Structures made of the thermoplastic polymer polyether ether ketone (PEEK) are widely used in dynamically-loaded applications due to their high-temperature resistance and high mechanical properties. To design these dynamic applications, in addition to the well-known stiffness and strength properties the vibration-damping properties at the given frequencies are required. Depending on the application, frequencies from a few hertz to the ultrasonic range are of interest here. To characterize the frequency-dependent behavior, an experimental approach was chosen and applied to a sample polymer PEEK. The test setup consists of a piezoelectrically driven base excitation of the polymeric specimen and the non-contact measurement of the velocity as well as the surface temperature. The beam’s bending vibrations were analyzed by means of the Timoshenko theory to determine the polymer’s storage modulus. The mechanical loss factor was calculated using the half-power bandwidth method. For PEEK and a considered frequency range of 1 kHz to 16 kHz, a storage modulus between 3.9 GPa and 4.2 GPa and a loss factor between 9 103 and 17 103 were determined. For the used experimental parameters, the resulting mechanical properties were not essentially influenced by the amplitude of excitation, the duration of excitation, or thermal degrad.ation due to self-heating, but rather slightly by the clamping force within the fixation area.

This research investigates the challenges Scandinavian organizations face in adapting their ESG reporting practices to comply with the Corporate Sustainability Reporting Directive (CSRD), introduced in January 2024. The CSRD aims to enhance Environmental, Social and Governance (ESG) reporting by implementing double materiality assessment (DMA) and expanding the scope of value chain reporting. Given its novelty and the limited academic literature on this topic, this research provides critical insights into these transformations.  Three research questions guide this study: (1) How do Scandinavian organizations conduct the DMA of their ESG reporting under the CSRD? (2) How do Scandinavian organizations address challenges in ESG reporting along the entire value chain after adopting the CSRD? (3) How is the CSRD reshaping the ESG reporting challenges faced by Scandinavian organizations? The research employs a qualitative, exploratory approach, including expert interviews and textual analysis. Grounded in Stakeholder Theory and Value Chain Theory, the study provides perspectives for understanding stakeholder engagement and value chain dynamics in ESG reporting. The findings reveal that organizations exhibit varying approaches to DMA, influenced by conflicting definitions of materiality, differing stakeholder engagement practices and subjectivity. Despite ESRS guidance, this creates challenges in comparability and implementation. In terms of value chain reporting, organizations face significant challenges in data gathering and transparency. The CSRD reshapes ESG reporting by standardizing requirements and addressing previous inconsistencies of its predecessor, the Non-Financial Reporting Directive (NFRD). However, the CSRD introduces both opportunities and challenges for Scandinavian organizations.  By integrating Stakeholder and Value Chain Theory, this study highlights the importance of comprehensive stakeholder engagement and robust data systems. The findings underscore the need for ongoing adjustments and improvements of the reporting standards as organizations navigate the evolving ESG landscape under the CSRD. Ultimately, the CSRD is contributing to more sustainable and transparent business practices.

Dagens samhälle förändras snabbt, och digitala marknader med det. Digitaliseringen har lett till revolutionerande utvecklingar av vårt samhälle, och bakom dessa förändringar står primärt ett fåtal dominerande teknikjättar och deras plattformar. Dessa dominerande digitala plattformar, och de marknader på vilka dessa verkar, är ofta flersidiga och karaktäriseras av särskilda möjligheter till kostnadsfördelning, utveckling och ett beroende av starka nätverkseffekter, samt möjligheter att utveckla affärsmodeller som på olika sätt utnyttjar och kapitaliserar på insamlad data. Detta möjliggör inte bara upprättandet och bibehållandet av marknadsmakt på dessa marknader, utan leder även till höga inträdeshinder med resultatet att marknadens aktörer blir få och att inträdeshindren är höga. Trots att digitaliseringen till stora delar måste anses positiv, har utvecklingen även medfört nya typer av konkurrensproblematik som inte alltid kan hanteras på ett effektivt och adekvat sätt av den tidigare EU-rättsliga konkurrenslagstiftningen. Denna framställning undersöker hur EU:s konkurrenslagstiftning kan tillämpas på nyare typer av dominansmissbruk på digitala plattformar genom att analysera den tidigare regleringen av dominansmissbruk och hur denna har tillämpats rent praktiskt. För att uppnå detta mål undersöker detta arbete de särskilda utmaningar och särdrag som finns på dessa marknader, och ger en utförlig sammanfattning av hur artikel 102 FEUF har använts för att hantera dessa. Här konstateras att denna konkurrenslagstiftning lämnar en del att önska, och att inträdeshinder och risken för tippning ger starka incitament för dominanta digitala plattformar att försöka kringgå prestationsbaserad konkurrens. Framställningen utvärderar även de kompletteringar som gjorts av konkurrenslagstiftningen på dessa områden genom DMA, och hur denna reglering kan tänkas påverka hanteringen av vissa av de dominanta digitala plattformarnas beteenden framöver. Här konkluderas att DMA är en välbehövlig komplettering av tidigare konkurrensreglering på området, men att det fortfarande finns osäkerheter och utvecklingspotential, samt att de snabbföränderliga marknaderna förr eller senare kommer att hitta nya, innovativa sätt att kringgå även denna reglering. Därmed är det viktigt att den EU-rättsliga konkurrensregleringen gör vad den kan för att ligga steget före.

The aim of the present thesis is to explore sustainable low cost environmentally friendly composite materials. It is a step by step experimental research. Firstly, taking under consideration the so far commercial available non-organic materials used as reinforcement and the petroleum based resins used as matrices, composite materials were fabricated and mechanically characterized. Different components in micro- and nano- scale were combined. Afterwards, the non-organic materials used as reinforcements were substituted by different types of non conventional natural-based fillers. The fillers (corn starch and olive pit granules) were in powder form, derived from agricultural local resources and additionally flax fabric used to produce laminated composites. All the semi-green epoxy composites were characterized by means of three-point bending testing. Moreover, the manufactured composites were induced in several sources of damage and their residual properties were extensively investigated. More precisely, the effect of the strain-rate and low velocity impact as well as of thermal fatigue, on the mechanical properties of the olive pit and the flax fabric reinforced resin was studied. Since, conventional and semi-green composite materials were fabricated and experimentally investigated, the final objective of the present thesis was to produce novel green composites materials by substituting the petroleum-based epoxy resin with a biodegradable derived from natural resources biopolyester. In order to accomplish this target, polylactic acid (PLA) was combined with olive pits in powder form at different concentrations. Olive pits, is almost unknown non-traditional filler to composites, obtained during the oil extraction process. It is a raw material characterized by its low cost and its abundance, since it consists a waste product of the olive oil industry. In order to successfully accomplish this part of research, experiments were taken place in France at the CMGD (Centre des Matériaux de Grande Diffusion) Institute of the École Nationale Supérieure des Mines d’ Alés, under the guidance of Prof. A. Bergeret within the framework of research cooperation with the main supervisor of this thesis, Prof. G. Papanicolaou. The most important feature of the present green composites is their satisfactory mechanical and thermal performance in combination with their complete biodegradability. The PLA/olive pit composites could be applied to various components with moderate strength such as automotive interiors, interior building applications, durable goods, serviceware and food packaging material The aim of this part of the study was to investigate the effect of three types of olive pit powder at different weights fractions on the physical and mechanical properties of polylactide (PLA) matrix composites. For the preparation of the powder, two different grinding procedures were applied, producing three types of olive pit powder. Various measurements were accomplished to determine characteristics such as the density and the size distribution and the shape of the powder. Different PLA/ olive pits powder composites were manufactured by extrusion and injection molding. A comparative study between the different composites was made in order to investigate the matrix-filler interactions, occurring between the PLA and olive pit granules and their overall physical, mechanical and thermomechanical properties were investigated by means of TGA, FT-IR, DSC, SEM, flexural and uni-axial tensile testing. Finally, theoretical predictive models were applied in most of the composite materials manufactured in the present work. These models making use of minimal number of experimental results can satisfactorily predict the residual properties of damaged materials, irrespectively of the type of the material investigated and the damage source. Namely, the Modulus Predictive Model (ΜPM), the Residual Properties Model (RPM) and the Residual Strength after Impact Model (RSIM), have been successfully applied. A big number of interesting conclusions have been derived from the present work. However, a general conclusion is that a totally green composite with useful properties and applications is a promising target for the humanity and the planet survivability. / Σκοπός της παρούσας διδακτορικής διατριβής είναι η κατασκευή και μελέτη συνθέτων υλικών χαμηλού κόστους ενισχυμένων με φυσικά υλικά, φιλικά προς το περιβάλλον. Η επίτευξη αυτού του στόχου πραγματοποιήθηκε σταδιακά. Αρχικά, πραγματοποιήθηκε μια εκτεταμένη μελέτη διαφορετικών συνθέτων υλικών τα οποία ήταν εξ’ ολοκλήρου κατασκευασμένα από ανόργανα και συνθετικά υλικά. Γι’ αυτό το σκοπό κατασκευάστηκαν και μελετήθηκαν οι μηχανικές ιδιότητες συνθέτων υλικών που έχουν ως μήτρα μια εμπορικά διαθέσιμη πετροχημική εποξειδική ρητίνη. Η εποξειδική ρητίνη ενισχύθηκε με ανόργανα υλικά σε μικρο- (συμπαγή και κενά σφαιρίδια γυαλίου) και νανο- (νανοσωλήνες άνθρακα πολλαπλού τοιχώματος) διαστάσεις. Στη συνέχεια, βασιζόμενη στο ήδη υπάρχον επιστημονικό υπόβαθρο, καθώς η μεταπτυχιακή μου εργασία ειδίκευσης ήταν στο ίδιο ερευνητικό πεδίο με το αντικείμενο της διδακτορικής μου διατριβής, γίνεται προσπάθεια περαιτέρω εξέλιξης της έρευνας που σχετίζεται με την μελέτη και κατασκευή συνθέτων φιλικών προς το περιβάλλον. Ως εκ τούτου, το επόμενο στάδιο της πειραματικής μελέτης στα πλαίσια εκπόνησης της διατριβής αυτής, ήταν η κατασκευή και χαρακτηρισμός, ως προς την μηχανική τους συμπεριφορά, συνθέτων υλικών πολυμερικής εποξειδικής μήτρας ενισχυμένης με διαφορετικού τύπου φυσικές ενισχύσεις και περιεκτικότητες. Οι φυσικές ενισχύσεις που επιλέχθηκαν να μελετηθούν ήταν τόσο σε μορφή κόκκων και μικρο-ινών, όσο και σε μορφή υφάσματος. Τα εγκλείσματα που χρησιμοποιήθηκαν ήταν σκόνη από κόκκους ελαιοπυρήνα και σκόνη αμύλου καλαμποκιού. Στα σύνθετα υλικά ενισχυμένα με κόκκους ελαιοπυρήνα, έγινε μελέτη της επίδρασης των διαφορετικών ρυθμών παραμόρφωσης στις μηχανικές τους ιδιότητες, ενώ στα σύνθετα υλικά ενισχυμένα με την σκόνη αμύλου μελετήθηκαν εκτενώς οι στατικές μηχανικές τους ιδιότητες. Επιπλέον, κατασκευάστηκαν πολύστρωτα σύνθετα υλικά χρησιμοποιώντας για τις διάφορες στρώσεις ύφασμα από ίνες λιναριού. Τα πολύστρωτα σύνθετα υλικά χαρακτηρίστηκαν ως προς τις μηχανικές τους ιδιότητες, υποβλήθηκαν σε θερμική κόπωση και υπέστησαν κρούση χαμηλής ενέργεια. Οι εναπομένουσες μηχανικές ιδιότητες των υλικών αυτών μελετήθηκαν τόσο πειραματικά όσο και θεωρητικά. Ο απώτερος στόχος αυτής της διδακτορικής διατριβής ήταν να γίνει η δυνατή η κατασκευή συνθέτων υλικών τα οποία να είναι πλήρως βιοδιασπώμενα και φιλικά προς το περιβάλλον. Για το σκοπό αυτό, το τρίτο και τελευταίο στάδιο της έρευνας που διεξήχθη στα πλαίσια της παρούσας διατριβής, ήταν η κατασκευή εξολοκλήρου φυσικών συνθέτων υλικών έχοντας ως μήτρα ένα βιοδιασπώμενο πολυεστέρα φυτικής προέλευσης, το πολύ (γαλακτικό οξύ), ενισχυμένο με σκόνη από κόκκους ελαιοπυρήνα. Ο ξηρός ελαιοπυρήνας που χρησιμοποιήθηκε, αποτελεί μέρος των αποβλήτων που προκύπτουν από την διαδικασία παραγωγής ελαιολάδου. Ο ελαιοπυρήνας σε αυτή την μορφή έχοντας μηδαμινό κόστος απαντάται σε εξαιρετικά μεγάλες ποσότητες και σε σημαντικό ποσοστό εναποτίθεται στους περιβάλλοντα χώρους των μονάδων παραγωγής του ελαιολάδου. Η ερευνητική εργασία που σχετίζεται με αυτό το αντικείμενο του διδακτορικού έλαβε χώρα στην Γαλλία στο École Nationale Supérieure des Mines d’ Alés, στο ερευνητικό ινστιτούτο CMGD (Centre des Matériaux de Grande Diffusion) υπό την επίβλεψη της καθηγήτριας A. Bergeret, στα πλαίσια ερευνητικής συνεργασίας του επιβλέποντα καθηγητή Γ. Παπανικολάου και της ερευνητικής του ομάδας. Τα πειράματα που διεξήχθησαν στο ερευνητικό ινστιτούτο CMGD, περιελάμβαναν αρχικά την προετοιμασία των κόκκων του ελαιοπυρήνα στην κατάλληλη μορφή για να είναι δυνατή η χρησιμοποίησή τους ως ενισχυτικό υλικό. Έγινε κονιορτοποίηση των κόκκων από την οποία προέκυψαν δύο τύπου σκονών που διέφεραν ως προς την διασπορά του μεγέθους των κόκκων, ενώ μια τρίτη σκόνη ελαιοπυρήνα είχε ήδη προετοιμαστεί με διαφορετική μέθοδο κονιορτοποίησης στο τμήμα Επιστήμης των Υλικών του Πανεπιστήμιου Πατρών. Έγινε εκτενής χαρακτηρισμός των φυσικών και μορφολογικών ιδιοτήτων όλων των σκονών ελαιοπυρήνα που χρησιμοποιήθηκαν για την κατασκευή των συνθέτων υλικών με μήτρα το PLA. Προσδιορίστηκαν διαφορετικού τύπου πυκνότητες και η διασπορά του μεγέθους των κόκκων. Έγινε θερμική ανάλυση με δοκιμή θερμοζυγού (TGA), μορφολογικός χαρακτηρισμός με χρήση ηλετρονικού μικροσκοπίου σάρωσης (SEM) καθώς και χαρακτηρισμός με φασματοσκοπία υπερύθρου με μετασχηματισμό Fourier (FT IR) και ακτίνων-Χ. Αφού ολοκληρώθηκε ο χαρακτηρισμός των ιδιοτήτων της ενισχυτικής φάσης, στη συνέχεια κατασκευάστηκαν σύνθετα υλικά μήτρας PLA ενισχυμένα με τους κόκκους ελαιοπυρήνα σε διαφορετικές περιεκτικότητες. Η προετοιμασία των σύνθετων αυτών υλικών πραγματοποιήθηκε σε δύο στάδια. Αρχικά έγινε μια πρώτη μορφοποίηση με εξώθηση (extrusion). Τα σύνθετα υλικά που προέκυψαν από την εξώθηση που ήταν στη μορφή δισκίων (pellets) χαρακτηρίστηκαν και αυτά με διάφορες τεχνικές (WAXD, DSC, TGA). Τα σύνθετα υλικά υπό μορφή δισκίων για να αποκτήσουν την τελική τους μορφή ως δοκίμια κατάλληλα για μηχανικές δοκιμές κατά τα πρότυπα ISO 527, μορφοποιήθηκαν με έγχυση (Injection molding). Τα σύνθετα υλικά στην τελική τους μορφή χαρακτηρίστηκαν με διάφορες τεχνικές (WAXD, DSC, TGA), έγινε χαρακτηρισμός των μηχανικών τους ιδιοτήτων και μορφολογική παρατήρηση των επιφανειών τους ύστερα από την μηχανική τους αστοχία (SEM). Τέλος, σε πολλά από τα σύνθετα υλικά που κατασκευάστηκαν και μελετήθηκαν πειραματικά, εφαρμόστηκαν διαφορετικά ημιεμπειρικά μοντέλα ανάλυσης και πρόβλεψης της μηχανικής τους συμπεριφοράς. Στο κυρίως κείμενο της διδακτορικής διατριβής, περιγράφεται σε ξεχωριστό κεφάλαιο το σύνολο των θεωρητικών μοντέλων που εφαρμόστηκαν στα πειραματικά αποτελέσματα. Στα επιμέρους κεφάλαια που παρουσιάζονται και αναλύονται τα πειραματικά αποτελέσματα, παρατίθενται η σύγκρισή τους με τις αντίστοιχες προβλέψεις που πρόεκυψαν από την εφαρμογή των θεωρητικών μοντέλων. Από τη σύγκριση αυτή παρατηρούμε ότι τα θεωρητικά μοντέλα που εφαρμόστηκαν που είναι το μοντέλο πρόβλεψης του μέτρου ελαστικότητας κοκκωδών υλικών, ΜPM (Modulus Predictive Model), το μοντέλο πρόβλεψης της υποβάθμισης ιδιοτήτων ύστερα από διαφορετικές είδους καταπονήσεις (θερμική κόπωση, κρούση χαμηλής ενέργειας και του ρυθμού παραμόρφωσης σε κάμψη τριών σημείων), RPM (Residual Properties Model) και το μοντέλο πρόβλεψης της υποβάθμισης της αντοχής των υλικών ύστερα από κρούση, Residual Strength after Impact Model (RSIM), έδωσαν ικανοποιητικές προβλέψεις για την μεταβολή των ιδιοτήτων κάνοντας χρήση ελάχιστων μόνο πειραματικών σημείων. Στην παρούσα διατριβή συνδυάστηκαν δύο διαφορετικού τύπου πολυμερικές ρητίνες με πληθώρα ενισχυτικών υλικών για την κατασκευή και μελέτη της μηχανικής τους συμπεριφοράς, τόσο πειραματικά όσο και θεωρητικά με την εφαρμογή ημιεμπειρικών μοντέλων πρόβλεψης και ανάλυσης. Για την κατασκευή των δοκιμίων, ανάλογα με τον τύπο του υλικού της μήτρας και της ενίσχυσης, εφαρμόστηκαν διαφορετικές τεχνικές και σύνθετες πειραματικές διαδικασίες. Ενώ, για την μελέτη των μηχανικών, θερμομηχανικών και μορφολογικών τους ιδιοτήτων εφαρμόστηκε σημαντικός αριθμός διαφορετικών τεχνικών χαρακτηρισμού.

This doctoral thesis consists of a literature review, presented in two papers, and another six papers describing experimental studies of the influence of different kinds of wax and polyphosporic acid on bitumen and asphalt concrete mixture properties. The literature review should give an extensive description of the field of knowledge concerning wax in bitumen. Effects of wax in crude oil, bitumen and asphalt concrete as well as test methods for studying these effects are described. Theories behind possible mechanisms are also discussed, and commercial wax as additive to bitumen for different purposes included. The experimental parts comprise laboratory studies involving totally five 160/220 penetration base bitumens from different sources, two isolated bitumen waxes, five commercial waxes and one polyphosphoric acid. Asphalt concrete slabs, containing base or modified bitumen were prepared and tested. Binder properties were evaluated using different types of laboratory equipment, such as dynamic shear rheometer (DSR), bending beam rheometer (BBR), differential scanning calorimeter (DSC), force ductilometer, as well as equipment for determining conventional parameters like penetration, softening point, viscosity, and Fraass breaking point. Fourier Transform Infrared (FTIR) spectroscopy and Thin Layer Chromatography (TLC-FID) were used for chemical characterization. The binders were aged by means of the rolling thin film oven test (RTFOT) and pressure ageing vessel (PAV) in combination. Asphalt concrete properties were evaluated at low temperatures using the tensile strain restrained specimen test (TSRST) and creep test at -25°C. Dynamic creep testing was performed at 40°C, as well as complex modulus tests between 0 and 20°C. Binder test results indicated that the magnitude and type of effect on bitumen rheology depend on the bitumen itself, type of crystallizing fraction in the bitumen and/or type and amount of additive used. Bitumen composition was found to be of decisive importance. Adding polyethylene wax or polyphosphoric acid, especially to a non-waxy 160/220 penetration grade bitumen, showed no or positive effects on the rheological behaviour at low temperatures (decrease in stiffness) as well as medium and high temperatures (increase in complex modulus and decrease in phase angle). However, the corresponding positive effects could not be shown in dynamic creep testing (at 40°C) of asphalt concrete mixtures containing these modified binders. Adding FT-paraffin decreased the physical hardening index for all bitumens. Also polyethylene wax and montan wax showed this effect for some bitumens. Slack wax showed a large increasing effect on physical hardening, and polyphosphoric acid none or a minor negative effect. No correlation between physical hardening index (PHI) and wax content by DSC was found in this study, involving both natural bitumen wax and commercial wax. Addition of the commercial waxes used showed no or marginally positive influence on bitumen ageing properties for the bitumens and test conditions used. Comparing asphalt mixture test results to the corresponding binder test results, the effects on asphalt mixtures from adding commercial wax or polyphosphoric acid were less evident. Significant binder physical hardening by BBR could not be confirmed by TSRST. / QC 20101006

Η ανάπτυξη ευφυών υλικών, ή καλύτερα ευφυών συστημάτων, βασίζεται στην αξιοποίηση των λειτουργικών ιδιοτήτων μιας σειράς υλικών με κυριότερους εκπροσώπους τα υλικά με μνήμη σχήματος, τα ηλεκτρορεολογικά αιωρήματα και τα πιεζο/σιδηροηλεκτρικά στοιχεία. Το επιστημονικό και τεχνολογικό πεδίο των «ευφυών υλικών» επιχειρεί να αναπτύξει συστήματα υλικών των οποίων η επιτυχία δε θα βασίζεται στην εκπλήρωση πολύ υψηλών και σταθερών προδιαγραφών, αλλά στη δυνατότητα ελεγχόμενης μεταβολής της συμπεριφοράς τους. Η εργασία αυτή αναφέρεται σε κράματα με μνήμη σχήματος και στη μελέτη των συντελούμενων σε αυτά κρυσταλλογραφικών μετασχηματισμών, με τη μέθοδο της διαφορικής θερμιδομετρίας σάρωσης και τη μέθοδο της δυναμικής μηχανικής ανάλυσης. Στόχος της παρούσας εργασίας ήταν η μελέτη των μετασχηματισμών φάσεων προτανυσμένων συρμάτων SMA που είναι ενσωματωμένα στο εσωτερικό πολυμερικής μήτρας. Για λόγους αναφοράς εξετάσθηκε και η θερμική απόκριση των συνιστωσών υλικών. Το πρώτο μέρος της εργασίας προσφέρει μια βιβλιογραφική επισκόπηση του αντίστοιχου επιστημονικού πεδίου και το δεύτερο μέρος αναφέρεται στην πειραματική μελέτη του ίδιου θέματος. Στη συνέχεια δίνεται μια συνοπτική περιγραφή της διάρθρωσης της παρούσης εργασίας. Στο πρώτο κεφάλαιο γίνεται λόγος για τα ευφυή υλικά. Ως ευφυή υλικά αναφέρονται συστήματα που έχουν την ικανότητα να μεταβάλλουν τη συμπεριφορά τους ή ορισμένα χαρακτηριστικά τους (σχήμα, ιδιοσυχνότητα, συντελεστή απόσβεσης δονήσεων και άλλα) με δεδομένο και ελεγχόμενο τρόπο, εξ’ αιτίας μιας διέγερσης. Τα συστήματα αυτά ενσωματώνουν αισθητήρες και ενεργοποιητές, οι οποίοι συνδέονται μεταξύ τους με έναν κατάλληλο βρόχο ελέγχου. Στο ίδιο κεφάλαιο αναφέρονται τα υλικά που μπορούν να χρησιμοποιηθούν ως αισθητήρες και ενεργοποιητές και οι τύποι τους, τα είδη ελέγχου που έχουν επιτευχθεί, καθώς και εφαρμογές των ευφυών συστημάτων. Στο δεύτερο κεφάλαιο γίνεται αναφορά στα σύνθετα υλικά. Ως σύνθετο υλικό χαρακτηρίζεται ένα σύστημα δύο ή περισσότερων, διαφορετικών σε σύσταση και χημική δομή, υλικών τα οποία είναι φυσικά συνδεδεμένα μεταξύ τους. Τα σύνθετα υλικά αποτελούνται από μια συνεχή φάση, που λέγεται «μήτρα», ενισχυμένη με κάποιο υλικό που συνήθως αποκαλείται «ενισχυτικό ή πληρωτικό μέσο» και μια τρίτη φάση τη «διεπιφάνεια». Στο κεφάλαιο αυτό αναφέρονται οι κατηγορίες των σύνθετων υλικών, τα είδη μήτρας και εγκλεισμάτων, καθώς και τα χαρακτηριστικά της διεπιφάνειας. Στο τρίτο κεφάλαιο παρουσιάζονται τα ευφυή σύνθετα υλικά με ενσωματωμένα σύρματα με μνήμη σχήματος. Τα κράματα με μνήμη σχήματος εμφανίζουν την ικανότητα να μεταβάλλουν αντιστρεπτά ορισμένες φυσικές ιδιότητες του υλικού καθώς και το σχήμα τους. Εδώ αναλύεται ο ευθύς και αντίστροφος μαρτενσιτικός μετασχηματισμός, το φαινόμενο μνήμης σχήματος, τα κυριότερα κράματα μνήμης σχήματος που χρησιμοποιούνται και οι μηχανικές τους ιδιότητες, ενώ γίνεται αναφορά στις δυνατότητες και στους περιορισμούς των κραμάτων στις διάφορες εφαρμογές. Στο τέταρτο κεφάλαιο αναφέρονται τα υλικά που χρησιμοποιήθηκαν για την παρασκευή των ευφυών συστημάτων στην παρούσα εργασία. Αρχικά γίνεται λόγος για τη χημική δομή, τη θερμική κατεργασία και τις εφαρμογές εποξειδικών ρητινών. Στη συνέχεια αναφέρονται οι ίνες Kevlar® και αναλύεται η χημική δομή τους, τα είδη των ινών Kevlar® που υπάρχουν και οι εφαρμογές τους. Στο κεφάλαιο αυτό παρουσιάζονται και τα σύρματα με μνήμη σχήματος. Στο πέμπτο κεφάλαιο περιγράφεται ο τρόπος με τον οποίο παρασκευάστηκαν τα σύνθετα με ενσωματωμένα σύρματα με μνήμη σχήματος. Στο έκτο κεφάλαιο αναφέρονται οι πειραματικές τεχνικές που χρησιμοποιήθηκαν για τη μελέτη των δοκιμίων. Εδώ αναφέρονται σε συντομία γενικά στοιχεία για τη μέθοδο της διαφορικής θερμιδομετρίας σάρωσης (DSC) και για τη μέθοδο της δυναμικής μηχανικής ανάλυσης (DMA). Επίσης, περιγράφονται οι συσκευές της διαφορικής θερμιδομετρίας σάρωσης και της δυναμικής μηχανικής ανάλυσης που χρησιμοποιήθηκαν για τη μελέτη της θερμικής και μηχανικής απόκρισης των δοκιμίων. Στο έβδομο κεφάλαιο παρατίθενται τα πειραματικά αποτελέσματα για δοκίμια Ni-Ti, Ni-Ti-Cu με 6% σε Cu, Ni-Ti-Cu με 12% σε Cu και για σύνθετα δοκίμια NiTi με προτάνυση 3%, NiTiCu (6% Cu) με προτάνυση 2%, NiTiCu (12% Cu) με προτάνυση 3%, που μελετήθηκαν με τη διάταξη της διαφορικής θερμιδομετρίας σάρωσης (DSC). Επιπλέον, παρουσιάζονται τα πειραματικά αποτελέσματα για σύρματα Ni-Ti-Cu με 12% σε Cu και Ni-Ti, καθώς και για σύνθετα Ni-Ti-Cu (12% Cu) με 3% προτάνυση και για ρητίνη με ίνες Kevlar 29®, που μελετήθηκαν με διάταξη δυναμικής μηχανικής ανάλυσης (DMA). Στο επόμενο κεφάλαιο σχολιάζονται τα αποτελέσματα αυτά, ενώ στο τελευταίο κεφάλαιο αναφέρονται τα συμπεράσματα που προκύπτουν από τη μελέτη των αποτελεσμάτων. / Exploiting the functional properties of materials such as shape memory alloys, electrorheological suspensions and piezo/ferroelectric elements results in the development of smart materials or systems. In the scientific and technological field of smart materials the major achievement is not related to the values of specific physical properties but to the “adopted” ability to control their own behaviour. The subject of the present work concerns the crystallographic transformations of Shape Memory Alloys (SMA) under constrained conditions. The occurring transitions are studied experimentally by means of Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA). The first part of this work is a bibliographical review of the field, while the second one is the experimental study of the same subject. In the following lines, a short description, of the present thesis is given. The first chapter gives an introduction to smart materials. Composite systems, which under the influence of an external cause, can vary their behaviour or some characteristics (shape, natural vibration frequency, damping coefficient etc) in a specific and controllable way, are referred as smart materials. These systems incorporate sensors and actuators, which in turn are connected by a suitable control loop. Suitable materials for being employed as sensors and actuators, as well as the types of the, up to now, achieved control are also discussed. Chapter two covers briefly, fundamental aspects of composite materials. A system of two or more different, in composition and chemical structure, materials physically bonded between of them is characterised as a composite material. Composite materials are consisted from a continuous phase, often called “matrix”, and a discrete phase, called “reinforcing or filling phase”. Composite materials exhibit always a third phase, namely interface, between matrix and reinforcement. In this chapter the types of composites, matrices, fillers and the characteristics of interface are referred. Chapter three presents smart composite systems with embedded shape memory alloys (SMA). Shape memory alloys have the ability to change, reversibly, a number of characteristics, including their own shape. In this chapter direct and reverse martensitic transformation, shape memory effect, important shape memory alloys and their mechanical properties, as well as a short description of the manufacturing procedure of smart systems with embedded shape memory alloys, is presented. In the fourth chapter the employed materials for the production of the smart systems are discussed. The chemical structure, the curing procedure and the applications of epoxy resins are referred. Aramid fibres, such as Kevlar® fibres are also discussed, connecting their reinforcing role with their microstructure. Chapter five describes analytically the preparation procedure of the specimens. Next chapter describes the main characteristics of differential scanning calorimetry, dynamic mechanical analysis, as well and the devices used to study the thermal and mechanical response of the specimens. Chapters seven and eight present the experimental results of all the examined specimens and the resulting discussion respectively. Finally, concluding remarks and possible future work are included in chapter nine.

No description available.

Advances in information technology in the past two decades have seen innovations in the field of domestic and industrial computing that led to a paradigm shift in the management and operation of urban water systems by water utility companies. The traditional public management policy that focused on ensuring a minimum quality of service regardless of the costs associated with the processes of catchment, treatment and distribution of water, in many cases even unknown, have evolved towards more efficient cost sensitive models. These new wholly or partly public funded management systems improve not only the quality of service offered to users, but also optimize resources by reducing the cost and causing the minimum environmental impact. The new challenges raised by the European Water Framework1 Directive by imposing cost recovery to improve water efficiency and environmental sustainability have led to a significant change at all levels of water management. Consequently, new priorities have been established in terms of infrastructure management that require the reduction of water losses and the improvement of the water efficiency in urban networks for human consumption. Likewise, in a broader context which includes the water--energy binomial, it is also desirable to improve the energy efficiency and carbon emissions of these systems. Today, network sectoring is the most commonly used strategy to improve management and increase network performance. It basically consists of dividing the network into several smaller hydraulic sectors, where water inlets and outlets are perfectly controlled. This simplifies the task of carrying out periodic water balances in each of the sectors, and allows water loss volume to be assessed for a given period of time. As configuring network sectors is not a trivial task, it is therefore important to have appropriate tools to perform the task efficiently and effectively. Mathematical models can play an important role as decision support tools to help water managers assess the performance of water network distribution systems. This thesis aims to address the current problems of managing urban water networks by combining new information-processing technologies with innovative network modelling techniques. It intends to facilitate the system diagnosis and extend the use of models on the decision-making process to provide better solutions to the management of urban water networks. For this purpose a software extension that works on a geographic information system (GIS) has been developed. It integrates: the hydraulic and water quality simulation program EPANET 2, innovative tools for model analysis and diagnostic, automatic tools for sectoring and computing tools to conduct water balances in the sectors using actual measurements. The work demonstrates the compatibility and complementarity of GIS and hydraulic models as technologies that can be used to support the assessment and diagnosis of water distribution networks. Considering that the majority of information linked to the network system has some geographic reference, it is not surprising that GIS has become a popular tool for dealing with such information. At the same time, the integration of mathematical modelling and simulation tools, offers the GIS a new dimension in the realm of hydraulic study of water networks. Furthermore, if this specific integration is provided with new features aimed not only to facilitate the model building, but also to assist the user in decision-making using powerful algorithms based on the application of the graph theory, the result is a powerful up-to-date analytical tool, which opens up new possibilities in the field of management and efficient operation of urban water supply systems. / Bartolín Ayala, HJ. (2013). Confección de modelos de redes de distribución de agua desde un Sig y desarrollo de herramientas de apoyo a la toma de decisiones [Tesis doctoral no publicada]. Universitat Politècnica de València. https://doi.org/10.4995/Thesis/10251/33152 / TESIS

This thesis deals with the development of embedded system for ultra light airplanes and helicopters. The aim is to design a system which would allow to measure and record the length of individual flights. It is therefore an onboard electronic diary which should facilitate and streamline the administration associated with sport aircraft operation. The base of the system is created on microcontroller of the MSP430 family by Texas Instruments. A reader will be offered the used hardware, the system design, the way of function and the possibility of using of the suggested system.

This diploma thesis deals with the design and implementation of an electronic module for acoustic detection. The module has the task of detecting a predetermined acoustic signals through them learned classification model. The module is used mainly for security purposes. To identify and classify the proposed model using machine learning techniques. Given the possibility of retraining for a different set of sounds, the module becomes a universal sound detector. With acoustic sound using the digital MEMS microphone, for which it is designed and implemented conversion filter. The resulting system is implemented into firmware microcontroller with real time operating system. The various functions of the system are realized with regard to the possible optimization (less powerful MCU or battery power). The module transmits the detection results of the master station via Ethernet network. In the case of multiple modules connected to the network to create a distributed system, which is designed for precise time synchronization using PTP protocol defined by the IEEE-1588 standard.