Made available in DSpace on 2015-04-14T13:29:45Z (GMT). No. of bitstreams: 1 425713.pdf: 1781396 bytes, checksum: 7eeb594432bb477d3935d002b3c3bfbb (MD5) Previous issue date: 2009-03-18 / O objetivo deste estudo in vitro foi avaliar a resist?ncia de uni?o entre infraestrutura de zirc?nia e cer?mica de cobertura de um sistema livre de metal comparado com um sistema metalo-cer?mico. Para isso, foram confeccionados 40 blocos de zirc?nia (Procera Zirconia), onde 32 n?o possu?am cor e 8 possu?am cor A2) e 8 blocos met?licos (liga Viron 99), todos nas dimens?es (10 x 10 x 2 mm). As amostras de zirc?nia foram divididas em 5 grupos (8 em cada), e receberam diferentes tratamentos: Grupo 1 (zirc?nia s/ cor): aplica??o da dentina; Grupo 2 (zirc?nia c/ cor): aplica??o da dentina; Grupo 3 (zirc?nia s/ cor): aplica??o do liner + dentina; Grupo 4 (zirc?nia s/ cor): aplica??o do liner + dentina na superf?cie interna; Grupo 5 (zirc?nia s/ cor): desgaste com broca diamantada + liner + dentina. Como Grupo Controle: metalo-cer?mica (viron 99 + IPS Dsign dentina A2). Ap?s sinteriza??o das cer?micas de acordo com o fabricante, as amostras foram submetidas ao teste de resist?ncia ao cisalhamento realizados em m?quina de ensaios EMIC DL 2000, onde os resultados foram obtidos em MPa. Atrav?s de fotografias e de MEV com magnitude de 37X, 200X e 2000X foi verificado o tipo de falha que ocorreu na interface infra-estrutura e cer?mica de cobertura. Ao submeter os resultados ao teste ANOVA, foi poss?vel observar que houve diferen?as estatisticamente significantes entre os grupos (p=0,000). De acordo com teste de Tukey, o grupo controle obteve os maiores valores de resist?ncia de uni?o, estatisticamente diferente (p<0,05) aos demais grupos de zirc?nia. Os grupos de zirc?nia n?o apresentaram diferen?a estat?stica entre si (p>0,05). O grupo 2 apresentou a maior m?dia entre os grupos de zirc?nia e o grupo 4 apresentou a menor m?dia de todos os grupos testados. As falhas encontradas na interface foram 100% mistas em todas amostras e apenas 1 amostra do grupo 2 constatou-se falhas coesivas na infra-estrutura de zirc?nia. Concluiu-se que o grupo controle mostrou uma resist?ncia de uni?o aproximadamente 50% maior que todos os grupos de zirc?nia testados.

Made available in DSpace on 2015-04-14T13:29:49Z (GMT). No. of bitstreams: 1 428173.pdf: 3267525 bytes, checksum: 111e79e4715696d409dab4a83d48e6c0 (MD5) Previous issue date: 2010-12-15 / OBJETIVO: Avaliar as altera??es histol?gicas ?sseas superficiais ap?s a inser??o de miniplacas e parafusos com diferentes composi??es met?licas. MATERIAL E METODOS: Dezoito ratos, da linhagem Wistar, foram utilizados. Uma miniplaca e dois parafusos foram inseridos na superf?cie externa do f?mur direito de cada animal. Todos os parafusos foram de 5,0 mm de comprimento e foram inseridos at? as pontas serem projetadas pelo lado endosteal. Os animais foram divididos em tr?s grupos com seis animais cada. Nos primeiros seis animais foram colocados uma placa e dois parafusos de tit?nio, em outros seis animais foram colocados uma placa de tit?nio e dois parafusos de a?o inoxid?vel, e nos animais restantes foram colocados placa e parafuso revestido com Diamond-Like Carbon (DLC). Ap?s 30 dias da realiza??o do procedimento cir?rgico, as miniplacas e os parafusos foram retirados e foram feitas avalia??es histol?gicas na interface placa parafuso no defeito ?sseo, em uma extens?o de 0,5 cm2. RESULTADOS: Na avalia??o histol?gica observou-se um maior processo inflamat?rio no grupo com diferentes composi??es met?licas (Grupo tit?nio-a?o)(p=0,204), como tamb?m uma maior presen?a de lacunas de Howship que indicam uma poss?vel oste?lise em decorr?ncia de um ?nicio de corros?o galv?nica entre o tit?nio e o a?o inoxid?vel (p=0.002). CONCLUS?ES: Os resultados deste estudo indicam que, quando usamos diferentes materiais com diferentes composi??es met?licas, os componentes de implantes de a?o inoxid?vel quando em associa??o com o tit?nio t?m uma maior suscetibilidade ? provocar oste?lise do que quando se utilizam os mesmos componentes como materiais de fixa??o.

Made available in DSpace on 2015-04-14T13:29:51Z (GMT). No. of bitstreams: 1 429330.pdf: 4876127 bytes, checksum: 03e0c09981d2813cd511c4f745b49744 (MD5) Previous issue date: 2011-01-17 / O objetivo desse estudo foi avaliar a interface e a resist?ncia de uni?o de cimentos resinosos autoadesivos ? dentina condicionada com ?cido poliacr?lico a 11,5%. Cinquenta e seis dentes, terceiros molares, foram divididos aleatoriamente em 7 grupos (n=24/grupo): G1 (controle) - Rely X ARC; G2 - RelyX Unicem; G3 - Maxcem Elite; G4 - Set; G5 - ?cido poliacr?lico + Rely X Unicem; G6 - ?cido poliacr?lico + Maxcem Elite; G7 - ?cido poliacr?lico + Set. Blocos de resina composta foram cimentados sobre dentina plana com carga de 1Kg por 2 minutos, seguido de fotoativa??o. Ap?s armazenagem em ?gua destilada a 37? C por 24 horas, seis conjuntos dente/resina foram cortados, paralelamente ao longo eixo do dente, nos sentidos x e y, com sec??o de aproximadamente 0,8 mm2. Foram obtidos 24 corpos de prova para cada grupo, sendo ent?o submetidos ao teste de resist?ncia ? microtra??o (RZt) em m?quina de ensaio universal com velocidade de 0,5 mm/min. Dois conjuntos de cada grupo foram seccionados no sentido m?sio-distal, no centro de suas coroas, com um disco diamantado de dupla face. As superf?cies foram polidas com lixas de carbeto de sil?cio 400, 600 e 1200, seguido de polimento com pastas dimantadas de granula??o 6, 3, 1 e ? &#956;m. As amostras foram desmineralizadas, desproteinizadas, secadas, metalizadas e observadas em microsc?pio eletr?nico de varredura em aumento de 4.000 vezes. De acordo com An?lise de Vari?ncia e teste de Tukey (a=0,05), a m?dia de RZt do RelyX ARC (24,19 MPa) e do RelyX Unicem associado ao ?cido poliacr?lico (23,12 MPa) n?o diferiram estatisticamente entre si e foram superiores aos outros grupos (p<0,05). A m?dia de RZt do Maxcem Elite associado ao ?cido poliacr?lico (13,09 MPa) foi, estatisticamente, superior ao Maxcem Elite sem ?cido poliacr?lico (8,14 MPa). O RelyX Unicem sem ?cido poliacr?lico (10,23 MPa) n?o diferiu, estatisticamente, do Maxcem Elite sem e com ?cido poliacr?lico. Todos os corpos de prova do Set foram perdidos durante o procedimento de corte. Para os cimentos resinosos autoadesivos n?o foi observada forma??o de camada h?brida, havendo a forma??o de tags de resina para o RelyX Unicem e Maxem Elite quando associados ao ?cido poliacr?lico. O pr?-tratamento com ?cido poliacr?lico a 11,5% foi efetivo para a uni?o do RelyX Unicem e Maxcem Elite ? dentina.

Made available in DSpace on 2015-04-14T13:29:52Z (GMT). No. of bitstreams: 1 430369.pdf: 669885 bytes, checksum: 002b0553e91e6ef0df52888b901e3907 (MD5) Previous issue date: 2010-12-28 / O objetivo deste estudo ? determinar em c?es, a influ?ncia dos tratamentos de superf?cie atrav?s de jateamento com biocer?micas nos per?odos iniciais de osseointegra??o. Quarenta e oito implantes (Ti-6Al-4V) tratados com jateamento com biocer?mica seguido de ataque ?cido (RBMa), jateamento com alumina e ataque ?cido (AB/AE) usado como controle, jateamento com alumina e ataque ?cido com subsequente jateamento com biocer?mica e ataque ?cido (AB/AE + RBMa). Tr?s implantes de cada grupo foram destinados a caracteriza??o f?sico/qu?mica por microscopia eletr?nica de varredura (SEM), microscopia de for?a at?mica (AFM) e Espectroscopia Fotoel?trica de Raios X (XPS). O estudo animal compreendeu a coloca??o de 48 implantes na por??o proximal da t?bia (8 c?es, 16 por superf?cie, 6 por c?o) os quais permaneceram por 2 semanas in vivo. Ap?s a eutan?sia, metade dos esp?cimes foram destinados ao teste de torque de remo??o e a outra metade foram processadas para obten?ao de l?minas n?o descalcificadas de aproximadamente 30&#956;m de espessura onde foram realizadas an?lises histomorfol?gica e histomorfom?trica de contato osso/implante (%BIC) e fra??o arial de osso formado (BAFO). O teste GLM ANOVA com 95% de signific?ncia foi utilizados para an?lise estat?stica com post-hoc de Dunn. A AFM demonstrou valores de rugosidade (Sa e Sq) significante maiores do grupo AB/AE em rela??o aos grupos RBMa e AB/AE + RBMa. O XPS demonstrou presen?a de Ti, Al, O, C, N, Ca e P para os grupos RBMa e AB/AE + RBMa, os mesmos elementos foram em contrados no grupo AB/AE, juntamente com o V, exceto Ca e P. N?o foram encontradas diferen?as estet?sticas para %COI e BAFO. Todos os grupos demonstraram bicompatibilidade com osso imaturo observado em ?ntimo contato com as superficies.

Made available in DSpace on 2015-04-14T13:29:54Z (GMT). No. of bitstreams: 1 431091.pdf: 6484611 bytes, checksum: ee0b40e71498d6a5f8496211522ca10f (MD5) Previous issue date: 2011-03-18 / O objetivo desse estudo foi avaliar a influ?ncia de quatro cimentos resinosos (um convencional e tr?s autoadesivos) na deflex?o de c?spides, carga de fratura e tipos de fratura de pr?-molares com acesso endod?ntico e restaurados com inlays em resina composta. Setenta e dois primeiros pr?-molares foram divididos aleatoriamente em seis grupos (n=12): G1 (controle) - h?gidos; G2 cavidades sem restaura??o; G3 RelyX ARC; G4 RelyX U100; G5- Maxcem Elite; G6 SeT. Os Grupos 2-6 receberam preparos cavit?rios MOD e acesso endod?ntico. Os grupos 3-6 foram moldados com silicona por adi??o e vazados com gesso especial para confec??o de inlays em resina composta Z350 XT. As restaura??es indiretas foram cimentadas nas respectivas cavidades com carga de 1 Kg e fotoativadas. Ap?s armazenagem em ?gua destilada a 37? C por 72 horas, carga de 200 N foi aplicada na regi?o oclusal com uma esfera de 8 mm de di?metro acoplada na m?quina de ensaio universal EMIC DL 2000, sendo medida a deflex?o de c?spides com um micr?metro digital. Os corpos de prova foram ent?o submetidos a 500.000 ciclos de fadiga mec?nica, e novo teste de deflex?o de c?spides foi realizado. Em seguida, os corpos de prova foram submetidos ao ensaio de compress?o at? a fratura na m?quina de ensaio universal. De acordo com o teste de Kruskal-Wallis, a maior deflex?o de c?spides pr?-fadiga foi obtida para o grupo 2 (69 &#956;m), n?o diferindo estatisticamente do grupo 6 (51 &#956;m). As menores deflex?es de c?spides foram obtidas para o grupo 1 (4 &#956;m), o grupo 3 (4 &#956;m) e o grupo 4 (5 &#956;m), os quais n?o diferiram estatisticamente entre si. Valor intermedi?rio foi obtido para o grupo 5 (21 &#956;m), n?o diferindo estatisticamente dos grupos 3, 4 e 6. De acordo com o teste de Wilcoxon, n?o houve diferen?a estat?stica entre a deflex?o de c?spides pr? e p?s-fadiga apenas para o grupo 3 (p=0,015). De acordo com Kruskal-Wallis, a maior carga de fratura foi obtida para o grupo 1 (1902 N), diferindo estatisticamente dos outros grupos. Segundo maior valor foi obtido para o grupo 3 (980,8 N), diferindo estatisticamente dos outros grupos. Grupo 4 (670,6 N), grupo 5 (533,5 N), grupo 6 (601,3 N) e grupo 2 (526,6 N) n?o diferiram estatisticamente entre si. Para os grupos restaurados, houve predomin?ncia de fraturas recuper?veis. Inlays em resina composta cimentadas com RelyX ARC mantiveram a estabilidade da deflex?o de c?spides, proporcionaram maior recupera??o da resist?ncia da estrutura dent?ria, assim como fraturas mais favor?veis para a reabilita??o.

Made available in DSpace on 2015-04-14T13:30:03Z (GMT). No. of bitstreams: 1 435410.pdf: 1188993 bytes, checksum: 90ccf493a5d3ef81edc737607cc0bec3 (MD5) Previous issue date: 2011-11-28 / Apical surgery is a procedure involving surgical exposure of the committed apex, amputation of the same, root-end cavity preparation and retrofilling of the root canal. The success of this surgery is associated with the proper performance of the various steps of all surgical procedures. This study aimed to compare results of apical surgery in vitro, using different restorative materials and two different storage modes of human teeth. The sample consisted of 60 single root human teeth witch were divided into two groups according to the storage mode (hydrated and not hydrated), each group was subdivided according to the retrofilling material (mineral trioxide aggregate and glass ionomer cement modified by resin). Each specimen was evaluated by digital radiographic images and scanning electron microscopy (SEM). It was concluded that mineral trioxide aggregate (MTA ?) obtained the best results for the apical seal in both mores of storage and that the glass ionomer cement modified by resin (Vitremer ?) showed significantly increased gap values when the teeth were hydrated. / A cirurgia paraendod?ntica ? um procedimento que inclui exposi??o cir?rgica do ?pice comprometido, amputa??o do mesmo, preparo cavit?rio e retrobtura??o do canal radicular. O sucesso desta cirurgia est? vinculado ? realiza??o adequada das diversas etapas desse procedimento cir?rgico. Esta pesquisa objetivou comparar resultados de cirurgia paraendod?ntica, in vitro, utilizando diferentes materiais restauradores e modos de armazenamento de dentes humanos. A amostra foi constitu?da por 60 dentes humanos monorradiculares divididos em dois grupos segundo o modo de armazenamento (hidratados e n?o hidratados), sendo que cada grupo foi subdividido de acordo com o material utilizado para retrobtura??o (o agregado tri?xido mineral e o cimento de ion?mero de vidro modificado por resina). Cada esp?cime foi avaliado por imagens radiogr?ficas digitais e Microscopia Eletr?nica de Varredura (MEV). Concluiu-se que o agregado tri?xido mineral (MTA?) obteve os melhores resultados para o selamento apical em ambas as formas de armazenamento dent?rio e que o cimento de ion?mero de vidro modificado por resina (Vitremer?) apresentou valores m?dios de gap consideravelmente aumentados quando utilizados dentes hidratados.

Made available in DSpace on 2015-04-14T13:30:10Z (GMT). No. of bitstreams: 1 438178.pdf: 2149932 bytes, checksum: 72e349d1108a96e32586f332a6db74c4 (MD5) Previous issue date: 2012-03-26 / This study evaluated different loads during the cementation on the microtensile bond strength of conventional and self-adhesive resin cement. Fortytwo extracted caries-free molars were selected. Flat coronal dentin surfaces were exposed until the removal of enamel. The selected teeth were embedded in autopolymerized acrylic resin. Composite resin discs (Filtek Z 350 XT, 3M ESPE) were made according to the manufacturer?s instructions. Luting procedures with Rely X ARC - Group 1 (3M ESPE) were made with etched with 37% phosphoric acid gel, rinsed with water and the excess dentin moisture was removed and were applied two consecutive coats of the adhesive (Adper Single Bond 2) and light cured with halogen light (3M ESPE). Immediately the cement was manipulated according to the manufacturer s instructions and the composite discs were placed under 10N, 30N or 60N static load for 2 minutes. Specimens were light cured for a total of 160 seconds. Luting procedures with Rely X U100 (3M ESPE) - self-adhesive resin cement - Group 2 were made with moist dentin, the cement was manipulated according to the manufacturer s instructions, following the same protocol of the luting procedures of conventional resin cement. The bonded specimens were stored in water at 37?C for 24 hours. The restorations were embedded in autopolymerized acrylic resin and then longitudinally sectioned in the x and y directions perpendicular to the bonded interface to produce rectangular bonded sticks. Specimens (n=15) were divided according to cement and the load. The microtensile bond strength was conducted on a mechanical testing machine EMIC DL-2000. In order to evaluate the hybrid layer, two teeth of each group were cut perpendicular to the bonding interface, exposing the middle of the teeth. The surfaces were flatted and followed by polished and a dehydration process. Specimens were sputter coated with gold and examined with a scanning electron microscope (SEM) at a x1000 to a x4000 magnification. Data were subjected to Analysis of Variance and Tukey s test (p<0.05). The load of 30 N showed the best mean of the microtensile bond strength of the both groups (17,27 ? 5,33 MPa to group 1 and 15,33 ? 2,75 MPa to group 2). The load of 10 N of group 2 showed intermediary values (9,47 ? 4,07 MPa) followed by load of 10N (9,36 ? 5,08 MPa) and 60N of group 1 (7,84 ? 2,49 MPa). The load of 60N of group 2 resulted in the lowest values (7,34 ? 2,64 MPa). The mode of failure was determined using SEM and the mixed failure werer predominant in all groups. The results suggest that different load during the luting procedures can interfere on the bond strength of resin cements. / Este trabalho avaliou a influ?ncia de diferentes cargas de cimenta??o na resist?ncia de uni?o de cimento resinoso convencional e autoadesivo. Para isso, foram selecionados 42 molares humanos h?gidos. Os dentes foram desgastados em politriz at? a remo??o de esmalte. Os dentes tiveram suas ra?zes embutidas em resina acr?lica autopolimeriz?vel. Foram confeccionadas pastilhas de resina composta (Filtek Z 350 XT, 3M ESPE), conforme as orienta??es do fabricante. Para cimenta??o com cimento resinoso convencional Rely X ARC (3M ESPE) Grupo 1 foi realizado condicionamento ?cido da superf?cie (?cido fosf?rico 37%), lavagem, secagem com algod?o, aplica??o de duas camadas de adesivo (Adper Single Bond 2) e fotoativa??o atrav?s de um fotopolimerizador de luz hal?gena, seguido da manipula??o e da aplica??o do cimento, conforme orienta??es do fabricante. J? a cimenta??o com o cimento resinoso autoadesivo RelyX U100 (3M ESPE) Grupo 2 foi feita em dentina ?mida, manipula??o e aplica??o do cimento de acordo com orienta??es do fabricante. Em ambos os grupos, o bloco de resina composta foi posicionado sobre o cimento com carga de 10 N, 30 N e 60 N pelo tempo de dois minutos e fotoativado pelo tempo de 160 segundos (3M ESPE). As amostras foram armazenadas por 24 horas em 100% de umidade a 37?C. As restaura??es foram inclu?das com resina acr?lica autopolimeriz?vel e submetidas a cortes seriados, obtendo-se o formato de prismas. Os esp?cimes (n=15 para cada carga) ficaram divididos conforme o cimento e a carga utilizados. Ap?s, foram submetidos ao teste de resist?ncia de uni?o a microtra??o na m?quina de ensaios universal EMIC DL-2000. Al?m disso, dois conjuntos de cada grupo foram seccionados no sentido m?sio-distal, com um disco diamantado de dupla face. As superf?cies foram polidas com lixas de carbeto de sil?cio, seguido de polimento com pastas diamantadas. As amostras foram desmineralizadas, desproteinizadas, secadas, metalizadas e observadas em microsc?pio eletr?nico de varredura em aumento de 1.000 a 4.000 vezes. Os resultados foram submetidos ? An?lise de Vari?ncia e ao teste de Tukey HSD. A carga de 30N apresentou o maior valor de resist?ncia de uni?o em ambos os grupos, sendo 17,27 ? 5.33 MPa no Grupo 2 (dois) e 15,33 ? 2.75 MPa no Grupo 1 (um). J? a carga de 10 N apresentou valores intermedi?ri?rios de resist?ncia de uni?o, sendo (9,47 ? 4.07 MPa) para o Grupo 2 (dois) e (9,36 ? 5.08) para o Grupo 1 (um). A carga de 60 N foi a que apresentou menores valores de resist?ncia de uni?o (9,47 ? 2.64 MPa) para o Grupo 2 (dois) e (9,36 ? 2.49) para o Grupo 1 (um). Houve diferen?a estat?stica entre a carga de 30 N do Grupo 2 (dois) e a carga de 60 N do Grupo 1 (um) e tamb?m entre a carga de 30 N do Grupo 2(dois) com a carga de 60 N do Grupo 2 (dois). O tipo de fratura foi analisado atrav?s de imagens obtidas em MEV e a falha do tipo mista foi predominante em ambos os grupos e cargas. Os resultados sugerem que diferentes cargas de cimenta??o podem interferir na resist?ncia de uni?o do cimento resinoso RelyX ARC e Rely X U100.

Made available in DSpace on 2015-04-14T13:30:27Z (GMT). No. of bitstreams: 1 451617.pdf: 638194 bytes, checksum: f2470bb81322e6a32a3d10b371e1182b (MD5) Previous issue date: 2013-08-29 / Objective: To evaluate the histological changes of bone surface after insertion of mini-plates and screws in the bone surface. Material and methods: Eighteen rats of Wistar strain were used, a plate and two screws were inserted in the external cortex of the femur of each animal. The animals were divided into three groups of six animals each, after thirty days of completion of the procedure the implanted material was removed cirurgiacamente after euthanasia of animals, and the bone surface ready to be removed and analyzed histologically. Results: Histological evaluation after marking immunohistochemistry, Group 3, with different materials, showed an increased inflammatory infiltrate in uperf?cie area analyzed, which indicated a possible area of osteolysis. Groups 1 and 2 showed no statistically significant differences showing an increase of the standard normal reparative inflammation. Conclusions: The results of study indicated that the use of different materials increase the chance of encountering large areas of osteolysis in the bone surface in contact with these materials. / Objetivo: Avaliar as altera??es histol?gicas da superf?cie ?ssea ap?s a inser??o de miniplacas e parafusos na superf?cie ?ssea. Materiais e m?todos: Dezoito ratos, da linhagem Wistar, foram utilizados; Uma placa e dois parafusos de fixa??o foram inseridos na cortical externa do f?mur de cada animal. Os animais foram divididos em tr?s grupos de seis animais cada, ap?s trinta dias da realiza??o do procedimento o material implantado foi removido cirurgicamente ap?s a eutan?sia dos animais, e a superf?cie ?ssea removida e preparada para ser analisadas histologicamente. Resultados: Na avalia??o histol?gica, ap?s a marca??o imunohistoqu?mica, O grupo 3, com diferentes materiais, apresentou um aumento do infiltrado inflamat?rio na superf?cie de ?rea analisada, que indicou uma poss?vel oste?lise da regi?o. Os grupos 1 e 2 n?o apresentaram diferen?as estat?sticas significantes que demonstrassem um aumento do padr?o normal de inflama??o reparativa. Conclus?es: Os resultados do trabalho indicam que o uso de diferentes materiais aumentam a possibilidade de ocorrer ?reas de oste?lise na superf?cie ?ssea em contato com esses materiais.

Made available in DSpace on 2015-04-14T13:30:34Z (GMT). No. of bitstreams: 1 459061.pdf: 2282963 bytes, checksum: c9b1fec421065d44d34540a0b1217b0a (MD5) Previous issue date: 2014-02-24 / The aim of this study was to evaluate the bond strength of Scotchbond Universal to dentin in both total-etch and self-etch applications after storage in water for 24 h and 6 months. The occlusal surface of 24 third molars was removed to obtain flat dentin surfaces, and the teeth were divided into four groups (n=6/grupo): G1 total-etch application of Scotchbond Universal; G2 self-etch application of Scotchbond Universal; G3 Scotchbond Multi Purpose (total-etch application control); G4 Clearfil SE Bond (self-etch application control). Following the adhesive application, a 6 mm height block of composite resin Z250 was built on the adhesive area. After storage in distilled water at 37?C for 24 hours, the tooth/resin sets were cut parallel to the long axis of the tooth, in the x and y directions, with a section of about 0.8 mm2. Forty specimens were obtained for each group; 20 specimens were immediately submitted to microtensile bond strength test, and the others after storage in distilled water at 37o C for 6 months. The microtensile bond strength test was performed in an universal testing machine (EMIC-DL 2000) at 0.5 mm/min crosshead speed. The failures were observed in scanning electron microscopy (SEM). Additionally, two sets of each group were sectioned mesio-distal in the center of their crown with a diamond blade. The surfaces were polished by wet sanding with 400, 600 and 1200-grit silicon carbide abrasive paper, followed by polishing with 6, 3, 1 and ? &#61549;m diamond paste. The samples were demineralized, deproteinized, dried, metalized and observed on a scanning electron microscope at 1.500x. The bond strength means (MPa) obtained were the following: 24 h G1 (39.37); G2 (31.02); G3 (35.09); G4 (35.84); 6 months G1 (36.99); G2 (40.58); G3 (32.44); G4 (41.75). According to two-way ANOVA, there was no significance for adhesive system (p=0,110) and storage time (0,108), but the interaction of adhesive system and storage time was significant (p=0.015). At 24 h, there was no statistical difference in bond strength between the adhesive systems (p>0,05). At 6 months, there was statistical difference between the adhesive systems (p<0.05). Clearfil SE Bond obtained the higher bond strength mean, not differing statistically from self-etch application of Scotchbond Universal. Total-etch application of Scotchbond Universal did not differ statistically from Scotchbond Multi Purpose. Most of failures were mixed in both periods of evaluation. The SEM images of the adhesive interface of Scotchbond Universal total-etch application and Scotchbond Multi Purpose showed thicker hybrid layers and more resin tags in comparison with Scotchbond Universal self-etch application and Clearfil SE Bond. It was concluded that the simplification of Scotchbond Universal in one bottle did not decrease the bond strength of this adhesive to dentin during 6 months of storage. / O objetivo do estudo foi avaliar a resist?ncia de uni?o ? dentina do sistema adesivo Scotchbond Universal na vers?o total-etch e self-etch em 24 horas e 6 meses de armazenamento. A superf?cie oclusal de 24 dentes terceiros molares h?gidos foi removida para obter superf?cie plana em dentina, sendo divididos aleatoriamente em quatro grupos (n=6/grupo): G1 - Scotchbond Universal na vers?o total-etch; G2 Scotchbond Universal na vers?o self-etch; G3 Scotchbond Multi Purpose (controle da vers?o total-etch); G4 Clearfil SE Bond (controle da vers?o self-etch). Sobre o sistema adesivo foi confeccionado um bloco de 6 mm de altura em resina composta Z250. Ap?s 24 horas de armazenagem em ?gua destilada a 37? C, os conjuntos dente/resina foram cortados paralelamente no longo eixo do dente, nos sentidos x e y, com sec??o de aproximadamente 0,8 mm2. Quarenta corpos de prova foram obtidos para cada grupo, sendo 20 submetidos imediatamente ao teste de resist?ncia ? microtra??o e, os outros 20, ap?s 6 meses de armazenamento em ?gua destilada a 37? C. O ensaio de microtra??o foi realizado em uma m?quina de ensaio universal EMIC DL-2000, com uma velocidade de 0,5 mm/min. Os tipos de falha foram observados em microscopia eletr?nica de varredura (MEV). Adicionalmente, dois conjuntos dente/resina foram preparados e seccionados no sentido m?sio-distal, no centro de suas coroas, com um disco diamantado de dupla face. As superf?cies foram polidas com lixas de carbeto de sil?cio 400, 600 e 1200, seguido de polimento com pastas diamantadas de granula??o 6, 3, 1 e ? &#61549;m. As amostras foram desmineralizadas, desproteinizadas, secadas, metalizadas e observadas em MEV em aumento de 1.500 vezes. No teste de microtra??o as m?dias obtidas (MPa) foram as seguintes: 24 h G1 (39,37); G2 (31,02); G3 (35,09); G4 (35,84); 6 meses G1 (36,99); G2 (40,58); G3 (32,44); G4 (41,75). De acordo com o teste ANOVA de duas vias n?o houve signific?ncia para o sistema adesivo (p=0,110) e para o tempo (0,108), mas apenas para a intera??o entre sistema adesivo e tempo (p=0,015). No per?odo de 24 horas, n?o houve diferen?a estat?stica significativa na resist?ncia ? microtra??o entre os sistemas adesivos (p>0,05). Na avalia??o de seis meses de armazenamento, houve diferen?a estat?stica entre os sistemas adesivos (p<0,05). O Clearfil SE Bond apresentou o maior valor m?dio de resist?ncia ? microtra??o, n?o diferindo estatisticamente do Scotchbond Universal self-etch e total-etch. O Scotchbond Universal total-etch n?o diferiu estatisticamente do Scotchbond Multi Purpose. Os tipos de falha foram predominantemente mistas para os dois per?odos de avalia??o. A interface adesiva do Scotchbond Universal na vers?o total-etch e o Scotchbond Multi Purpose apresentaram camada h?brida mais espessa e mais tags de resina em compara??o ao Scotchbond Universal na vers?o self-etch e Clearfil SE Bond. Concluiu-se que a simplifica??o em frasco ?nico do Scotchbond Universal n?o causou diminui??o nos valores de resist?ncia de uni?o deste material ? dentina em at? 6 meses de avalia??o.

Made available in DSpace on 2015-04-14T13:29:14Z (GMT). No. of bitstreams: 1 398805.pdf: 15997187 bytes, checksum: 0a7222ba3043d12a0e6af43149f8c843 (MD5) Previous issue date: 2007-12-07 / O presente estudo teve por objetivo investigar macroscopicamente e microscopicamente o processo do reparo ?sseo no local da fratura mandibular em coelhos da linhagem Nova Zel?ndia, com aten??o ?s miniplacas e aos parafusos de tit?nio (Neoortho?), empregados como material de fixa??o, em diferentes per?odos de tempo. Para a amostra foram selecionados 18 coelhos machos da linhagem Nova Zel?ndia, com peso at? 4000 gramas, distribu?dos aleatoriamente em tr?s grupos, de acordo com o per?odo de tempo de observa??o dos animais. Foram efetuadas osteotomias unilaterais em regi?o de ?ngulo mandibular, fixadas por uma miniplaca e quatro parafusos de tit?nio. Os animais foram mortos aos 30, 60 e 90 dias. Os resultados obtidos demonstram que, macroscopicamente, o sistema se fixa??o foi capaz de manter os segmentos ?sseos na posi??o desejada, sem propiciar complica??es como processos infecciosos ou pigmenta??o aos tecidos moles adjacentes. Histologicamente pode-se afirmar que o calo fibroso esteja estabelecido aos 30 dias e o calo ?sseo aos 60 dias. O col?geno tipo I, maduro, ? predominante na linha de reparo da fratura ?ssea, especialmente ao per?odo de 60 dias, entretanto a densidade do col?geno tipo II ? maior. Em torno das perfura??es estes ?nices mantem-se proporcionais. O tit?nio induz ao intenso crescimento ?sseo aposicional, sem apresentar potencial de dissolu??o nos tecidos adjacentes, ou complica??es que indiquem sua remo??o. Os ?ndices de c?lcio pouco variados entre os per?odos de tempo sugerem que estabelecido o reparo da fratura, o calo ?sseo seja composto por osso corticalizado, de densidade mineral padr?o. O sistema por placas e parafusos de tit?nio se mostrou eficaz para o tratamento das fraturas de ?ngulo mandibular.