Made available in DSpace on 2016-08-03T16:30:57Z (GMT). No. of bitstreams: 1 RESUMO - Kelly Portugal Rodrigues.pdf: 90584 bytes, checksum: a9009d09309f76e094fc03b33ceabe30 (MD5) Previous issue date: 2011-10-04 / The aim of this in vitro study was to compare the friction resistance among conventional and aesthetic orthodontic brackets with metal and vitreous slot with round and rectangular wires of different sections, simulating some situations without wire displacement, 2 mm of displacement and binding of 3o. A group of 125 brackets from 5 brands (Roth Standard, Composite, Elation, Invu and Radiance) was tested, 25 brackets for each brand. Five brackets were set on a device in order to simulate a top right hemi-arch (lateral and central incisors, canine, first and second premolars) and after that, the device was coupled on an universal testing machine EMIC DL2000. The archwires 0.016 , 0.018 and 0.017 x 0.025 NiTi were used on the no displacement and 2 mm displacement tests, while the wires 0.017 x 0.025 , 0.019 x 0.025 and 0.021 x 0.025 stainless steel were used to simulate the binding effect. Variance analysis and Tukey tests (p<0,05) were run to compare brackets with different archwires sizes and angulation. The study demonstrated that the polycarbonate aesthetic bracket Composite had the least friction in all archwires sizes tested. On the other hand, the monocrystalline ceramic bracket Radiance showed the greatest frictional resistance on the tests without wire displacement. Studies with archwire displacement and binding showed a statistically significant difference between the five accessories, of which Composite, Roth Standard, Elation, Invu and Radiance produced the highest friction resistance, in increasing order. Moreover, the insertion of a metal slot in the polycarbonate bracket Elation significantly reduced the friction. However, these friction was greater than the one from a metal bracket. To sum up, the insertion of a vitreous slot in the polycrystalline ceramic bracket Invu offered a greater surface smoothness, reducing consequently the friction and favoring the displacement. / O presente estudo visou comparar in vitro o atrito produzido por braquetes convencionais metálicos e estéticos com canaleta metálica e vítrea quando inseridos fios de secções redonda e retangular de diferentes dimensões, simulando situações sem deslocamento, com deslocamento de 2 mm e com simulação do efeito binding 3º. Foram utilizados 125 braquetes de 5 marcas comerciais (Roth Standard, Composite, Elation, Invu e Radiance), sendo 25 braquetes para cada corpo de prova. Para os ensaios laboratoriais, foram colados 5 braquetes simulando uma hemi-arcada superior direita (incisivos central e lateral, canino, primeiro e segundo premolares) em um dispositivo para posicionamento dos braquetes, sendo este acoplado à máquina universal de ensaios EMIC DL2000. Foram empregados os fios 0,016 , 0,018 e 0,017 x 0,025 NiTi para realização dos ensaios sem deslocamento e com deslocamento de 2 mm e os fios de secção 0,017 x 0,025 , 0,019 x 0,025 e 0,021 x 0,025 CrNi para realização dos ensaios com angulação zero grau e 3º. Para a comparação entre os braquetes nos diferentes fios e angulações, foi utilizada a Análise de Variância e o teste de Tukey (p<0,05). Os resultados demonstraram que nos ensaios sem deslocamento o braquete estético de policarbonato Composite apresentou menor atrito em todos os fios avaliados, enquanto o maior atrito em todas as combinações realizadas foi observado no braquete estético cerâmico monocristalino Radiance em relação aos demais braquetes. Nos ensaios com deslocamento de 2 mm e simulação do efeito binding 3º, os resultados foram semelhantes aos observados nos ensaios sem deslocamento. Contudo, houve uma diferença estatisticamente significante entre os cinco corpos de prova, sendo o atrito verificado, respectivamente e de forma crescente, nos braquetes Composite, Roth Standard, Elation, Invu e Radiance. Pôde-se concluir que a resistência friccional teve influência da composição dos braquetes, diâmetro dos fios e tipo de ensaio realizado (deslocamento de 2 mm e angulação de 3º). Além disso, a inserção da canaleta metálica no braquete estético de policarbonato Elation reduziu de forma estatisticamente significante o atrito, porém esse foi maior do que o gerado por um braquete convencional metálico e, por fim, a incorporação da canaleta vítrea no braquete estético cerâmico policristalino Invu ofereceu uma maior lisura de superfície, reduzindo as irregularidades e imperfeições presentes na canaleta o que levou, consequentemente, a uma redução estatisticamente significante no atrito, o que demonstra que a modificação em sua canaleta favoreceu o deslocamento e reduziu de forma efetiva essa resistência à fricção.

The integrity of enamel has attracted attention of researches. Structural modifications could lead to higher bacterial retention and light reflection changes, and there the need to restore dental enamel to conditions closer to its initial state after bonding and debonding orthodontic procedures. The aim of this work was to determine and compare roughness parameters and appearance of the enamel after remnant adhesive removal, and evaluate time required for the different methods. Sixty one healthy human premolars extracted for orthodontic reasons were used, and 60 of them were examined with a profilometry analysis of surface roughness into two axes, horizontal (X) and vertical (Y). Performed this step, the specimens were submitted to bracket bonding procedure with phosphoric acid conditioning, washed and dried, a thin layer of adhesive system and light curing. After bracket debonding the specimens were randomly divided by removal method into: group 1 (control) - tungsten carbide tip (5 blades), at high speed, group 2 - tungsten carbide tip (30 blades), at high speed, and group 3 - a diamond chemical vapor deposition with ultrasound. The removal time of each remnant was recorded in seconds, and all procedure occurred under light reflector, simulating the clinical management. Thus, the samples were again submitted to profilometry analysis. Two images were obtained with 20x and 100x increase in scanning electron microscopy (SEM) of one specimen per group, chosen randomly, and one specimen that had not had its roughness evaluated, forming the Healthy group. The images were scored by two calibrated observers, such as: score 0 - perfect surface, score 1 - acceptable surface, score 2 - imperfect surface, and score 3 - unacceptable surface. Comparing roughness with intact enamel, generally, in X axis, all roughness parameters increased after the three methods, with exception of Rku and Rsk parameters. And generally, in Y axis, Ra, Rz, and Rz parameters decreased after removal in groups 1 and 2 and increased after group 3. Comparing each group after removal, in X axis, the first group showed the lowest roughness values and group 3 the largest and, in Y axis, the second group had the lowest values of Ra, Rq and Rz and group 3 the lowest values of Rku and Rsk parameters. The images were classified as Healthy Group - score 0, Group 1 - score 1, Group 2 - score 2 and Group 3 score 3. A significant increase in time removal occurred in group 1 relative to group 3. Thus, no cleanup procedures restore the enamel roughness to its original surface in all groups. The slowest procedure was performed with tungsten carbide 5 blades group. / A integridade do esmalte tem atraído a atenção de pesquisas, pois sua modificação poderá gerar maior retenção bacteriana e alterar a reflexão luminosa do esmalte, além de haver a necessidade de restituir o esmalte dentário às condições mais próximas ao seu estado inicial, após os procedimentos de colagem e descolagem ortodôntica. Este trabalho teve como objetivo determinar e comparar os parâmetros de rugosidade e aspecto do esmalte dentário após a remoção do remanescente resinoso, e do tempo despendido pelos diferentes métodos. Para isso, foram utilizados 61 pré-molares humanos hígidos, extraídos por razões ortodônticas, sendo que 60 pré-molares foram submetidos à análise prévia de rugosidade por perfilometria de superfície em dois eixos, horizontal (X) e vertical (Y). Realizada esta etapa, os espécimes foram submetidos aos procedimentos de colagem de bráquetes com condicionamento ácido, lavagem e secagem, aplicação de adesivo e fotoativação. Após a descolagem dos bráquetes, os espécimes foram divididos quanto ao método de remoção do remanescente residual em: grupo 1 (controle) ponta de carboneto de tungstênio (5 lâminas), em alta rotação; grupo 2 ponta de carboneto de tungstênio (30 lâminas), em alta rotação; e, grupo 3 ponta diamantada por deposição química, em ultrassom. O tempo de remoção de cada remanescente foi registrado, em segundos, para posterior comparação até a sua completa remoção, que ocorreu sob luz de refletor odontológico, simulando a conduta clínica. Após, os corpos de prova foram novamente submetidos à análise perfilométrica para obtenção de diferentes parâmetros de rugosidade do esmalte dentário. Foram obtidas duas imagens, com aumento de 20x e 100x em microscopia eletrônica de varredura (MEV), de um espécime por grupo, escolhido aleatoriamente, e mais um espécime que não teve a sua rugosidade avaliada, formando o grupo Hígido. As imagens foram classificadas, por dois observadores calibrados, como: escore 0 superfície perfeita; escore 1 superfície aceitável; escore 2 superfície imperfeita; e escore 3 superfície inaceitável. Foi encontrado no eixo X, aumento da rugosidade após os 3 métodos testados, com exceção do parâmetro Rsk. No eixo Y, houve diminuição da rugosidade nos grupos 1 e 2, com exceção dos parâmetros Rku e Rsk e no grupo 3 houve aumentou da rugosidade, com exceção do parâmetro Rsk. No eixo X, o grupo 1 apresentou os menores valores de rugosidade e o grupo 3, os maiores e no eixo Y, o grupo 2 apresentou os menores valores de rugosidade nos parâmetros Ra, Rq e Rz e o grupo 3 os menores valores nos parâmetros Rku e Rsk. As imagens foram classificadas como: Grupo Hígido escore 0; Grupo 1 escore 1; Grupo 2 escore 2; Grupo 3 escore 3. Houve aumento significativo no tempo de remoção do grupo 1 em relação ao grupo 3. Dessa maneira, não houve restituição das condições originais do esmalte após a remoção do remanescente resinoso em todos os grupos e o grupo 1 apresentou aumento no tempo de remoção do remanescente resinoso.

Resumo: A presente Dissertação foi composta de dois estudos. O objetivo do primeiro estudo foi avaliar in vivo, por meio da técnica Checkerboard DNA-DNA Hybridization, a contaminação de bráquetes metálicos por 40 espécies diferentes de microrganismos pertencentes aos complexos amarelo, verde, laranja e vermelho, grupo dos Actinomyces e bactérias cariogênicas. Participaram do estudo 18 pacientes (11 a 29 anos), em tratamento ortodôntico, nos quais foram colados 2 bráquetes metálicos novos, em pré-molares diferentes. Decorridos 30 dias, os bráquetes foram removidos e processados pela técnica Checkerboard DNA-DNA Hybridization. Os resultados foram analisados por meio do teste não-paramétrico de Kruskal-Wallis e pós-teste de Dunn (α=5%). De acordo com os resultados obtidos, a maioria dos microrganismos estava presente em 100% dos indivíduos. Dentre os microrganismos cariogênicos, S. mutans e S. sobrinus foram encontrados em maiores quantidades que L. acidophillus e L. casei (p<0,001). As bactérias periodontopatogênicas pertencentes ao complexo laranja foram evidenciadas em maiores quantidades do que as pertencentes ao complexo vermelho (p<0,0001). Dentre os demais microrganismos não associados com patologias específicas, a espécie observada em maior quantidade foi V. parvula (p<0,0001), pertencente ao complexo roxo. A quantidade dos microrganismos dos complexos amarelo, verde e do grupo dos Actinomyces foram semelhantes (p>0,05). O objetivo do segundo estudo foi avaliar, in vivo, por meio da técnica Checkerboard DNA-DNA Hybridization, a contaminação de bráquetes metálicos por 17 espécies de microrganismos periodontopatogênicos dos complexos vermelho e laranja e a eficácia do gluconato de clorexidina a 0,12% (Periogard®), sob a forma de bochechos. Participaram do estudo 39 pacientes (11 a 33 anos), em tratamento ortodôntico, nos quais foram colados 2 bráquetes... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The present Master's degree thesis was composed of two studies. The purpose of the first study was to evaluate in vivo by the Checkerboard DNA-DNA Hybridization technique the contamination of metallic orthodontic brackets by 40 microbial species of the yellow, green, orange and red complexes, Actinomyces group and cariogenic bacteria. Eighteen patients aged 11 to 29 years under orthodontic treatment were enrolled in this study and all subjects had 2 new metallic brackets bonded to different premolars in a randomized manner. After 30 days, the brackets were removed and processed for analysis by Checkerboard DNA-DNA Hybridization. The data were analyzed statistically by the non-parametric Kruskal-Wallis and Dunn's post tests (α=5%). According to the obtained results, most evaluated microorganisms were present in 100% of the individuals. Among the cariogenic microorganisms, S. mutans and S. sobrinus were found in larger numbers than L. acidophillus and L. casei. (p<0.001). The periodontopathogenic bacteria of the orange complex were detected in larger numbers than the red complex bacteria (p<0.0001). Among the other microorganisms not associated with specific pathologies, V. parvula, belonging to the purple complex, was the most frequently detected specie (p<0.0001). The number of yellow and green complex bacteria and Actinomyces group microorganisms was similar (p>0.05). The purpose of the second study was to evaluate in vivo by the Checkerboard DNA-DNA Hybridization technique the contamination of metallic orthodontic brackets by 17 periodontopathogenic microorganisms of the red and orange complexes, and the efficacy of 0.12% chlorhexidine gluconate (Periogard®) mouthwashes against these microbial strains. Thirty-nine patients aged 11 to 33 years under orthodontic treatment were enrolled in this study and all subjects had 2 new metallic brackets... (Complete abstract click electronic access below) / Orientador: Lídia Parsekian Martins / Coorientador: Paulo Nelson Filho / Banca: Luís Gonzaga Gandini Júnior / Banca: Mírian Aiko Nakane Matsumoto / Mestre

Made available in DSpace on 2014-06-11T19:27:55Z (GMT). No. of bitstreams: 0 Previous issue date: 2004Bitstream added on 2014-06-13T20:36:31Z : No. of bitstreams: 1 bertoz_apm_me_araca.pdf: 3969582 bytes, checksum: bceb452a18ac260c5d9321687a89fc4b (MD5) / Os recentes materiais de colagem dos acessórios ortodônticos têm visado reduzir o tempo de trabalho do clínico, simplificando o procedimento do condicionamento ácido por meio dos sistemas adesivos autocondicionantes. Todavia, as qualidades adesivas desses materiais ainda demandam ser avaliada. Assim, o presente estudo objetivou avaliar a resistência às forças de compressão de três sistemas adesivos. Cento e oitenta incisivos inferiores bovinos foram seccionados e incluídos em matrizes de resina acrílica, nos quais acessórios ortodônticos foram colados com os sistemas Transbond XT (2 grupos de 30), Transbond XT Plus Self Etching Primer (2 grupos de 30) e Tyrian (2 grupos de 30). Para cada sistema, os testes de resistência foram realizados imediatamente (30 dentes) e 24 horas (30 dentes) após a colagem, em uma máquina de ensaio Versat 2000 (Pantec), utilizando célula de carga de 500 Kgf com uma velocidade de 1mm/minuto, de acordo com a literatura. Os sistemas convencional Transbond XT, Transbond XT Self Etching Primer e Tyrian apresentaram, respectivamente, valor médio de resistência à compressão de 7,43, 7,09 e 3,41 MPa no tempo imediatamente após a colagem, e 7,42, 8,81, 5,35 MPa no tempo 24 horas após a colagem, sendo as diferenças estatísticas significantes ao nível de 5% entre os grupos Tyrian e Transbond para ambos os tempos de estudo. Concluiu-se que o material Tyrian apresentou resistência à compressão significativamente inferior em relação aos grupos Transbond que foram similares. / Recent orthodontic bonding materials have aimed to reduce the working time of the clinician, by simplifying the acid etching procedure by applying self-etching primer adhesive systems. However, the adhesion quality of these materials still demands investigation. Thus, the present study aimed to evaluate the bond strengths of three different adhesive systems. A hundred and eighty bovine lower incisors were cut and embebbed in acrylic resin matrices, in which orthodontic brackets were bonded with Transbond XT (2n = 60), Transbond XT Self Etching Primer (2n = 60) e Tyrian (2n = 60). For each composite, bond strength tests were executed immediately (n = 30) and 24 hours (n = 30) after the bonding, in the assay machine Versat 2000 (Pantec), by applying 500 Kgf of load at 1mm/min of velocity. Transbond XT, Transbond XT Self Etching Primer and Tyrian presented, respectively, average values of bond strength of 7.43, 7.09 and 3.41 MPa at the time immediately, and 7.42, 8.81 and 5.35 MPa at 24 hours after the bonding, where differences were statistically significant at 5% between Tyrian and Transbond groups at both observation times. It was concluded that Tyrian was the material that presented significant lower bond strength with regard to Transbond groups that were similar.

Submitted by Maike Costa (maiksebas@gmail.com) on 2017-03-16T12:14:26Z No. of bitstreams: 1 arquivototal.pdf: 1679756 bytes, checksum: 5065ecafba4b6ac4c0113ddd5cc81002 (MD5) / Made available in DSpace on 2017-03-16T12:14:26Z (GMT). No. of bitstreams: 1 arquivototal.pdf: 1679756 bytes, checksum: 5065ecafba4b6ac4c0113ddd5cc81002 (MD5) Previous issue date: 2014-02-18 / OBJECTIVE: The focus of this study was to test the hypothesis that treatment time and oral pH had an influence on the physical chemical properties of orthodontic brackets and arch wires. METHODS: 120 metal brackets were evaluated. They were divided into 4 groups (n=30): Group C (Control) and Groups T12, T24 and T36 (brackets recovered after 12, 24, and 36 months of treatment, respectively), rectangular stainless steel arch wires that remained in the oral cavity for 12 to 24 months were also analyzed. Dimensional stability, surface morphology and composition of brackets, resistance to sliding of the bracket/wire set and surface roughness of wires were analyzed by optical microscopy by measurement, scanning electron microscopy and energy dispersive x-ray, universal test machine and atomic force microscopy assays, respectively. Oral pH was evaluated by means of pH indicator strips by the colorimetric method. One-way analysis of variance ANOVA, followed by Tukey multiple comparisons test were used for statistical analysis (p<0.05). RESULTS: There was gradual influence of time from the 12th to 36th month for biofilm and food debris accumulation on bracket surfaces, presence of deformations on winglets and points of corrosion. Occlusal and cervical heights of brackets increased significantly after clinical use for 36 months, compared with new bracket heights (p<0.05). Carbon and Oxygen were shown to be elements that increased expressively and in direct proportion to time, and there was a progressive increase in the coefficient of friction and roughness of wires as a function of time of clinical use after 36 months. Oral pH showed significant difference only between group T36 and its control (p<0.05). CONCLUSIONS: The hypothesis was partially accepted, brackets and orthodontic wires suffered significant physical-chemical changes due to clinical use. However, the treatment time and biofilm and debris accumulation in bracket slots were shown to have more influence on the degradation process and frictional force of these devices than oral pH. / OBJETIVO: Este estudo teve como foco atestar a hipótese de que o tempo de tratamento e o pH bucal possuem influência sobre as propriedades físico-químicas de fios e bráquetes ortodônticos. MÉTODOS: Cento e vinte bráquetes metálicos foram avaliados, divididos em 4 grupos (n=30 por grupo): grupo C (Controle, como recebido do fabricante) e os grupos T12, T24 e T36 (bráquetes recuperados após 12, 24, e 36 meses de tratamento, respectivamente), fios de aço inoxidável retangulares que permaneceram na cavidade oral por 12 a 24 meses também foram analisados. Estabilidade dimensional, morfologia da superfície e composição dos bráquetes, resistência ao deslizamento do conjunto bráquete/fio e rugosidade superficial dos fios foram analisados por microscopia óptica de medição, microscopia eletrônica de varredura e por energia dispersiva de Raios X, máquina universal de ensaios e microscopia de força atômica, respectivamente. O pH bucal foi avaliado nos diferentes tempos de tratamento a partir de tiras indicadoras de pH pelo método colorimétrico. RESULTADOS: O tempo influenciou gradativamente do 12° ao 36° mês para o acúmulo de biofilme e detritos alimentares sobre a superfície dos bráquetes, presença de deformações nas aletas, além do aparecimento de pontos de corrosão. Alturas oclusal e cervical dos bráquetes aumentaram significativamente após o uso clínico de 36 meses comparado as alturas dos bráquetes novos (p<0.05). Carbono e Oxigênio demonstraram ser elementos com aumentos expressivos e diretamente proporcional ao tempo, assim como, houve um aumento progressivo do coeficiente de atrito e rugosidade dos fios em função do tempo de uso clínico com maior aumento após 36 meses. O pH bucal demonstrou diferença significativa apenas entre o grupo T36 com seu controle (p<0.05). CONCLUSÕES: A hipótese foi parcialmente aceita, bráquetes e fios ortodônticos apresentaram alterações físico-químicas significativas devido ao uso clínico. No entanto, o tempo de tratamento e o acúmulo de biofilme/detritos nos slots dos bráquetes demonstraram ser mais influentes sobre o processo de degradação e força de atrito destes dispositivos do que o pH bucal.

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / Incipient carious lesions manifested by white spots are frequently visualized around the orthodontic brackets. Further to possible progression of these lesions to cavities, a reduction on the bond strength of the bracket to the tooth enamel might occur due to mineral loss. Adhesive systems containing monomers that inhibits the bacteria adhesion or activity have been developed to help at caries control around of brackets. This study evaluated the caries inhibition and shear bond strength reached by addition of antibacterial monomer 2-(Methacryloyloxy)ethyl]trimethylammonium chloride (MADQUAT) to adhesive used to cement orthodontic brackets when submitted to cariogenic challenge. Sound premolars were sectioned in halves and brackets are cemented to the buccal and lingual surfaces using experimental adhesives with 0 (control), 5 or 10% of MADQUAT. Half of the samples was subjected to cariogenic challenge using a microcosm biofilm model with intermittent exposure to sucrose for 6 hours per day during 5 days. Following, the samples were embedded in resin cylinders and brackets submitted to shear loading until the de-bonding. The mode failure was analyzed under optical microscopy. The tested samples were sectioned and the internal enamel hardness measured to calculate the integrated mineral loss (ΔS). Data of bond strength and ΔS were submitted to two-way ANOVA and Tukey test, while the chi-square test was used to assess the effect of factors on failure mode (α = 0.05). The adhesive containing 10% of MADQUAT significantly reduced the demineralization around the bracket, but also reached lowest bond strength values. No effect on the bond strength and ΔS was observed by addition of 5% MADQUAT to adhesive. The cariogenic challenge did not affect the bond strength and the failure mode, which was influenced only by the adhesive. It was concluded that the MADQUAT was only effective to reduce demineralization when added to the adhesive at a concentration of 10%, whereas this concentration also reduced the bond strength. / Lesões cariosas incipientes, manifestadas por meio de manchas brancas, são comumente visualizadas ao redor dos bráquetes. Além destas lesões poderem progredir para cavidades, uma redução na resistência de união do bráquete ao esmalte dental pode ocorrer devido à perda mineral. Sistemas adesivos contendo monômeros que inibem a adesão ou atividade bacteriana têm sido desenvolvidos para auxiliar no controle de cárie ao redor dos bráquetes. Este estudo avaliou a inibição de cárie e a resistência de união alcançado pela adição do monômero antibacteriano [2 - (metacriloxi) etil] trimetil cloreto de amônio (MADQUAT) ao adesivo usado para colagem de bráquetes ortodônticos quando submetidos ao desafio cariogênico. Para isto, foram utilizados trinta pré-molares hígidos, seccionados ao meio. Bráquetes foram colados nas faces vestibular e lingual usando adesivos experimentais com 0% (controle), 5% ou 10% de MADQUAT. Metade das amostras foram submetidas ao desafio cariogênico em modelo de biofilme com microcosmos, com exposição intermitente a sacarose por 6 horas por dia, durante 5 dias. Em seguida, as amostras foram embutidas em cilindros de resina e os bráquetes submetidos ao carregamento de cisalhamento até ruptura. O padrão de falha foi analisado em microscopia óptica. As amostras ensaiadas foram seccionadas ao meio e a dureza interna do esmalte mensurada para calcular a perda mineral integrada (ΔS). Os dados de resistência de união e ΔS foram submetidos à ANOVA de duas vias e teste de Tukey, enquanto queo teste Qui-quadrado foi usado para avaliar o efeito dos fatores no padrão de falha (α = 0,05). O adesivo contendo 10% de MADQUAT reduziu significativamente a desmineralização ao redor do bráquete, porém alcançou menores valores de resistência de união. Nenhum efeito na resistência de união e na ΔS foi observado com a adição de 5% de MADQUAT ao adesivo. O desafio cariogênico não afetou a resistência de união e o padrão de falha, o qual foi influenciado pelo adesivo. Concluiu-se que o MADQUAT apenas foi eficaz na redução da desmineralização quando adicionado ao adesivo para uma concentração de 10%, mas esta concentração também reduziu a resistência de união.

Dental erosion is a process of wear of the enamel surface, which may be caused by the low pH present in acidic foods and beverages. Changing the tooth surface may influence the bond strength of brackets during the orthodontic treatment. Thus, this study evaluated two erosive challenge protocols from the bond strength of metal orthodontic brackets after changes in bovine enamel due to two acidic drinks. This is an experimental study, in vitro, using 60 bovine incisors. The sample was randomly divided into six groups: G1 (artificial saliva - 7 days); G2 (Coca-Cola® - 7 days); G3 (Lemon juice - 7 days); G4 (artificial saliva - 30 days); G5 (Coca-Cola® - 30 days); G6 (Lemon juice - 30 days). Initially, it was performed the analysis of dental Knoop microhardness to verify the standardization of the samples. Then, the immersion of the specimens was performed in the drinks, following the prescribed protocols. Finishing the erosive protocol, the metal brackets were cemented and, 48 hours later, the resistance was evaluated through the shear test. For statistical analysis of the data, we used the ANOVA test of two factors (solution factor and period of the treatment factor) followed by Tuckey's Post Hoc and the T Test of Student for paired samples, all with α = 5%. The sample presented normal distribution according to the Kolmogorov-Smirnov test (p= 0,77). The mean and the standard deviation of the microhardness of the total samples were 281,89 ± 44,51 KHN. There was no statistically significant difference in shear strength to the period of treatment factor (seven or 30 days F5,54= 0,105; p= 0,901), however, there were statistically significant differences for the solution factor (F5,54= 6,671; p= 0,003). The Tukey's Post Hoc test found that these differences occurred between Saliva x Coca-Cola® solutions (p= 0,003) and Coca-Cola® x Lemon juice (p= 0,029). When comparing if the treatment period would be significant for the shearing results in each solution, the T test did not show any influence of the period to any solution used. When comparing if the treatment time it would be significant for the shearing results in each solution, the T test did not show any influence of the time to any solution used. It is concluded that the period of the protocol used does not influence the bond strength of the bracket to the tooth, but, regarding the immersion substances, Coca-Cola® presented higher shear strength values. / A erosão dental é um processo de desgaste da superfície do esmalte que pode ser provocado pelo baixo pH presente em alimentos e bebidas ácidas. A alteração da superfície dental pode influenciar na resistência adesiva de bráquetes durante o tratamento ortodôntico. Desta forma, este trabalho avaliou dois protocolos de desafio erosivo a partir da resistência adesiva de bráquetes ortodônticos metálicos após alterações provocadas em esmalte bovino por duas bebidas ácidas. Trata-se de um estudo experimental, in vitro, utilizando 60 incisivos bovinos. A amostra foi dividida aleatoriamente em seis grupos: G1 (saliva artificial - 7 dias); G2 (Coca-Cola® - 7 dias); G3 (Suco de limão - 7 dias); G4 (saliva artificial - 30 dias); G5 (Coca-Cola® - 30 dias); G6 (Suco de limão - 30 dias). Inicialmente, foi realizada a análise da microdureza dental Knoop para verificar a padronização das amostras. Em seguida, foi realizada a imersão dos corpos de prova nas bebidas seguindo os protocolos estipulados. Finalizando o protocolo erosivo, os bráquetes metálicos foram cimentados e 48 horas depois foi avaliada a resistência por meio do teste de cisalhamento. Para análise estatística dos dados foi utilizado o Teste ANOVA de dois fatores (fator solução e fator tempo de tratamento) seguido do Post Hoc de Tukey e o Teste T de Student para amostras pareadas, todos com α= 5%. A amostra apresentou distribuição normal segundo o teste de Kolmogorov-Smirnov (p= 0,77). A média e desvio padrão da microdureza das amostras totais foram 281,89 ± 44,51 KHN. Não houve diferença estatisticamente significativa na resistência ao cisalhamento para o fator tempo (sete ou 30 dias; F5,54= 0,105, p= 0,901), contudo, houve diferença estatisticamente significativa para o fator solução (F5,54= 6,671; p= 0,003). O Teste Post Hoc de Tukey identificou que estas diferenças ocorreram entre as soluções Saliva x Coca-Cola® (p= 0,003) e Coca-Cola® x Suco de limão (p= 0,029). Ao se comparar se o tempo de tratamento seria significativo para os resultados do cisalhamento em cada solução, o Teste T não revelou influência do tempo para nenhuma solução utilizada. Conclui-se que o tempo de protocolo utilizado não influencia na resistência adesiva do bráquete ao dente, porém em relação às substâncias de imersão, a Coca-Cola® apresentou maiores valores de resistência ao cisalhamento.

Orientadores: Darcy Flavio Nouer, Paulo Roberto Aranha Nouer / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-08T18:00:39Z (GMT). No. of bitstreams: 1 Queiroz_VanessaSalvadegode_M.pdf: 1882065 bytes, checksum: 8fbe21dcd63e35f093d5db84e1faff56 (MD5) Previous issue date: 2007 / Resumo: Este trabalho teve como objetivo avaliar in vivo a superfície do esmalte de dentes humanos e a margem da interface braquete/esmalte por meio de microscopia óptica e laser de fluorescência. Foram analisados premolares com indicação de extração, de 35 pacientes, com idades entre 11 e 20 anos, em início de tratamento ortodôntico, divididos em grupo 1 (flúor-controle n=15), sendo 5 do gênero masculino e 10 do feminino, e grupo 2 (pré-flúor n=20), sendo 9 do gênero masculino e 11 do feminino. No total, avaliaram-se 137 dentes e 207 faces de colagem. Em cada dente observaram-se 9 pontos, sendo as 4 margens das interfaces braquete/esmalte (pontos próximos), 4 pontos à 2mm destas (pontos distantes) e 1 ponto de calibração. A avaliação foi realizada: no dia da colagem do braquete (F1), uma semana pós-colagem (F2) e quatro semanas pós-colagem (F3). Para o grupo 2, acrescentou-se uma avaliação 15 dias antes da colagem (F0). Os pacientes receberam dentifrício contendo 1.450 ppm de flúor (MFP), uma escova dentária e foram orientados à escovação 3x/dia, após as principais refeições, sendo que foram instruídos a diminuir o consumo de açúcar. Tais instruções e produtos foram oferecidos na F1 para o grupo 1 e na F0 para o grupo 2; além disso, o grupo 2 também recebeu um isolamento superficial ao redor da área de colagem. Para as avaliações, foram utilizados o laser de fluorescência - DIAGNOdent e o microscópio óptico - Sistema Galileu inclinado, acoplado a uma câmera digital Sentech STC-C83USB-AT. Para a colagem dos braquetes Microarch, utilizou-se 4 diferentes materiais: Transbond XT; Concise Ortodôntico; Fuji Ortho LC; e Monolok2. Os dados foram submetidos às análises estatísticas Mann-Whitney, Wilcoxon e Friedman (p > 0,05) e foram obtidos os seguintes resultados: as leituras com o DIAGNOdent foram significantemente maiores, ou seja, maior desmineralização, nos pontos próximos que nos distantes, em ambos os grupos; o grupo 1 apresentou leituras maiores que o grupo 2 em todas as fases do estudo; houve diminuição das leituras com o laser no decorrer das fases do estudo, para ambos os grupos; não houve diferença estatisticamente significante nas leituras para nenhum dos materiais; quanto aos gêneros, no grupo 1, o masculino apresentou leituras maiores que o feminino; já no grupo 2, o gênero feminino apresentou leituras maiores que o masculino; a face vestibular apresentou leituras maiores que a palatina em todas as fases, grupos e gêneros; foi encontrado menos excesso de material de colagem nas margens das interfaces do grupo 2 e isso parece indicar que o isolamento ao redor da área de colagem proporcionou maior proteção, porém, a presença de excesso não esteve correlacionada com o aumento de leitura do DIAGNOdent. Pôde-se concluir que o uso de dentifrício fluoretado e higienização bucal 3x/dia, com motivação semanal e controle da dieta colaboraram para a diminuição da desmineralização e/ou aumento da remineralização da superfície de esmalte, sendo que, de acordo com os resultados obtidos, esses procedimentos devem se iniciar antes da instalação do aparelho ortodôntico fixo / Abstract: The aim of this study was to evaluate in vivo the human tooth enamel surface and the bracket/enamel interface through optical microscopy and fluorescent laser. Premolars, indicated for extraction, from 35 patients (between 11 e 20 years old) beginning orthodontic treatment were evaluated. The patients were divided into 2 groups: G1 (control-fluor) (n=15) consisting of 5 males and 10 females; and G2 (pre-fluor) (n=20) consisting of 9 males and 11 females. A total of 137 teeth and 207 bond faces were evaluated. Nine points of each tooth were analyzed: 4 bracket/enamel interfaces (near points), 4 points 2mm far from these interfaces (far points) and 1 calibration point. The patients received a 1.450 ppm MFP fluoride toothpaste and a toothbrush and were instructed to brush 3x/day, after the principal meals and restrict the sugar consume. The evaluation was separated in the following Phases: at the day of bracket bonding (F1), a week after bonding (F2), and four weeks after bonding (F3). Group 2 was also evaluated 15 days before bonding and oral hygiene instructions (F0). Group 1 received the instructions at the F1 and group 2 received those at the F0. In addiction, in the group 2, the bonding area received a protection layer. It was used the DIAGNOdent and a visual inspection using optical microscopy, Galileu System (200mm) coupled to a Sentech Digital Camera model STC-C83USB-AT. The Microarch brackets were bonded with 4 different materials: Transbond XT; Orthodontic Concise; Fuji Ortho LC; and Monolok2. The data was statistically analyzed by Mann-Whitney, Wilcoxon and Friedman (p > 0,05) and DIAGNOdent showed readings significantly higher near the brackets than at far points, for both groups. However, group 1 showed higher readings at all phases tested. The laser readings decreased according to the phases, for both groups. The results showed no statistically difference between the materials used. Considering patient gender, in group 1, males showed higher readings. Females showed higher readings in group 2, though. Buccal aspect showed higher readings than palatine aspect at all phases and for both groups and genders evaluated. It was found less material excess for group 2, and this result indicates that the vaseline layer protected the interface, although the material excess was not related to DIAGNOdent readings. In conclusion, the use of fluoride toothpaste and oral hygiene with toothbrush 3x/day, added to weekly motivation and diet control can help reducing enamel demineralization and/or increasing remineralization. According to the present results, these procedures must be done before orthodontic bonding / Mestrado / Ortodontia / Mestre em Radiologia Odontológica

Objetivo: Avaliar o efeito da adrenalina e da noradrenalina sobre a adesão de Streptococcus mutans em braquetes ortodônticos. Método: Para esta finalidade, braquetes ortodônticos foram distribuídos em poços (microplaca com 96 poços com fundo cônico) contendo 105ufc/ml de S. mutans. Os braquetes foram divididos em três grupos (n=12/grupo): (1) 12 poços contendo noradrenalina (50M); (2) 12 poços contendo adrenalina (100M) e (3) 12 poços contendo NaCl 0,9% (controle). Após o período experimental (24 horas, 37C), os microrganismos não aderidos foram removidos e os braquetes submetidos à sonicação para o desprendimento de S. mutans aderidos, possibilitando assim a contagem microbiana (ufc/ml). Resultados: Ambas as substâncias testadas (adrenalina e noradrenalina) aumentaram significativamente (p<0,05) a adesão de S. mutans aos braquetes ortodônticos Conclusão: Os achados do presente estudo sugerem que a adrenalina e a noradrenalina podem contribuir para um aumento na adesão de S. mutans à braquetes ortodônticos, tornando-se assim um possível fator de risco para o desenvolvimento da doença cárie. / Aim: To evaluate the effect of adrenaline and noradrenaline (hormone/neurotrasmissor released during the stress) on the adhesion of Streptococcus mutans on orthodontic brackets. Methods: Orthodontic brackets were placed in wells (96-well plates) containing 105cfu/mL of S. mutans. The brackets were divided into three groups (n=12/group): (1) 12 wells containing noradrenaline (50M); (2) 12 wells containing adrenaline (100M) and (3) 12 wells containing NaCl (0.9%) control. After the experimental period (24 hours, 37C), the non-adherent bacteria were removed and the adherent S. mutans were detachment by sonication and counted (cfu/mL). Results: Both adrenaline and noradrenaline significantly increased (p<0,05) the adhesion of S. mutans on orthodontic brackets compared to control group. Conclusions: The findings of the present study sugests that adrenaline and noradrenaline can improve the adhesion of S. mutans to orthodontic brackets, acting as a risk factor to the development of caries.

Os efeitos mecânicos exercidos sobre os dentes pela deformação do fio de níqueltitânio dependem de sua rigidez e das características dos braquetes. Os fatores associados ao braquete são a largura, que influencia o comprimento de fio interbraquetes e o coeficiente de atrito. O objetivo desta pesquisa foi comparar a influência dos braquetes autoligáveis passivos Damon, Easy Clip e Smart Clip, sobre as forças, momentos e binding produzidos pela deformação do fio Contour NiTi .014. Metodologia: um dispositivo de simulação clínica com 3 braquetes .022x.028 de aço, correspondentes ao canino e pré-molares, foi acoplado à maquina de tração universal Instron para registro das forças e ao dinamômetro Lutron para registro dos momentos na unidade de ancoragem. A deformação de primeira ordem do fio superelástico Contour NiTi .014 foi propiciada pelo deslocamento do braquete do primeiro pré-molar fixo à máquina Instron. Foi utilizada célula de carga de 500 Newtons e velocidade de 0,05mm/segundo durante a deformação. As forças e momentos foram registrados até deslocamento máximo de 4,5 mm e durante retorno à zero. Foram realizadas dez repetições para cada modelo de braquete. O registro do binding foi obtido em teste separado por meio da tração contínua do fio Contour NiTi durante deformação de primeira ordem até 4,8 mm e retorno até zero. Os efeitos mecânicos foram comparados com deformação de 4 mm. Resultados: na unidade de movimentação as forças de ativação apresentaram diferenças significantes (Damon 224, Easy Clip 241 e Smart Clip 299 cN) enquanto as forças de desativação foram menores no Damon (62 Cn) e semelhantes entre os braquetes Easy Clip (71 cN) e Smart Clip (76 Cn). Na unidade de ancoragem os momentos de ativação apresentaram diferenças significantes (Damon 314, Easy Clip 356 e Smart Clip 438 cN/mm) enquanto os momentos de desativação foram semelhantes entre os braquetes Damon e Easy Clip (239/242 cN/mm) e significativamente maiores no Smart Clip (317 cN/mm). Os valores de binding na ativação e desativação foram semelhantes. O percentual de histerese das forças foi 70% e dos momentos 28%. Conclusões: 1) as forças de desativação produzidas pelo fio Contour NiTi .014 foram semelhantes, o que indicou equivalência mecânica entre os braquetes Damon, Easy Clip e Smart Clip na unidade de movimentação; 2) os momentos de desativação produzidos pelo fio Contour NiTi .014 foram semelhantes entre os braquetes Damon e Easy Clip, e maiores no Smart Clip, o que indicou equivalência mecânica apenas entre os braquetes Damon e Easy Clip na unidade de ancoragem ; 3) a medição das forças de atrito por meio da tração contínua do fio ortodôntico não se mostrou adequada para medir o binding associado à força de desativação; 4) a histerese acentuada observada no início da desativação das forças foi influenciada pela superelasticidade do fio e pelo binding na unidade de ancoragem. / Bracket characteristics and wire stiffness dictate the mechanical effects that nickel titanium wire deformation will cause upon teeth. The main variables associated to bracket characteristics include bracket length (that influence interbracket distance), and coefficient of friction. The purpose of this research was to compare how self ligated brackets such as Damon, Easy Clip and Smart Clip influence moments, forces, and binding produced by the deformation of a .014 Niti Contour wire. Methods: a clinical simulation device with three .022x.028 stainless steel brackets representing canine and bicuspids was attached to an Instron universal traction machine in order to register the forces, and to a Lutron dynamometer to register the moments produced on the anchor unit. The displacement of the first bicuspid fixed on the Instron machine produced a first order deformation on the superelastic .014 Niti Contour wire. A load cell of 500 Newtons under a speed of 0,05mm/second was used during the deformation. Forces and moments were registered up to 4,5mm maximum displacement and during the return to zero. For each bracket model ten repetitions were performed. Binding registration was obtained on a separate test, by continuous traction of the Contour Niti wire during first order deformation up to 4,8mm and back to zero. The mechanical effects were compared with a 4mm deformation. Results: on the moving unit, the activation forces presented significant differences (Damon 224, Easy Clip 241 and Smart Clip 299cN), while the deactivation forces were smaller on Damon (62cN) and similar on the Easy Clip (71cN) and Smart Clip (76 cN). The activation moments on the anchor unit presented significant differences (Damon 314, Easy Clip 356 and Smart Clip 438 cN/mm), while the deactivation moments were similar in the Damon (239 cN/mm) and Easy Clip (242 cN/mm) brackets, and significantly larger on Smart Clip (317cN/mm). Activation and deactivation binding values were similar. The hysteresis percentage on forces was 70% and on moments 28%. Conclusions: 1) the forces produced by the .014 Contour Niti at the movement unit are similar among the Damon, Easy Clip and Smart Clip brackets; 2) the moments produced by the .014 Contour Niti at the anchor unit are similar between Damon and Easy Clip brackets, while the Smart Clip produces larger moments; 3) the method of measuring friction forces by continuous traction of the orthodontic wire is not adequate to measure the binding associated with deactivation forces; 4) hysteresis observed at the beginning of deactivation is influenced by binding.