Orientador: Celia Marisa Rizzatti Barbosa / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-05T02:25:21Z (GMT). No. of bitstreams: 1 Joia_FabioAlves_M.pdf: 5977969 bytes, checksum: e66707336fade444f0c8a18dedfa11c1 (MD5) Previous issue date: 2005 / Resumo: O presente estudo avaliou a movimentação dental linear em prótese total superior e inferior em função de diferentes técnicas de inclusão. Quarenta pares do conjunto modelo-base de prova em cera, com os dentes artificiais montados, das arcadas superior e inferior, foram distribuídos ao acaso em quatro grupos de 10 pares cada, recebendo os seguintes tratamentos: Grupo A ¿ Inclusão em mufla monomaxilar de Cloreto de Polivinila (PVC) com muralha de gesso Tipo III; Grupo B ¿ Inclusão em mufla de PVC bimaxilar com muralha de silicone para laboratório, sem retenção nos dentes artificiais; Grupo C ¿ Inclusão em mufla de PVC bimaxilar com muralha de gesso Tipo III; Grupo D ¿ Inclusão em mufla de PVC bimaxilar com muralha de silicone para laboratório, com retenção nos dentes artificiais. Nos quatro grupos a resina acrílica utilizada na polimerização das próteses foi a resina termicamente ativada por energia de microondas, sendo o ciclo de polimerização realizado com um tempo de 20 minutos a 20% da potência, mais um ciclo de 5 minutos a 60% da potência do forno de microondas de 960 W de potência máxima, sem intervalo entre os ciclos. Sete distâncias em arco, duas distâncias diagonais e três distâncias transversais foram mensuradas, por um único avaliador, antes da inclusão e após a polimerização da base, com auxílio do microscópio mensurador linear (Olympus STM), com precisão de 0,0005 milímetro. Os dados obtidos foram submetidos à análise estatística pelo método não paramétrico de Kruskal-Wallis (p<0,05) e pelas comparações múltiplas pelo método de Dunn. A análise demonstrou diferenças estatisticamente significantes para três medidas em arco, as duas distâncias diagonais e as três distâncias transversais, entre o grupo de inclusão monomaxilar (A) e pelo menos um grupo de inclusão bimaxilar (B, C ou D), sendo os menores valores de alterações dentais lineares encontrados, em sua maioria, nos grupos de inclusão bimaxilar com muralha de silicone (B e D). Diante das condições experimentais presentes, foi possível concluir que o método de inclusão bimaxilar é mais viável quando associado ao uso da muralha de silicone com ou sem retenções nos dentes artificiais, em relação à inclusão monomaxilar / Abstract: The present study evaluated linear dental movement in maxillary and mandibular complete denture using different flasking technics. Forty pairs of the joint model-wax base, of maxillary and mandibular arches, with mounted artificial teeth, had been randomized distributed into four groups of 10 pairs each, receiving the following treatments: GA: invested in conventional flask, in a total gypsum environment; GB: invested in special flask for simultaneous polymerization using silicone and gypsum base; GC: invested in special flask for simultaneous polymerization of maxillary and mandibular prostheses in a total gypsum environment; GD: invested in special flask for simultaneous polymerization using silicone, gypsum base, and retentions on artificial teeth. The prostheses were processed with heat-polymerized acrylic resin for microwaves energy polymerization, during 20 minutes at 20% of the power, plus an additional cycle of 5 minutes at 60% of the power, of a microwave oven of 960W maximum power, without interval between the cycles. Seven arch distances, two diagonal distances and three transversal distances had been measured, by an only appraiser, before flasking and after processing, with aid of a measuring microscope (Olympus, model STM), with 0.0005 millimeter precision. Data had been statistically analyzed by Kruskal-Wallis test (p<0.05) and Dunn test. It demonstrated statistically significant differences in three arch distances, two diagonal distances and three transversal distances, between group A (conventional flask) and at least one group of bimaxilar flask (B, C or D), with the lesser values of linear dental alterations been found, in its majority, at bimaxilar flask with silicone and gypsum base groups (B and D). Ahead of the experimental conditions gifts, it was possible to conclude that bimaxilar flasking method is more viable when associate to the use of the silicone and gypsum base with or without retention in artificial teeth, when compared with conventional flasking procedure / Mestrado / Protese Dental / Mestre em Clínica Odontológica

Orientador: Celia Marisa Rizzatti-Barbosa / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-22T22:45:14Z (GMT). No. of bitstreams: 1 Pitta_MariaSuzanaSchmidt_M.pdf: 3666397 bytes, checksum: 33e4befacc233ce608c609e61a4a6fc8 (MD5) Previous issue date: 1997 / Resumo: Em Prótese Dental, as técnicas para polimerizar resinas acrílicas tem sido melhoradas com o objetivo de minimizar as distorções que ocorrem durante as diversas fases do processamento. e que podem causar alterações nas próteses totais e/ou removíveis, com conseqüentes traumas oc1usais e injúrias aos tecidos subjacentes. Este estudo tem por objetivo mensurar a variação na inclinação das cúspides mésio palatinas dos primeiros molares superiores de próteses totais após processamento, por três métodos diferentes. Para isto, foram confeccionadas, a partir de um modelo metálico representando uma maxila edêntula, 30 próteses totais superiores com as mesmas características quanto à espessura, forma e montagem dos dentes. As próteses foram divididas em três grupos de 10 amostras e foram polimerizadas por diferentes técnicas. As próteses do Grupo I foram polimerizadas por banho de água aquecida a 73°e durante, 9 horas, as próteses do Grupo II foram polimerizadas por energia de microondas a 440 W durante 4 minutos, e as próteses do Grupo III foram polimerizadas por energia de microondas a 80 W durante 15 minutos. Os ângulos formados pela intersecção das retas que representavam o prolongamento das vertentes triturantes das cúspides mésio palatinas dos primeiros molares superiores foram medidos antes da polimerização, após a polimerização e após o polimento. Os dados foram submetidos a análise estatística descritiva por não apresentarem distribuição normal. Foram confeccionadas matrizes de correlação para os ângulos medidos e encontrou-se que entre a passagem da fase de pré polimerização para a fase de pós-polimerização houve uma melhor aproximação dos ângulos (34%) para o Grupo II e que houve diferenças significativas entre as fases de pós polimerização e polimento, com grande discrepância para os três grupos, sendo 57% de aproximação para o Grupo I, 37% para o Grupo II e apenas 7% para o Grupo III, mesmo tendo sido utilizado o mesmo método de polimento para os três grupos. A partir destes dados iniciais, foram calculados a média, variância e desvio padrão. das variações angulares ocorridas na passagem das fases de pré polimerização para pós polimerização e na passagem das fases de pós polimerização para polimento. Os dados da matriz de correlação da Variância das variações angulares foram, para o Grupo I = 19% de aproximação, para o Grupo II = 54% e para o Grupo III = 33%. Os resultados das matrizes de correlação do Desvio Padrão entre as variações angulares foram: para o Grupo I = 24% de aproximação, para o Grupo II = 62% e para o Grupo III = 30%. Considera-se que a técnica mais eficiente deva apresentar coeficiente de correlação mais próximo da unidade, significando que os ângulos sofreram poucas alterações durante os procedimentos. Dessa forma, pudemos constatar que: 1. Os três métodos estudados apresentaram alterações nas inclinações das cúspides. 2. O método de polimerização por energia de microondas a 440W por 4 minutos foi o que apresentou menor alteração nas inclinações das cúspides dos dentes estudados. 3. O polimento pelo método convencional alterou significativamente a inclinação das cúspides das amostras estudadas / Abstract: In Dental Prosthesis, the techiques to polymerize acrylic resins have been improved with the objective to minimize the distortions that occur during the several phases of execution and that may cause alteration in total and/or partial removable prosthesis, with subsequent occlusal trauma and injury to underlying tissues. The purpose of this is to measure the variation in the mesial palatine cuspids inclination in the first superior molars of total prosthesis, after polymerization by three different methods. To achieve this goal, it has been prepared 30 complete dentures with the same characteristcs, after what they were divided into three groups. The dentures of the Group I were polymerized with hot water bath tecnique at 73° C during 9 hours; the dentures of the Group II were polymerized with microwave energy at 440 W during 4 minutes, the dentures of the Group III were polimerized with microwave energy at 80 W during 15 minutes. The angles obtained by the intersection of the two straight lines representing the extension of the crushing slopes of the mesial palatine cuspids of the first superior molars were measured before and after polymerization and after polishing. The data was submitted to analysis using descriptive statistics, as it did not presented a normal distribution. It has been prepared correlation matrices for all the mesured angles and it has been found that during the phase pre-polymerization to post-polymerization the angles of the Group II had a better approach (34%). During the phase post-polymerization to polishing have occurred significant differences, with great discrepancy among the three groups (57% of approach for the Group I, 37% of approach for the Group II and 7% of approach for the Group III), even considering that it has been used the same polishing method for all the groups. Starting with this initial data, it has been calculated the mean, variance and standard deviation of the angular variations occurred during the phase pre-polymerization to post-polymerization and during the phase post-polymerization to polishing. The results of the variance correlation matrix of the angular variations were, for Group I, 19% of approach, for Group II, 54% and for Group III, 33%. The results of the standard deviation correlation matrix of the angular variations wee for Group I, 24% of approach, for Group II, 62% and for Grupo III, 30%. The most efficient technique shall result in correlation coefficient near 1, what means that the angles had small alterations during the process. ... Note: The complete abstract is available with the full electronic digital thesis or dissertations / Mestrado / Fisiologia e Biofisica do Sistema Estomatognatico / Mestre em Odontologia

Orientadores: Peter Jurgen Tatsch, Jose Alexandre Diniz / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Eletrica e de Computação / Made available in DSpace on 2018-07-26T08:12:11Z (GMT). No. of bitstreams: 1 Sotero_AnnaPauladaSilva_D.pdf: 5591978 bytes, checksum: facb394156f11ef20e8b46319d5225bc (MD5) Previous issue date: 1999 / Resumo: Este trabalho descreve a obtenção e caracterização de filmes finos e ultra-finos de óxido (SiO2) e oxinitreto de silício (SiOxNy)em sistema "home-made"de plasma remoto (RP) de baixa temperatura. O sistema RP, com gerador de microondas de 2.45GHz e potência de saída de 6OOW,permite a formação de filmes tanto por processos de deposição (RPCVD) como pelo processo de oxidação (RPO). Os filmes foram caracterizados por elipsometria, perfilometria, por taxa de decapagem, microscopia eletrônica de transmissão (TEM), por espectrometria de absorção de intra-vermelho (FTIR), por espectrometria de fotoelétron de raios-x (XPS), por espectrometria de massa do íon secundário SIMS), medidas de capacitância versus tensão (C-V) e medidas de corrente versus tensão (1-V). As espessuras dos filmes produzidos variaram de 3nm a 160nm, as densidades de carga efetivas entre 1.7xl010/cm2eT5xlp12/cm2 e o campo de ruptura dielétrica foi de até 18.3MV/cm...Observação: O resumo, na íntegra, poderá ser visualizado no texto completo da tese digital / Abstract: This work describes the formation and the characterization of thin and ultra-thin silicon oxide (SiO2) and oxynitride (SiOxNy) films formed by a home-made low temperature remote plasma system (RP). In this system, a 6O0W, 2.45GHz microwave generator, allows the formation of films by deposition (RPCVD) and oxidation (RPO) processes. The films were characterized by ellipsometry, profilometry, etching rate, transmission electronic microscopy (TEM), fourier transform infrared spectrometry (FTIR), x-ray photoeletron spectrometry (XPS), secondary ion mass spectrometry (SIMS), capacitance versus voltage (C-V) and current versus voltage (I-V) measurements. The films presented thicknesses ranging trom 3nm to 160nm, effective charge densities ranging ITom 1.7xlOlO/cm2to 2.5xlO12/cm2and dieletric breakdown fields of 18.3MV/cm...Note: The complete abstract is available with the full electronic digital thesis or dissertations / Doutorado / Doutor em Engenharia Elétrica

Orientador: Altair Antoninha Del Bel Cury / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-27T06:49:07Z (GMT). No. of bitstreams: 1 Rached_RodrigoNunes_D.pdf: 4205811 bytes, checksum: 1ed41d341da9732e487d8fd07df025a9 (MD5) Previous issue date: 2000 / Resumo: Este estudo avaliou a eficiência de uma técnica de reparo para próteses totais utilizando resina acrílica para microondas e silicone extra-duro como material de revestimento. Avaliou-se a resistência ao impacto Izod (IZ), penetração (PR) e recuperação Rockwell (RR), sorção (SO) e solubilidade em água (SL), e estabilidade de cor (EC) de resinas polimerizadas pelas técnicas L (Lucitone 199, L199, 8 h./74°C, molde de gesso ), A (Acron MC, AMC, 3 mÍn./500 W, molde de gesso), AR (Acron MC/R, GC Int., 2 bares/45°C/15 min.) e ASI (ídem à técnica A, porém molde de silicone). As amostras de IZ foram confeccionadas com e sem entalho, e as de EC envelhecidas artificialmente. Adicionalmente, 40 próteses totais superiores (PT) (metade em L199 ou AMC) foram fraturadas na linha média e reparadas com L, A, AR ou AS, e tiveram os parâmetros adaptação (AD) e alterações horizontal (AR) e vertical (AV) do plano oclusal avaliadas antes e após o reparo. Testes de resistência à flexão (RF) foram conduzidos em 84 espécimes retangulares. Destes, 24 foram confeccionados com L, A, AR e ASI e mantidos intactos. Os 60 restantes foram confeccionados com L ou A, tiveram a parte central removida (10 mm) e foram reparados com L, A, AR, AS (ídem à ASl, porém ciclo de 2 min./500 W - 1 min./O W - 2 mÍn./500 W) ou ASI. Os resultados mostraram que apenas L diferiu e foi superior às Ldemais técnicas para IZ. O entalho reduziu IZ nas técnicas. Os resultados de PR para A, ASI, AR e L foram, respectivamente, 71,1-70,5-104-88,5 um; A e ASI não diferiram entre si, e diferiram de AR e L, os quais diferiram entre si. AR apresentou a menor (75,1%) RR, e os demais grupos (L=83,1%; A=86,9% e ASl=86,8%) não diferiram entre si. Para a SO, houve diferença entre os pares L-A e AR-AS! (29,6-28,3-20,9 e 21,7 J.lglmm3). Nenhum grupo diferiu para SL. Para EC, A e AS não diferiram, sendo que os demais grupos diferiram entre si; o envelhecimento acelerado afetou EC de todos os grupos. Os grupos intactos de RF diferiram entre si (L=70,8 A=80,6 AR=65,3 ASl=75,4 MPa). Nos espécimes confeccionados com L, AS (49,6 MPa) foi inferior a AS! (65,7 MPa). AS diferiu das demais técnicas e AS! não; as demais técnicas de reparo (L=70,7 A=69,2 AR=63,5 MPa) não diferiram entre si. Nos espécimes confeccionados com AMC, AS (51,2 MPa) e AS!(44 MPa) diferiram dos demais, e estes não diferiram entre si; as demais técnicas (L=70,6 A=67,2 AR=65 MPa) não diferiram entre si. O reparo com AS! apresentou maior RF em espécimes confeccionados com L199 comparado com aqueles confeccionados com Acron MC. Falhas coesivas foram mais frequentes para L e A. Já AR, AS e ASl mostraram falhas adesivas com maior frequência. Houve influência do fator "reparo" para AD, sendo que AR apresentou a melhor adaptação (0,5%); as demais técnicas não diferiram entre si (L=27,2 A=28,9 AS=21,2%). Na avaliação da AR, houve diferença entre AR e as demais técnicas para 16-26, 11-26 e 21-16, entre AR e AS para 11-21, e entre A e AS para 16-26. Quanto a AV, não houve diferenças entre os grupos. As conclusões são: 1) O molde de silicone afetou apenas a SO de AMC; 2) A interação "material da base-reparo" não influenciou AD; 3) AR forneceu a melhor AD; 4) A interação "material da base-reparo" não afetou AH; 5) O fator "reparo" alterou AH; 5) Nenhum fator alterou AV / Abstract: This study evaluated the efficacy of a new repair technique of removable prosthodontics using microwave acrylic resin and very-hard silicone as the investment material. The first part evaluated Izod impact test (IZ), Rockwell penetration (RP) and recovery (RR), water sorption (WS) and solubility (SO), and color stability (CS) of acrylic resin samples processed by the following techniques: L (Lucitone 199, L199, 8 h./74°C, gypsum mold), A (Acron MC, AMC, 3 min./500 W, gypsum mold), AR (Acron MC/R, GC Int., 2 bars/45°C/15 min.) and AS1 (similar as A, but silicone mold was used). Notched and unnotched samples were tested for IZ. EC samples were artificially aged. In the second part, forty upper dentures were equally made of L199 or AMC. These dentures were sagittally ITagmented in the middle line and repaired by L, A, AR or AS. Adaptation (AD), horizontal: (HC) and vertical changes (VC) in the occlusal plane were assayed by comparing measurements taken before and after the repair procedure. Eighty four rectangular specimens were tested for flexural strength (RF). Twenty-four intact ones were made with L, A, AR and AS1. The 60 remained ones were made ofL199 or AMC and had the middle part removed (10 mm). Then, they were repaired with L, A, AR, AS (similar to AS1, but a different cyc1e was used: 2 min./500 W - 1 mÍn./O W - 2 min./500 W) or AS1. The results showed that L was superiorly different than the other techniques for IZ; additionally, unnotched samples were stronger than notched ones. Considering RP, A and AS1 (71,1-70,5 um) were not different, whilst AR and L (104-88,5 um) differed ITom each other as well as ITom A and AS1. AR showed the lowest value (75,1%) for RR and differed ITom the other groups (L=83,1%; A=86,9% and AS1=86,8%), which did not differ among each other. For WS, the pairs L-A and AR-ASI (29,6-28,3-20,9 e 21,7 _glmm3) were statistically different. No differences were detected for SO tests. EC results did not differ for A and AS; the other groups differed among each other, and artificial aging affected EC of alI groups. RF intact groups were all different (L=70,8 A=80,6 AR=65,3 ASl=75,4 MPa). For specimens made ofL199, AS (49,6 MPa) was weaker than ASI (65,7 MPa); AS differed from the other techniques, and ASI did not; the other techniques were not different (L=70,7 A=69,2 AR=63,5 MPa). ASI showed higher RF values when performed in samples made of L199, compared to those made of AMC. Cohesive failures were more common in L and A, while adhesive ones were in AR, AS e ASI. The technique AR showed the best AD (0,5%), while the other techniques were not different (L=27,2 A=28,9 AS=21,2%). There was a statistical difference between AR and the other techniques for the HC measurements between teeth 16-26, 11-26 e 21-16; AR and AS were different for 11-21 measurement, as well as A and AS for 16-26. Differences were not detected for VC variable. The conclusions were: 1) Silicon mold technique affected WS of AMC; 2) AD was not affected by the interaction "base material-repair procedure"; 3) AR technique generated the best AD results; 4) "Base material-repair procedure" interaction did not affect HC; 5) HC was affected by the "Repair" variable; 6) Differences were not detected for VC assessments / Doutorado / Protese Dental / Doutor em Clínica Odontológica

Orientador: Altair A. Del Bel Cury / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-28T00:02:27Z (GMT). No. of bitstreams: 1 Mello_JoseAntonioNunesde_D.pdf: 2954501 bytes, checksum: a0971bb352ee05fe0cb36fed63855884 (MD5) Previous issue date: 2001 / Resumo: A técnica de injeção de resina na mufla é um eficiente e preciso método de confeccionar próteses. Contudo, este processo pode alterar as propriedades químicas e mecânicas da resina. Este estudo avaliou o efeito De um sistema de injeção de resina na mufla, no ciclo de polimerização no microondas sob pressão (resina Onda-cryl). O grupo controle foi formado pela técnica da compressão (GI, 3 min a 360 W + 4 min a O W + 3 min a 810 W). Os outros foram pela técnica de injeção (G2, 3 min a 360 W + 4 min a O W + 3 min a 810 W), e técnica de injeção com polimerização sob pressão (G3, 6 min a 180 W + 4 min a O W + 3 min a 810 W /0,1 MPa). Monômero residual (MR), resistência ao impacto (RS), resistência à flexão (RF) e microdureza superficial (MDS) foram avaliados. A análise de variância e a comparação utilizando o teste de Tukey, mostraram diferença entre os grupos, cujas médias estão seguidas por letras distintas na mesma coluna (a=5%). O sistema de injeção de resina na mufla diminuiu o nível de monômero residual e a resistência à flexão, e não teve efeito sobre a resistência ao impacto e microdureza superficial da resina / Abstract: Injection molded technique is an efficient and accurate method for processing dentures. However, the process may cause adverse effects upon chemical and physical properties of the restn. This study evaluated the effects of injection-molded system, upon a microwave polymerization cycle under pressure (Onda-cryl resin). Control group was formed by compression molded (Gl, 3 min 360 W + 4 min O W + 3 min 810 W). The others were by Injection molded (G2, 3 min 360 W + 4 min O W + 3 min 810 W), and injection molded and polymerization under pressure (G3, 6 min 180 W + 4 min O W + 3 min 810 W / 0.1 MPa). Residual monomer (RM), impact strength (1S), flexural strength (FS) and surface Knoop hardness (SKH) were evaluated. The results of analysis of variance and the means comparison using Tukey test showed difference between the groups. The means followed by different letters showed significant difference (a=5%). Injection molded system decreased RM and FS, and did not affect IS and KH of the restn / Doutorado / Protese Dental / Mestre em Clínica Odontológica

Submitted by Alex Sandro R?go (alex@ifpb.edu.br) on 2016-12-06T12:08:56Z No. of bitstreams: 1 7- Joalle Jos? Rodrigues Barros - EFEITOS DA INTERFER?NCIA GERADA POR FORNOS DE MICRO-ONDAS NAS REDES SEM FIO IEEE 802.11bgn.pdf: 4184282 bytes, checksum: f681afced9cb0342c6756cfd85fc9174 (MD5) / Approved for entry into archive by Alex Sandro R?go (alex@ifpb.edu.br) on 2016-12-06T12:10:06Z (GMT) No. of bitstreams: 1 7- Joalle Jos? Rodrigues Barros - EFEITOS DA INTERFER?NCIA GERADA POR FORNOS DE MICRO-ONDAS NAS REDES SEM FIO IEEE 802.11bgn.pdf: 4184282 bytes, checksum: f681afced9cb0342c6756cfd85fc9174 (MD5) / Made available in DSpace on 2016-12-06T12:10:06Z (GMT). No. of bitstreams: 1 7- Joalle Jos? Rodrigues Barros - EFEITOS DA INTERFER?NCIA GERADA POR FORNOS DE MICRO-ONDAS NAS REDES SEM FIO IEEE 802.11bgn.pdf: 4184282 bytes, checksum: f681afced9cb0342c6756cfd85fc9174 (MD5) Previous issue date: 2016-12-06 / Fornos de micro-ondas dom?sticos s?o dispositivos de pot?ncia que utilizam a energia das ondas eletromagn?ticas para indu??o de calor. Esses dispositivos, apesar de n?o transmitirem informa??es, radiam sinais na faixa n?o licenciada de 2,4 GHz, agindo como fontes n?o intencionais de interfer?ncia sobre outros dispositivos ISM, e sobre as redes sem fio que utilizam padr?es IEEE 802.11b/g/n e operam nessa mesma faixa. Nesta pesquisa s?o avaliados os efeitos da interfer?ncia gerada pelo forno de microondas dom?stico sobre o desempenho das redes sem fio que utilizam os padr?es IEEE 802.11b/g/n, quando operando em um mesmo ambiente, sob diferentes configura??es. As caracter?sticas do sinal interferente, proveniente das ondas que escapam da cavidade ressonante do forno de micro-ondas, s?o analisadas nos seus aspectos fundamentais, tais como, intensidade, distribui??o na frequ?ncia e varia??o no tempo, e ainda, quanto ?s suas caracter?sticas de propaga??o, a exemplo dos diagramas de radia??o vertical e horizontal e da polariza??o. Taxas de Erro de CRC de uma rede sem fio, operando em um ambiente com e sem a presen?a do sinal interferente, s?o obtidas, considerando, ainda, a utiliza??o dos tr?s padr?es, associados ? varia??o do canal utilizado e ? mudan?a da posi??o relativa dos dispositivos. A partir dos resultados obtidos, ? poss?vel avaliar se a influ?ncia da interfer?ncia gerada pelo forno de micro-ondas sobre as redes sem fio pode ser agravada ou amenizada, de acordo com a configura??o utilizada. Desse modo, o padr?o e o canal utilizados, assim como, a localiza??o dos dispositivos sem fio em rela??o ao forno, podem ser pr?-determinados de modo a minimizar os efeitos da interfer?ncia sobre o desempenho dessas redes.

Submitted by Alex Sandro R?go (alex@ifpb.edu.br) on 2017-06-06T12:21:00Z No. of bitstreams: 1 34- Josefa Gilliane de Oliveira Mariano - IMPLEMENTA??O DE FILTROS PLANARES BASEADOS NA GEOMETRIA MATRIOSKA.pdf: 2828908 bytes, checksum: 1c0801d52ad64d38cd8011edfc26a340 (MD5) / Approved for entry into archive by Alex Sandro R?go (alex@ifpb.edu.br) on 2017-06-06T12:34:10Z (GMT) No. of bitstreams: 1 34- Josefa Gilliane de Oliveira Mariano - IMPLEMENTA??O DE FILTROS PLANARES BASEADOS NA GEOMETRIA MATRIOSKA.pdf: 2828908 bytes, checksum: 1c0801d52ad64d38cd8011edfc26a340 (MD5) / Made available in DSpace on 2017-06-06T12:34:10Z (GMT). No. of bitstreams: 1 34- Josefa Gilliane de Oliveira Mariano - IMPLEMENTA??O DE FILTROS PLANARES BASEADOS NA GEOMETRIA MATRIOSKA.pdf: 2828908 bytes, checksum: 1c0801d52ad64d38cd8011edfc26a340 (MD5) Previous issue date: 2017-05-06 / Os filtros desempenham um papel fundamental nos sistemas de telecomunica??es. Embora seja uma das tecnologias mais consolidadas na Engenharia de micro-ondas, o intenso crescimento das aplica??es dos sistemas de telecomunica??es imp?e um desafio constante, requerendo o estudo de novas configura??es de filtros e uma melhor compreens?o do funcionamento dessas estruturas, em face aos requisitos de miniaturiza??o, baixo custo, largura de banda e seletividade em frequ?ncia. Neste contexto, prop?e-se neste trabalho a implementa??o de filtros planares utilizando a geometria matrioska com uma e duas se??es. Como exemplos de filtros de uma se??o s?o apresentados os resultados num?ricos e experimentais de filtros utilizando a geometria matrioska, com um, dois e tr?s an?is matrioska, observandose uma boa concord?ncia entre esses resultados. S?o apresentados os resultados num?ricos e experimentais de filtros com duas se??es, tanto com as mesmas dimens?es, como com se??es de dimens?es diferentes. Al?m disto, s?o propostas equa??es iniciais para as duas primeiras frequ?ncias de resson?ncia, que podem auxiliar no processo de otimiza??o do filtro, fornecendo os valores inicias de projeto. Dentre as caracter?sticas obtidas, destacam-se: dimens?es reduzidas, r?pida transi??o da banda passante para a banda de rejei??o e ajuste da largura de banda, o que incentiva a continuidade das pesquisas do filtro proposto.

Orientador: Antonio Marsaioli Junior / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia de Alimentos / Made available in DSpace on 2018-08-08T14:52:00Z (GMT). No. of bitstreams: 1 Pereira_NadiaRosa_D.pdf: 2441787 bytes, checksum: 905d577c0be232df49ad4362e6f6452b (MD5) Previous issue date: 2007 / Doutorado / Doutor em Engenharia de Alimentos

Orientador: Elza Cotrim Soares / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Ciencias Medicas / Made available in DSpace on 2018-08-09T15:18:59Z (GMT). No. of bitstreams: 1 Monici_LeonardoTrevizan_M.pdf: 992979 bytes, checksum: 421e46aba044c21d7aac0098bd50c43b (MD5) Previous issue date: 2007 / Resumo: Antecedentes: A ligadura elástica endoscópica (LE) é um dos métodos mais utilizados para profilaxia secundária de sangramento por varizes esofágicas, mas a recorrência varicosa é freqüente após este tratamento. A associação de LE com escleroterapia endoscópica por injeção (EI) reduz este risco. A coagulação por microondas (MC) é um método térmico de terapia endoscópica e sua associação com LE poderia reduzir o risco de recidiva de varizes. Objetivo: Avaliar a segurança e a eficácia da associação de LE com MC para o tratamento e prevenção da recidiva de varizes esofágicas em pacientes cirróticos com antecedente de hemorragia por varizes, em comparação com a associação de LE com EI. Desenho: Estudo prospectivo randomizado e controlado. Pacientes: Setenta pacientes cirróticos com episódio prévio de sangramento por varizes esofágicas tratados com LE até que restassem apenas vasos de fino calibre. Métodos: Trinta e seis pacientes foram randomizados para receber EI com etanol absoluto (Grupo A) e trinta e quatro para receber MC (Grupo B) até a completa erradicação das varizes. Foi realizado seguimento endoscópico para detecção de recidiva. Principais parâmetros avaliados: Ressangramento, complicações das intervenções, mortalidade dos pacientes, recorrência de varizes e fatores que afetam a recidiva. Resultados: Não houve diferença significativa entre os grupos A e B em termos de recidiva de varizes (27,7% versus 17,6%), ressangramento (8,3% versus 0%) e mortalidade em um tempo médio de seguimento de 34,9 ± 11,4 meses. As complicações foram raras e nenhuma diferença significativa foi verificada entre os grupos. A presença de varizes gástricas afetou a recorrência de varizes com um risco relativo de 3,9 vezes (IC de 1,14 a 13,1). Conclusões: A aplicação de MC no esôfago após a LE é segura e eficaz no tratamento de varizes esofágicas. Não houve diferença nas taxas de recorrência comparando-se a associação de LE com MC em relação à LE com EI. A presença de varizes gástricas aumenta o risco de recidiva / Abstract: Background: Endoscopic band ligation (LE) is an usual choice for secondary prophylaxis of esophageal variceal bleeding but recurrence of varices is frequent after this treatment. Association of EBL with endoscopic injection sclerotherapy (EI) reduces this risk. Microwave coagulation (MC) is a thermal endoscopic therapy method and its association with EBL may reduce the risk of variceal recurrence. Objective: Evaluate the safety and efficacy of the association of LE with MC for treatment and prevention of recurrence of esophageal varices compared to the association of LE with EI. Design: Randomized controlled trial. Patients: Seventy cirrhotic patients with previous bleeding from esophageal varices treated with EBL until only thin vessels remained. Interventions: Thirty-six patients were randomized to receive EI with ethanol (Group A) and thirty-four to receive MC (Group B) until complete eradication. Endoscopic follow-up was performed to detect recurrence. Main outcome measurements: Rebleeding, intervention complications, mortality, variceal recurrence and factors that affect recurrence. Results: No significant difference was found between Groups A and B in variceal recurrence (27.7% vs. 17.6%), rebleeding (8.3% vs. 0%) and mortality in a mean follow-up of 34.9 ± 11.4 months. Complications were rare and no difference was observed between both groups. The presence of gastric varices affects recurrence with an odds ratio of 3.9 (1.14 to 13.1). Conclusions: Application of MC in the esophagus after band ligation is safe and effective. There is no difference in recurrence rates comparing the association of LE with MC to LE plus EI. The presence of gastric varices increases the risk of esophageal varices recurrence / Mestrado / Clinica Medica / Mestre em Clinica Medica

Submitted by Cássia Santos (cassia.bcufg@gmail.com) on 2016-09-02T15:22:14Z No. of bitstreams: 2 Dissertação - Jaqueline Evangelista Costa Bezerra - 2015.pdf: 7466332 bytes, checksum: edc3cbe3c99471a17023acf2ede3160b (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Approved for entry into archive by Luciana Ferreira (lucgeral@gmail.com) on 2016-09-05T13:04:33Z (GMT) No. of bitstreams: 2 Dissertação - Jaqueline Evangelista Costa Bezerra - 2015.pdf: 7466332 bytes, checksum: edc3cbe3c99471a17023acf2ede3160b (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2016-09-05T13:04:33Z (GMT). No. of bitstreams: 2 Dissertação - Jaqueline Evangelista Costa Bezerra - 2015.pdf: 7466332 bytes, checksum: edc3cbe3c99471a17023acf2ede3160b (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Previous issue date: 2015-11-09 / Although the literature evidence the importance of using heated solution to clean injuries while doing a curative, there is not a safe and accessible procedure to heat solutions for this purpose yet. Objective: Test the efficiency of equipment produced to heat saline solution applied to treat injuries at ambulatory of curative; identify the time to cold the heated saline solution when exposed to the environmental temperature. Objective: Test the efficiency of equipment produced to heat saline solution applied to treat injuries at ambulatory of curative; identify the time to cold the heated saline solution when exposed to the environmental temperature. Method: Experimental study of technological innovation accomplished in three stages: the prototype development; efficiency test of heating saline solution flacons; instruction of the using time of the heated solutions. Result: It was developed three prototypes: one of heating by means of Peltier cells, other one of heating by resistance and another one by electromagnetic irradiation, with different results regarding the efficiency.The time of cooling varied from 3 to 35 minutes, depending on the inicial heating,the size of the flacon and the type of wrapper Conclusion: The prototype that best complied with the purpose of safe heating of the solutions was the adapted microwave by reverse engineering, from parameters of standardization created at this research. The prototype was efficient to heat flacons except the 100-ml -tough wrapper flacon which did not reach the expected temperature, however it does not derail its use at wounds treatment. The heated solutions presented time of use differed in relation to the volume of the flacons. At clinical practice can be recommended the use of the flacons of 100 ml to 250 ml per 10 minutes ( except the 100- ml- tough flacon, which is 3 minutes) and of 20 minutes for larger flacons. / Embora a literatura evidencie a importância de usar solução aquecida para a limpeza de feridas durante a realização de curativo, ainda não existe um procedimento seguro e acessível para o aquecimento de soluções com essa finalidade. Objetivos: Testar a eficácia de equipamentos produzidos para aquecer soro fisiológico destinado ao tratamento de feridas em ambulatório de curativos; identificar o tempo para o resfriamento do soro fisiológico aquecido, quando exposto à temperatura ambiente. Método: Estudo experimental de inovação tecnológica realizado em três etapas: desenvolvimento de protótipo; teste de eficácia para aquecimento de frascos de soro fisiológico; determinação do tempo de usabilidade das soluções aquecidas. Resultado: Desenvolveram-se três protótipos: um de aquecimento mediante células de Peltier, outro de aquecimento por resistência e outro por radiação eletromagnética, com diferentes resultados em relação à eficácia. O tempo de resfriamento variou de 3 a 35 minutos, dependendo do aquecimento inicial e do tamanho do frasco e tipo de invólucro. Conclusão: O protótipo que melhor atendeu à finalidade de aquecimento seguro das soluções foi o micro-ondas adaptado por engenharia reversa, a partir de parâmetros de normatização criados nesta pesquisa. O protótipo foi eficaz para aquecer frascos exceto o de 100 ml de embalagem rígida, que não alcançou a temperatura desejada, porém isso não inviabiliza a sua utilização no tratamento de feridas. As soluções aquecidas apresentaram tempo de usabilidade diferenciado em relação ao volume dos frascos. Na prática clínica pode-se recomendar a usabilidade dos frascos de 100 a 250 ml por 10 minutos (exceto para a embalagem rígida de 100 ml, que é 3 minutos) e de 20 minutos para os frascos maiores.