such the severity of initial Class II molar relationship, treatment time, retention time and time of postretention evaluation. Sample comprised 39 subjects (16 female; 23 male) with initial Class II malocclusion treated orthodontically without extractions, with fixed appliances. Mean age at the beginning of treatment was 12.94 ± 1.21 years, at the end of treatment was 15.14 ± 1.38 years and at postretention stage was 21.18 ± 2.65 years. Mean treatment time was 2.19 ± 0.83 years and mean time of posttreatment evaluation was 6.12 ± 2.23 years. To verify influence of severity of initial Class II molar relationship in stability of molar relationship, sample was divided into two groups, one presenting a half-cusp or 3/4-cusp Class II molar relationship, and other with full-cusp Class II molar relationship. In dental casts from initial, final and postretention stages, it was measured molar, first and second premolars and canine relationships. Data obtained were analyzed by dependent ANOVA, Tukey and Pearson\'s correlation tests, besides of independent t test between the two groups divided by severity of initial molar relationship. There was a small and not significant relapse of molar relationship of 0.12mm. The initial severity of the Class II molar relationship was not correlated to its relapse in the postretention period. When sample was divided into two groups, with half-cusp or 3/4 cusp, and full-cusp Class II molar relationship at the beginning of treatment, no difference in relapse of molar relationship was found between the two groups. It was concluded that correction of Class II molar relationship is stable and initial severity does not influence relapse of molar relationship.

Submitted by Márcio Ropke (ropke13marcio@gmail.com) on 2017-06-21T12:50:38Z No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Efeito da adição de monômeros funcionalizados em um cimento ortodôntico.pdf: 1936663 bytes, checksum: 47dd85a59adae3a7b7b5560fd6403dfe (MD5) / Made available in DSpace on 2017-06-21T12:50:38Z (GMT). No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Efeito da adição de monômeros funcionalizados em um cimento ortodôntico.pdf: 1936663 bytes, checksum: 47dd85a59adae3a7b7b5560fd6403dfe (MD5) Previous issue date: 2016-07-27 / Sem bolsa / O advento da adesão na Odontologia permitiu o uso de acessórios ortodônticos cimentados diretamente sobre a superfície dental. Com estes procedimentos adesivos, surge um importante questionamento acerca do método mais indicado para a remoção dos bráquetes e desgaste do agente de cimentação remanescente sobre o esmalte dental. Várias são as técnicas propostas no que tange aos instrumentos de remoção, mas a literatura aponta que, independente da técnica, sempre há dano à estrutura dental. O uso de acessórios ortodônticos, associados ao excesso de agente de cimentação ao redor dos bráquetes, possibilita um maior acúmulo de biofilme e, consequentemente, desenvolvimento de cárie ao redor dos acessórios. Assim, este estudo tem o objetivo adicionar metacrilatos metálicos coloridos - cobre e prata - a cimento ortodôntico experimental e avaliá-los quanto a influência da cor dos novos cimentos na identificação dos excessos, previamente à fotoativação do produto, e no desgaste do remanescente após a descimentação dos acessórios ao final do tratamento. Outro objetivo foi avaliar o efeito antimicrobiano produzido pela adição dos metacrilatos contra o Streptococcus mutans, microorganismo fortemente associado à carie dental. Os grupos testados foram: Cimento ortodôntico experimental sem metacrilato metálico (C), Cimento ortodôntico experimental com Metacrilato de Prata (CMAg), Cimento ortodôntico experimental com Metacrilato de Cobre (CMCu) e referências comerciais - cimento ortodôntico convencional (Transbond XT, 3M Unitek, Monrovia, CA, EUA) e resina composta de coloração distinta da estrutura dental (Resina Composta Filtek Z250 XT D3, 3M ESPE, St Paul, MN, USA). Os materiais foram caracterizados quanto ao grau de conversão, propriedades colorimétricas, propriedades físicas, químicas e mecânicas, viabilidade celular e efeito antibacteriano (através de Teste de Difusão e Ágar e Teste de Contato Direto Modificado). O tempo utilizado na cimentação e remoção dos bráquetes foi avaliado e a superfície do esmalte foi caracterizada em microscopia eletrônica de varredura (MEV), bem como a perda estrutural de esmalte, resultante da remoção do agente de cimentação residual, foi avaliada através da Perfilometria 3D (Rugosidade superficial - Sa e volume de esmalte perdido - V). Os procedimentos experimentais de cimentação, remoção e desgaste do remanescente de cimento foram realizados por operador experiente. Para todos os testes foi considerado o valor p<0,05 como estatisticamente significante. Através dos testes realizados, foi possível identificar que os CMCu e CMAg podem ser potencialmente antimicrobianos, uma vez que apresentaram halo de inibição maior que os dos demais grupos. CMCu inibiu o crescimento microbiano no período de 24h, havendo a necessidade de testar este efeito em um período prolongado. Os cimentos coloridos facilitaram a identificação e remoção do material que permaneceu sobre a estrutura dental, reduzindo o tempo de trabalho. / The advent of adhesion in dentistry allowed the use of orthodontic appliances directly cemented on the tooth surface. With these adhesive procedures, an important question about the most appropriate method for debond brackets and for wearing remnant bonding agents on dental enamel arises. There are several methods and instruments used for that purposes, but the literature indicates that, regardless of the technique, there is always damage to tooth structure. The use of orthodontic appliances associated with the excess bonding agent around the brackets allows a biofilm accumulation and thus caries development around accessories. This study aims to add colored metal methacrylates - copper and silver - on experimental orthodontic cement, and evaluate the influence of the color of new cements when identifying excesses prior to photoactivation of the product, and the remaining wear after debonding of accessories at the end of the treatment. Another objective was to evaluate the antimicrobial effect produced by the addition of methacrylates against Streptococcus mutans, a microorganism that is strongly associated to dental caries. The groups tested were experimental orthodontic cement without metal methacrylate (C), experimental orthodontic cement with Silver Methacrylate (CMAg), experimental orthodontic cement with Copper Methacrylate (CMCu) and commercial references - conventional orthodontic cement (TB - Transbond XT, 3M Unitek, Monrovia, CA, USA) and resin composed of distinct coloration of the dental structure (RZ250 - Filtek Z250 XT D3, 3M ESPE, St Paul, MN, USA). The materials were characterized as the degree of conversion, colorimetric properties, physical, chemical and mechanical properties, cell viability and antibacterial effect (through Agar Diffusion Method and Modified Direct Contact Test). The time used in cementing brackets and removal of the remnant bonding agent was evaluated, then the enamel surface was characterized by scanning electron microscopy (SEM), and the structural enamel loss resulting from the removal of the residual bonding agent was evaluated by means of 3D profilometry (surface roughness - Sa and volume of enamel loss - V). Experimental procedures of cementing, removal and wear of the remaining cement were performed by an experienced operator. For all tests it was considered p <0.05 as statistically significant. Through the tests, it was possible to identify that CMCu and CMAg can potentially be antimicrobial, since they showed inhibition zone larger than the other groups. CMCu inhibited microbial growth in the 24 hour period, needing to test this effect in a longer period. Colored cement facilitated the identification and removal of the material that remained on the tooth structure, reducing the working time.

Submitted by Márcio Ropke (ropke13marcio@gmail.com) on 2017-07-06T14:18:08Z No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Caracterização de adesivos ortodônticos contendo diferentes agentes antimicrobianos.pdf: 3166148 bytes, checksum: 5862bf27e3e8385240db0ee1ec39a812 (MD5) / Made available in DSpace on 2017-07-06T14:18:08Z (GMT). No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Caracterização de adesivos ortodônticos contendo diferentes agentes antimicrobianos.pdf: 3166148 bytes, checksum: 5862bf27e3e8385240db0ee1ec39a812 (MD5) Previous issue date: 2017-02-22 / Sem bolsa / Neste trabalho, foi realizada uma revisão sistemática e meta-análise dos agentes antimicrobianos incorporados em sistemas adesivos ortodônticos e um estudo laboratorial a fim de caracterizar e incorporar nanopartículas de ß-TCP dopadas com agentes antimicrobianos em uma matriz de um adesivo ortodôntico. Inicialmente, a revisão sistemática e meta-análise foram realizadas para avaliar a efetividade dos agentes antimicrobianos incorporados em sistemas de adesão ortodônticos, bem como seu futuro desenvolvimento. Uma busca em oito bases de dados foi realizada: MedLine (PubMed), Lilacs, Ibecs, Web of Science, Scopus, Scielo e Google acadêmico. Enquanto isso, um estudo laboratorial foi conduzido com o objetivo de avalir o efeito antimicrobiano, a inibição de cárie, a resistência de união por cisalhamento e as propriedades físico-químicas alcançadas pela adição de nanopartículas de ß-TCP dopadas com agentes antimicrobianos a um adesivo ortodôntico. Na revisão sistemática e meta-análise, de um de total de 1320, 32 estudos estavam relacionados a sistemas de adesão ortodônticos com atividade antibacteriana e foram incluídos no estudo. Dez estudos foram excluídos da meta-análise por não apresentarem dados quantitativos de atividade antimicrobiana. Todos os estudos relataram a inclusão de agentes antimicrobianos em sistemas de adesão ortodônticos como uma estratégia de tratamento odontológico eficaz. Já no estudo laboratorial, os adesivos ortodônticos contendo nanopartículas de ß-TCP dopadas com agentes antimicrobianos inibiram significativamente o crescimento bacteriano, mas também não resultaram em nenhum efeito sobre ?S sob e em torno dos braquetes. Para a força de ligação, não foi observada diferença entre TB e YO. A utilização de YOß-TCP@CHX resultou em valores mais baixos de resistência de ligação, enquanto a adição de nanopartículas de ß-TCP dopadas com outros agentes antimicrobianos não reduziu a resistência de ligação de YO. O tipo de adesivo ortodôntico não afetou dramaticamente o grau in situ de conversão, sorção de água e solubilidade em água. Apesar de serem necessários estudos clínicos para confirmar a efetividade desses materiais no controle antimicrobiano, a revisão sistemática e meta-análise e o estudo laboratorial demonstraram que há evidência, in vitro, de atividade antibacteriana sem prejudicar drasticamente as outras propriedades investigadas desses adesivos ortodônticos. / In this work, a systematic review and meta-analysis of antimicrobial agents incorporated in orthodontic adhesive and a laboratory study were carried out to incorporate and characterize ß-TCP nanoparticles doped with antimicrobial agents in an orthodontic adhesive. Initially, the systematic review and meta-analysis were performed to evaluate the effectiveness of the antimicrobial agents incorporated in orthodontic adhesion systems, as well as their future development. A search in eight databases was performed: MedLine (PubMed), Lilacs, Ibecs, Web of Science, Scopus, Scielo and Google academic. Meanwhile, a laboratory study was conducted to evaluate the antimicrobial effect, caries inhibition, shear bond strength and physico-chemical properties achieved by the addition of anti-microbial doped nanoparticles with antimicrobial agents to an adhesive Orthodontic. In the systematic review and meta-analysis, out of a total of 1320, 32 studies were related to orthodontic adhesion systems with antibacterial activity and were included in the study. Ten studies were excluded from the meta-analysis because they did not present quantitative data of antimicrobial activity. All studies have reported the inclusion of antimicrobial agents in orthodontic adhesion systems as an effective dental treatment strategy. In the laboratory study, orthodontic adhesives containing ß-TCP nanoparticles doped with antimicrobial agents significantly inhibited bacterial growth, but also did not result in any effect on ?S under and around brackets. For the binding force, no difference was observed between TB and YO. Using YOß-TCP@CHX resulted in lowest values of bond strength, while addition of ß-TCP nanoparticles doped with other antimicrobial agents did not reduce the bond strength of YO. The orthodontic adhesive type did not dramatically affect the in situ degree of conversion, water sorption, and water solubility. Although clinical studies are required to confirm the effectiveness of these materials in antimicrobial control, systematic review and meta-analysis and laboratory study have demonstrated that there is evidence, in vitro, of antibacterial activity without impairing the other investigated properties of these in vitro orthodontic adhesive.

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / A influência da dieta e da hereditariedade nas características dentofaciais foi avaliada através do exame de duas populações indígenas amazônicas divididas por um processo de fissão linear. Os indígenas que constituem a aldeia Arara-Iriri são descendentes de um único casal expulso da aldeia Arara-Laranjal. O crescimento da aldeia Iriri ocorreu pelo acasalamento de parentes próximos, ratificado por um alto coeficiente de consanguinidade (F=0,25, p<0,001). A epidemiologia da má oclusão e das características da face foi analisada nos indivíduos entre dois e 22 anos, das aldeias Iriri (n=46) e Laranjal (n=130). A biometria da dentição e da face foi obtida em 55 indígenas em dentição permanente sem perdas dentárias, através da fotogrametria facial e dos modelos de gesso. O desgaste dentário foi examinado em 126 indivíduos através da análise de regressão múltipla. Os resultados revelaram uma determinação significativa da idade no desgaste dos dentes (R2=87,6, p<0,0001), que se mostrou semelhante entre as aldeias (R2=0,027, p=0,0935). Por outro lado, diferenças marcantes foram observadas nas características dentofaciais. Revelou-se uma face mais vertical (dolicofacial) entre os índios Iriri e o predomínio do tipo braquifacial nos indígenas da aldeia original, corroborado pela fotogrametria. Uma face sagitalmente normal foi observada em 97,7% da aldeia Laranjal, enquanto faces convexas (26,1%, RR-16,96) e côncavas (15,2%, RR=19,78) eram mais prevalentes na aldeia Iriri (p<0,001). A biprotrusão, com consequente redução do ângulo nasolabial, era uma característica comum entre os Arara, porém com maior prevalência no grupo Iriri (RP=1,52, p=0,0002). A prevalência da má oclusão foi significativamente mais alta na aldeia Iriri (RP= 1,75, p=0,0007). A maioria da população da aldeia original (83,8%) apresentou uma relação normal entre os arcos dentários, contudo, na aldeia resultante (Iriri), 34,6% dos indivíduos era Classe III (RP=6,01, p<0,001) e 21,7% era Classe II (RP=2,02, p=0,05). Enquanto nenhum caso de apinhamento e de sobremordida foi observado na aldeia Iriri, a razão da prevalência era 2,64 vezes maior para a mordida aberta anterior (p=0,003), 2,83 vezes (p<0,001) para a mordida cruzada anterior, 3,93 (p=0,03) para a sobressaliência aumentada, e de 4,71 (p=0,02) para a mordida cruzada posterior. Observou-se uma alta prevalência das perdas dentárias, sem diferença entre as aldeias (RP=1,46, p=0,11). O exame dos modelos revelou uma tendência de incisivos maiores e pré-molares e caninos menores na aldeia Iriri, delineando uma semelhança na massa dentária total entre as aldeias, que, aliada a arcadas dentárias maiores, justificaram o menor índice de irregularidade dos incisivos entre esses indígenas. Esses resultados minimizam a influência do desgaste dentário, uma evidência direta de como um indivíduo se alimentou no passado, no desenvolvimento dentofacial e enfatizam o predomínio da hereditariedade, através da endogamia, na etiologia da variação anormal da oclusão dentária e da morfologia da face. / The influence of diet and genetics on dentofacial features was examined through the analysis of two split indigenous Amazon populations originated by a process of a linear fission. The Arara-Iriri indigenous are descendants of a single couple who were expelled from a larger village (Arara-Laranjal). In the resultant new village, the initial expansion occurred through the mating of closely related people, causing a high coefficient of inbreeding (F=0.25, p<0.001). The epidemiology of malocclusion and facial characteristics were analyzed in individuals aged from 2 to 22 years, from the Arara-Iriri (n=46) and Arara-Laranjal (n=130) villages. The biometric study of the dentition and face was performed in the permanent dentition of the indigenous without tooth loss (n=55) by facial photogrammetry and dental casts analysis. Tooth wear was examined in 126 individuals in the permanent dentition through multiple regression analysis. Findings pointed out a significant determination of age on tooth wear (R2=87.6, p<0.0001), which was similar between the villages (R2=0.027, p=0.0935). However, we found marked differences in the dentofacial morphology. The indigenous of the Iriri village presented a more vertical face (dolichofacial) compared to the people of the original village, predominantly braquifacial. This clinical data was corroborated by facial photogrammetry. A sagitally normal face was observed in 97.7% of the Laranjal village, while convex (26.1%, RR=16.96) and concave faces (15.2%, RR=19.78) were significantly more prevalent in the Iriri village (p<0.001). Biprotrusion, with consequent reduction of nasolabial angle, was a common feature among the Arara indigenous, but its occurrence in the Iriri village was higher (RP=1.52, p=0.0002). The prevalence of malocclusion was significantly higher in the Iriri population (RP=1.75, p=0.0007). While the majority of the population (83.8%) in the Laranjal village presented a normal Class I relationship, in the Iriri village 34.6% were Class III (RP=6.01, p<0.001) and 21.7% were class II (RP=2.02, p=0.05). No case of crowding and overbite was observed in the Iriri village, however the relative risk was 2.64 times greater for anterior open bite (p=0.003), 2.83 for anterior crossbite (p<0.001), 3.93 for increased overjet (p=0.03), and 4.71 times (p=0.02) for posterior crossbite. We observed a high prevalence of tooth loss, with no significant difference between the villages (RP=1.46, p=0.11). The dental cast analysis revealed larger incisors combined to smaller cuspids and bicuspids in the Iriri sample, causing an overall similarity in the total tooth size between the villages, which associated to larger dental arch dimensions, explained a decreased incisor irregularity in the Iriri indigenous. These findings mitigates the influence of tooth wear, a direct evidence of what an individual ate in the past, on dentofacial development and emphasize the role of heredity, through inbreeding, in the etiology of abnormal variation of dental occlusion and facial morphology of current human populations.

Orientador: Rebeca Di Nicoló / Banca: Clovis Pagani / Banca: Daniela Raggio / Resumo: Este estudo in vitro teve como objetivo avaliar a influência das ciclagens térmica e termomecânica na resistência adesiva de bráquetes colados em esmalte bovino com primers convencionais e auto-condicionates. Noventa incisivos bovinos foram aleatoriamente divididos em 2 grupos (G), de acordo com o primer utilizado: XT (n=45) - bráquetes colados com primer convencional (Transbond XT/3M, Unitek); SEP (n=45) - bráquetes colados com primer auto-condicionante (Transbond Plus SEP/3M, Unitek). Após a colagem dos bráquetes, cada grupo foi subdividido em 3 subgrupos (n=15): SC (sem ciclagem) - as amostras não receberam nenhum tipo ciclagem; CT (ciclagem térmica) - as amostras receberam apenas ciclagem térmica (500 ciclos de 50C a 550C); CTM (ciclagem termomecânica) - as amostras receberam ciclagem termomecânica (100.000 ciclos de 50C a 550C). A seguir, foi realizado o teste de cisalhamento em uma máquina de ensaios universal (EMIC) a uma velocidade de 1mm/min com célula de carga de 100kg. Após o descolamento dos bráquetes, amostras de cada grupo foram submetidas à avaliação microscópica em microscópio eletrônico de varredura, a fim de analisar a superfície do esmalte e quantificar o Índice de Adesivo Remanescente (IAR) sobre a superfície. Os resultados mostraram que o grupo SEP apresentou maior resistência adesiva (14,70±4,85 MPa) quando comparado com o grupo XT (11,27±4,48 MPa). Para os grupos XT, a resistência adesiva manteve-se semelhante independente do tipo de ciclagem (SC, 11,44 MPa; CT, 11,20 MPa; CTM,11,19 MPa), enquanto que para os grupos SEP o subgrupo CTM foi o que apresentou maiores valores de resistência adesiva (16,84 MPa), seguido do CT (14,99 MPa) e SC (12,26 MPa). O teste ANOVA - 2 fatores revelou que o efeito interação não é estatisticamente significante; indicando, assim, que o efeito do tipo de ciclagem para o grupo XT é o mesmo ... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aim of this in vitro study was to evaluate the influence of thermal and thermomechanical cycling on shearbond strength of orthodontic brackets bonded with conventional and self-etching primers. 90 bovine incisors were randomly divided into 2 groups (G) according to the primer: XT (n=45) - brackets bonded with conventional primer (Transbond XT/3M, Unitek); SEP (n=45) - brackets bonded with self-etching primer (Transbond Plus SEP/3M, Unitek). After bonding, each group were divided into 3 subgroups (n=15): NC (no cycling) - the specimens did not receive any kind of cycling; TC (thermal cycling) - the specimens received only thermal cycling (500 cycles); TMC (thermomechanical cycling) - the specimens received thermomechanical cycling (100.000 cycles). Next, the shearbond strength test was performed in a universal testing machine (EMIC) at a crosshead speed of 1mm/min. After debonding, specimens of each group were submitted to microscopic evaluation in order to analyze the enamel surface, the adhesive penetration and quantify the Adhesive Remaining Index (ARI). The results showed that the SEP group presented higher bond strength (14,70±4,85 MPa) compared with XT (11,27±4,48 MPa). For XT, the bond strength remained similar despite cycling (NC, 11,44 MPa; TC, 11,20 MPa; TMC,11,19 MPa), meanwhile for SEP, the subgroup TMC showed higher values of bond strength (16,84 MPa), followed by TC (14,99 MPa) e NC (12,26 MPa). 2-way ANOVA test indicated that the interaction effect is not statistically different, so the kind of cycling effect for XT is equal for SEP. But the primer effect (XT vs SEP) is statiscally significant. According to the ARI , the group that presented the highest remaining adhesive on the enamel surface was SEP/TMC (ARI=3). The results showed that self-etching primers can be safely used in orthodontic practice because presents adequate values of bond strength ... (Complete abstract click electronic access below) / Mestre

Made available in DSpace on 2014-12-17T15:43:51Z (GMT). No. of bitstreams: 1 BeatrizAA_DISSERT_.pdf: 1031233 bytes, checksum: 81241c856d961aa9ae1b6fb199efa20a (MD5) Previous issue date: 2013-03-21 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / Tratamentos ortod?nticos s?o realizados na expectativa de melhorar a apar?ncia e fun??o mastigat?ria dos indiv?duos e geralmente s?o indicados por meio de crit?rios cl?nicos, n?o levando, algumas vezes, em considera??o a percep??o do indiv?duo. O objetivo desse estudo foi avaliar a rela??o entre as necessidades ortod?nticas tecnicamente definidas (crit?rios normativos) e a satisfa??o com a apar?ncia, mastiga??o e necessidade de tratamento percebida em um grupo de adolescentes. Foi realizado um estudo transversal com 215 alunos entre 15 e 19 anos foi realizado no Instituto Federal de Educa??o, Ci?ncia e Tecnologia (IFRN). Question?rio na forma de entrevista estruturada foi aplicado aos indiv?duos com perguntas a respeito da satisfa??o com a apar?ncia, satisfa??o com a mastiga??o e percep??o quanto ? necessidade de tratamento ortod?ntico. Um ?nico examinador, treinado e calibrado, coletou os dados normativos de necessidade de tratamento ortod?ntico atrav?s de crit?rios estabelecidos pelo ?ndice Dental Est?tico (DAI). Os resultados demostram que existe associa??o significativa entre o escore do DAI e a percep??o do participante quanto ? necessidade de tratamento ortod?ntico (p < 0,001), satisfa??o com a apar?ncia (p = 0,003) e satisfa??o com a mastiga??o (p = 0,047). Os alunos que possu?am necessidade normativa de tratamento se perceberam mais com problemas. Quando as caracter?sticas oclusais foram analisadas separadamente, uma maior quantidade de problemas estava associada ? necessidade percebida pelo paciente e ? satisfa??o com a apar?ncia, dentre eles o apinhamento, a irregularidade da maxila, a irregularidade da mand?bula e o trespasse maxilar acentuado (p< 0,05). Na an?lise com a satisfa??o com a mastiga??o, foi encontrada associa??o apenas com a mordida aberta (p= 0,003). Esses achados demostram uma tend?ncia dos indiv?duos de relacionar os problemas oclusais mais ? est?tica, tornando esse aspecto bastante relevante ao tratamento ortod?ntico

Orientador: Maurício Tatsuei Sakima / Banca: João Roberto Gonçalves / Banca: Cyneu Aguiar Pansani / Banca: Ana Cláudia Moreira Melo / Banca: Hélio Hissashi Terada / Resumo: Um estudo cefalométrico longitudinal e retrospectivo foi desenvolvido com o propósito de estudar diferentes métodos de sobreposições cefalométricas para a maxila e mandíbula. O método dos pontos cefalométricos (PC) para sobreposições parciais na maxila (BRONZI, 2002) e os métodos das estruturas anatômicas para sobreposições na maxila e mandíbula (SAKIMA et al., 2004) foram comparados o método dos implantes metálicos (padrão ouro) para verificar sua confiabilidade. Foram selecionadas telerradiografias em norma de 45 graus do lado esquerdo de 19 indivíduos, com faixa etária entre 6,7 anos e 10,2 anos. As radiografias foram tomadas em um mesmo aparelho de raios X, com um intervalo de tempo médio de 1 ano. O principal critério de inclusão era a presença de implantes metálicos em todas as telerradiografias. Análises intra-examinador e inter-examinadores foram realizadas para verificar a confiabilidade de diferentes examinadores nas mensurações realizadas na pesquisa. Foram verificadas as médias das diferenças das mudanças nas posições dentárias (coroa e raiz) da radiografia inicial para a final, em cada tipo de traçado cefalométrico quando comparado aos implantes metálicos nos métodos testados. Após análise estatística de Wilcoxon e verificação das médias e desvio padrão das medidas analisadas, é permitido sugerir sobreposições parciais na maxila em pontos cefalométricos e estruturas anatômicas para telerradiografias em norma de 45 graus. Para as sobreposições cefalométricas em estruturas anatômicas na mandíbula, poderiam ser sugeridas apenas no sentido horizontal, provavelmente pela dificuldade de marcação das estruturas anatômicas em algumas radiografias, principalmente o canal mandibular. As análises intra-examinador e inter-examinadores demonstraram uma boa confiabilidade dos métodos de sobreposições... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: A study longitudinal and retrospective cephalometric was developed with the purpose of studying different methods of maxillary and mandibular cephalometrics superimposition. The method of the cephalometric points (PC) for partial maxillary superimposition (BRONZI, 2002) and the methods of the anatomical structures for maxillary and mandibular cephalometrics superimposition (SAKIMA et al., 2004) they were compared the method of the metallic implants (golden standard) to verify his reliability. Forty-five degrees cephalometric radiographs of 19 persons, left side, aged between 6,7 years and 10,2 years were selected. The x-rays were taken in a same X ray device, with an interval of medium time 1 years old. The main inclusion criterion was the presence of metallic implants in all radiographs. Analyses intra-examiner and inter-examiners were accomplished to verify the different examiners' reliability in the mensurements accomplished in the research. The averages of the differences of the changes in the dental positions (it crowns and root) were verified of the initial x-ray for to final, in each type of cephalometric tracing when compared to the metallic implants in the tested methods. After statistical analysis of Wilcoxon and verification of the averages and standard deviation of the analyzed measures, it is allowed to suggest partial superimposition maxillary in the points cephalometrics and anatomical structures for 45º cephalometric radiography. For the mandibular superimposition in anatomical structures, they could just be suggested in the horizontal reference, probably for the difficulty of demarcation of the anatomical structures in some x-rays, mainly the mandibular canal. The analyses intra-examiner and inter-examiners demonstrated a good reliability for the methods of cephalometric superimposition, with results inferior for the method of mandibular cephalometric superimposition in anatomical structures. / Doutor