No / The in-line development of crystalline morphology and orientation during melt extrusion of low density polyethylene (LDPE) tape at nil and low haul-off speeds has been investigated using Small-Angle X-Ray Scattering (SAXS). The processing parameters, namely haul-off speed and distance down the tape-line have been varied and the resulting crystalline morphology is described from detailed analysis of the SAXS data. Increasing haul-off speed increased orientation in the polymer tape and the resulting morphology could be described in terms of regular lamellar stacking perpendicular to the elongation direction. In contrast, under nil haul-off conditions the tape still showed some orientation down the tape-line, but a shish-kebab structure prevails. The final lamellae thickness (similar to 50 angstrom) and bulk crystallinity (similar to 20%), were low at, for all processing conditions investigated, which is attributed to the significant short-chain branching in the polymer acting as point defects limiting lamellae crystal growth. (C) 2013 Elsevier Ltd. All rights reserved.

This report summarizes the work on the cloning, expression, and purification of PerR, a metal sensing regulator from Saccharopolyspora erythraea and the subsequent characterization using small angle X-ray scattering and other biochemical methods. The report aims to provide an insight into prokaryotic metal homeostasis, provide a better understanding of how PerR works and provide valuable information for the continued work on the crystallization of PerR.

Aus den frühen Bindungsstudien des globalen Regulators AbrB mit der ausgedehnten phyC-Promotorregion von Bacillus amyloliquefaciens FZB45 konnte ein mehrstufiger kooperativer Bindungsprozess abgeleitet werden. Dabei verlangt die AbrB-vermittelte Repression von phyC nach Integrität zweier großer Bindungsstellen, ABS1 und ABS2, die 162 bp voneinander entfernt liegen. In der vorliegenden Arbeit wurden die ersten Echtzeitkinetiken zur DNA-AbrB-Interaktion mittels der Oberflächenplasmonresonanz (SPR) gemessen und analysiert. AbrB zeigte hohe Affinitäten zu den 40 bp langen Oligonukleotiden, die den beiden Bindungsstellen entstammen. Dabei verursachten alle Oligonukleotide der ABS2 und nur eine kurze Region innerhalb der ABS1 bei der Bindung von AbrB Konformationsänderungen im Protein und in der DNA (CD - Zirkulardichroismusspektroskopie) und wiesen eine Kooperativität von 2 / In previous binding studies it could be demonstrated that a global regulator AbrB and the extensive phyC promoter region of Bacillus amyloliquefaciens FZB45 interact in a complex manner. AbrB binding is a multistep cooperative process. The integrity of both binding sites, ABS1 and ABS2, which are separated by 162 bp, is crucial for the AbrB-mediated repression of phyC. This work presents the first real-time binding kinetics of the AbrB-DNA interaction using surface plasmon resonance (SPR). AbrB exhibited high affinities to all analyzed 40-bp oligonucleotides that were derived from the ABSs of phyC. All parts of the ABS2, but only a small region within ABS1, were bound cooperatively to AbrB with a stoichiometry of 2 DNA to 1 AbrB tetramer and with 2

Dans le travail actuel, nous avons entrepris une étude structurale des monocristaux de polystyrène-polyoxyde d'éthylène (PS-b-PEO) pour élucider l'influence de la conformation du bloc de PS sur la cristallisation à partir d'une solution diluée. Nous avons également étudié le comportement des monocristaux lors d'une chauffe. Il est à noter que l'intérêt dans ces systèmes a été récemment réapparu en vue d'utilisation des monocristaux de copolymères pour générer des brosses amorphes uniformes. Lors de la cristallisation du PEO le bloc amorphe, c. à d. le PS, est rejeté du cristal et s'accumule donc sur des surfaces basales des lamelles cristallines. Puisque l'épaisseur cristalline qui résulte d'un processus de cristallisation isotherme a une valeur bien définie, la densité de greffage de PS en est aussi. Ainsi en changeant l'épaisseur du cristal nous pouvons générer des brosses de PS ayant des densités de greffage très variées. Dans notre étude, nous avons employé une combinaison des techniques d'analyse qui sont opérationnelles dans l'espace directe et réciproque telles que l'AFM et le SAXS/WAXS. Les expériences AFM ont été réalisées sur des monocristaux isolés tandis que les mesures SAXS/WAXS ont été faites sur des gâteux de monocristaux orientés qui ont été préparés par sédimentation lente à partir d'une solution diluée. L'interprétation des résultants SAXS se base sur le modèle à deux phases où les épaisseurs des régions cristallines (Lc) et amorphes (La) peuvent être déterminées en suivant les approches conventionnelles de la fonction de corrélation ou la fonction de distribution des interfaces. / In the present work, we have undertaken a structural study of PS-b-PEO single crystals to elucidate the influence of the state of the PS block on crystallization from dilute solution and on subsequent thermal annealing at elevated temperature. It is noteworthy that the interest in these systems has been recently renewed in the perspective of using them as a model of grafted amorphous brushes with variable grafting density. Indeed, during crystallization of PEO, the amorphous block, i.e. PS, is rejected from the crystal accumulating on its basal surfaces. Since the crystal thickness formed during isothermal crystallization is a sharply selected value, the grafting density of the resulting PS brush is also well defined. Therefore by varying the crystal thickness one can obtain the PS brushes with grafting density varying in a broad range.In our study, a combination of reciprocal and direct-space techniques such as SAXS/WAXS and AFM was employed. While AFM experiments were performed on isolated single crystals, the SAXS investigation was carried out on oriented mats of single crystals slowly sedimented from the "mother" solution. In this case, the one-dimensional two-phase system model was used for the data interpretation where the thickness of the amorphous (La) and crystalline (Lc) layers are conventionally determined following the correlation fonction and interface distribution fonction approaches.

Notre étude a porté sur la compréhension microscopique des mécanismes de déformation du polyamide 6 (PA6) à l’état massif. Par des traitements thermiques appropriés, on a obtenu un jeu d’échantillons présentant des microstructures semi-cristallines variées, avec différentes formes cristallographiques (allotropes : α, γ ou β), différents taux de cristallinité (de 24 à 35%), différentes périodes de l’empilement des lamelles cristallines (de 7 à 12nm), ceci pour deux masses moléculaires différentes. Les propriétés mécaniques en traction ont été caractérisées au-dessus et au-dessous de la transition vitreuse de la phase amorphe (Tg). Les différents matériaux présentent des différences notables de comportements. Le taux de cristallinité semble être le facteur prédominant au-dessus de Tg, mais d’autres facteurs sont à prendre en compte en dessous de Tg, comme la forme cristalline et la morphologie lamellaire (épaisseur et facteur de forme). Grâce à un dispositif expérimental fabriqué sur mesure, des essais de traction ont été suivis par diffusion des rayons X aux petits (SAXS) et grands angles (WAXS) sur la ligne D2AM, ESRF, pour caractériser les déformations à l’échelle des empilements lamellaires et à l’échelle de la maille cristalline. Dans les échantillons présentant principalement de la phase cristalline β, les lamelles tendent à s’orienter perpendiculairement à la direction de traction (TD). Ce mécanisme d’orientation local (que nous appelons « modèle de réseau de chaînes ») est induit par la transmission des contraintes par les chaînes amorphes reliant les lamelles cristallines adjacentes. L’allongement local est plus faible que l’allongement macroscopique dans les lamelles perpendiculaire à TD, ce qui implique que les lamelles inclinées doivent être cisaillées. De plus, la phase β se transforme en phase α aux fortes extensions. Dans les échantillons présentant principalement de la phase α (la plus rigide), au-dessus de Tg, dans le régime élastique, les chaînes tendent d’abord à s’orienter perpendiculairement à TD, ce qui implique que les lamelles s’orientent parallèlement à TD (« modèle de lamelles rigides »). Ensuite, dans le régime plastique, une majeure partie des lamelles se réoriente perpendiculairement à TD, comme dans le « modèle de réseau de chaînes », tandis qu’une fraction mineure reste orientée parallèlement à TD. Une morphologie fibrillaire fortement orientée est finalement obtenue pour tous les échantillons quelle que soit la température. / Mechanical properties of bulk polyamide 6 (PA6) have been studied in relation to microscopic deformation mechanisms. By applying various thermal treatments, sets of samples with different semi-crystalline microstructures, namely various crystalline allotropic forms (denoted α, γ and β) and different values of the crystallinity index (from 24 to 35%) and of the long period of the lamellar stacks (from 7 to 12 nm), have been obtained, for two different molecular masses. Mechanical properties have been measured in the linear (viscoelastic) and nonlinear (plastic) regimes below and above the glass transition of the amorphous phase (Tg). Differences of behavior have been observed depending on the microstructure. While the crystallinity index seems to be the predominant factor affecting the mechanical behavior above Tg, other structural parameters such as the crystalline form and the lamellar morphology (thickness and aspect ratio) have to be taken into account below Tg. Deformations at the scales of lamellar stacks and of the crystalline unit cell have been characterized by small and wide angle X-ray scattering (SAXS and WAXS) performed in-situ during tensile tests. In samples with predominantly β phase, lamellae tend to orient perpendicular to the tensile direction (TD). This orientation mechanism (which we denote as ‘Chain Network model’) is driven by the amorphous chains which transmit the stress between adjacent lamellae. The tensile strain in lamellar stacks perpendicular to TD is lower than the macroscopic tensile strain, which must be compensated by increased shear in inclined stacks. Also, at high extension ratios, the β phase transforms into α phase. In samples with predominantly α phase and above Tg, morphology changes are more complex. In a first step, chains orient perpendicular to TD, which implies that lamellar planes tend to orient parallel to TD, possibly due to their high aspect ratio (denoted as ‘Rigid Lamella’ model). In a second step, beyond the yield, a major fraction of crystallites then reorients normal to TD, i.e. chains themselves become parallel to TD, while a minor fraction remains oriented along TD. A highly oriented fibrillar morphology is ultimately obtained in all cases.

<p>A new kind of lipid/polymer composite particle, consisting of a biodegradable polymer matrix with well-defined lipid domains, has been created. The lipid used is the water-swelling lipid monoolein (MO), which forms a reversed bicontinuous cubic diamond structure in aqueous solutions. The polymer is poly(d,l-lactide-co-glycolide) (PLG), which degrades into water-soluble monomers through hydrolysis. This new particle might be a good alternative for encapsulation of active substances intended to be released over a longer period of time, i.e. sustained/retained/controlled release.</p><p>To prepare such particles can be difficult. Suitable phase behaviour and a solvent with the right properties are needed. For this reason, the phase behaviours of several different lipid/polymer/solvent/water systems have been explored. From the phase behaviour of a suitable system (i.e. MO/PLG/ethyl acetate/water), a route for formation of lipid/polymer composite particles has been deduced. Particles have been formed and distinct, water-swelling, lipid domains have been confirmed by characterization by means of confocal laser scanning probe microscopy (CLSM). </p><p>The sample preparation process has been automated and a method based on using a robotic liquid handler has been developed. Phase diagrams have been determined by examination of macroscopic behaviours and the microstructures of the phases have been studied by small- and wide-angle X-ray scattering (L₃, V₂, L_α, L), nuclear magnetic resonance self-diffusion (L, L₃), viscosimetry (L) and rheology (L). Several different theoretical models have been applied for interpretation of the results. For example, the swelling of the reversed bicontinuous cubic phases and the sponge phase have been modelled by applying the theory of infinite periodical minimal surfaces, the sponge phase has been shown to be bicontinuous according to the theory of interconnected rods and the phase behaviour of the polymer has been described by the Flory-Huggins theory. The main focus of this work (4/5) concerns phase studies in multicomponent systems from a physical-chemical point of view.</p>

A new kind of lipid/polymer composite particle, consisting of a biodegradable polymer matrix with well-defined lipid domains, has been created. The lipid used is the water-swelling lipid monoolein (MO), which forms a reversed bicontinuous cubic diamond structure in aqueous solutions. The polymer is poly(d,l-lactide-co-glycolide) (PLG), which degrades into water-soluble monomers through hydrolysis. This new particle might be a good alternative for encapsulation of active substances intended to be released over a longer period of time, i.e. sustained/retained/controlled release. To prepare such particles can be difficult. Suitable phase behaviour and a solvent with the right properties are needed. For this reason, the phase behaviours of several different lipid/polymer/solvent/water systems have been explored. From the phase behaviour of a suitable system (i.e. MO/PLG/ethyl acetate/water), a route for formation of lipid/polymer composite particles has been deduced. Particles have been formed and distinct, water-swelling, lipid domains have been confirmed by characterization by means of confocal laser scanning probe microscopy (CLSM). The sample preparation process has been automated and a method based on using a robotic liquid handler has been developed. Phase diagrams have been determined by examination of macroscopic behaviours and the microstructures of the phases have been studied by small- and wide-angle X-ray scattering (L3, V2, Lα, L), nuclear magnetic resonance self-diffusion (L, L3), viscosimetry (L) and rheology (L). Several different theoretical models have been applied for interpretation of the results. For example, the swelling of the reversed bicontinuous cubic phases and the sponge phase have been modelled by applying the theory of infinite periodical minimal surfaces, the sponge phase has been shown to be bicontinuous according to the theory of interconnected rods and the phase behaviour of the polymer has been described by the Flory-Huggins theory. The main focus of this work (4/5) concerns phase studies in multicomponent systems from a physical-chemical point of view.

Title: Self-assembly of polymers with amphiphilic compounds (surfactants) in aqueous solutions Abstract: This PhD Thesis is devoted to the co-assembly in systems containing electrically charged polymers (polyelectrolytes and block copolymers containing polyelectrolyte sequences). I studied the interactions between block copolymers and oppositely charged surfactants in aqueous solutions, and the structure and properties of co-assembled nanoparticles by a combination of several experimental methods. I found that the spontaneous formation, solubility and stability of complex nanoparticles depend not only on the electrostatic attractive forces but also on the hydrophobic effects. In a major part of my Thesis, I studied the interaction of polyelectrolytes with oppositely charged gemini surfactants (containing two charged head-groups interconnected by a short linker and two hydrophobic tails) which is a relatively new topic - much less studied than the co-assembly with conventional single tail surfactants. Better understanding of the formation and properties of complexes containing gemini surfactants and polymers provides knowledge that should lead to novel tailor-made nanoparticles with desired properties for applications in medicine and new technologies (including nano-technologies). We have shown that the...

Ce travail de thèse a visé la préparation de matériaux biohybrides à base de poly (liquide ionique)s (PIL) et de polysaccharide, en l’occurrence la gomme de guar. Les chaînes de poly (1- [2-acryloyl éthyl] -3 bromure-méthylimidazolium (poly (AEMIBr)) ont été synthétisées par polymérisation contrôlée de type RAFT. Des homopolymères de DP élevé (jusqu'à 300) et de faible dispersité (inférieur à 1,19) ont été obtenus seulement en quelques heures dans l'eau. Ces PIL ont par ailleurs été utilisés comme macroagents de transfert pour générer différents copolymères à blocs en milieu homogène et en émulsion dans le but d’accéder à des nano objets autoassemblés. En effet, différentes morphologies ont été obtenues en s’appuyant sur lesconcepts de la PISA. De plus, des copolymères greffés de type guar-g-PIL ont finalement été construits en milieu liquide ionique.en utilisant des dérivés de guar macroagents de transfert Les PIL combinent à la fois les propriétés des IL (non-volatile, stabilité thermique et chimique, haute conductivité...) et celles des polymères en termes de renforcement mécanique, c’est pourquoi ils ont été exploités pour élaborer des matériaux biohybrides de haute performance. La stratégie envisagée dans ce travail réside sur l’exploitation de trois composants: (i) les chaînes de poly (AEMIBr), (ii) le guar et (iii) un liquide ionique: le chlorure de butylméthylimidazolium (BMIMCl). La voie expérimentale permettant l’obtention de tels matériaux est très simple et non dégradante puisqu’elle n’implique que des étapes de solubilisation de polymères en milieu IL. Les propriétés rhéologiques et thermiques de ces matériaux ont été évaluées. En outre, la morphologie interne, par des mesures de WAXS et SAXS, ainsi que le transport ionique ont été étudiés. Il en ressort que de multiples interactions synergiques sont formées entre le guar et les chaînes de PIL, en parallèle des interactions de type PIL/IL et guar/IL. Des ionogels possédant un haut module élastique (jusqu'à 30 000 Pa) et une stabilité thermique élevée (jusqu'à 310 °C) ont ainsi été obtenus. En particulier, la présence de PIL a permis d’améliorer de façon considérable la stabilité dimensionnelle des gels, en limitant complétement les phénomènes d’exudation rencontrés dans les systèmes binaires guar/IL. Il s’avère, de plus, que ces matériaux sont parfaitement homogènes à l’échelle d’observation des analyses SAXS et WAXS. Ces gels ioniques présentent d'excellentes propriétés de transport ionique (10-4 S/cm à 30 °C) grâce notamment à leur structuration interne continue. Cette famille des matériaux multicomposants à base de guar, présente un fort potentiel, notamment pour une utilisation en tant que gel électrolyte dans le domaine de l’énergie. / This Ph.D work focuses on the preparation of biohybrid materials based on poly(ionic liquid)s (PIL) and a polysaccharide, guar gum. Poly(1-[2-acryloylethyl]-3-methylimidazolium bromide (poly(AEMIBr)) chains were synthesized through RAFT polymerization. Homopolymers with DP up to 300 and dispersity below 1.19 were obtained within hours in water. High chain-end fidelity further allowed for PIL chain extension with various monomers and stable PIL-based nanoparticles with various morphologies using the PISA concept were achieved. A series of guar-g-PIL graft copolymers were finally constructed in IL using guar macroRAFT agents. As PILs combine the attributes emanating from IL molecules (non-volatile, thermally stable, conducting…) with the ones of polymers in terms of mechanical reinforcement, the resulting polymers were exploited to elaborate high performance biohybrid materials. The cornerstone of this subsequent work was based on the straightforward formation of three-component blends: (i) poly(AEMIBr), (ii) guar and (ii) ionic liquid: butylmethylimidazolium chloride (BMIMCl). The pathway to obtain such ternary blends is very simple, since it only implies successive polymer solubilisation steps in IL. The rheological and thermal properties of the resulting materials were investigated. Also, the internal morphology by WAXS and SAXS measurements as well as the ionic transport were studied. It appeared that strong synergistic hydrogen bonding are developed between guar and PIL chains in addition to PIL/IL and guar/IL interactions. Ionogels with high elastic modulus (up to 30 000 Pa) and high thermal stability (up to 310°C) were prepared. Importantly, addition of PIL significantly enhanced the dimensional stability of the resulting ionogels and overcame IL exudation encountered in IL/guar binary systems. SAXS and WAXS revealed a homogeneous morphology and the ionogels were proven to exhibit excellent conductive properties (10-4 S/cm at 30°C) thanks to their highly continuous morphology. The resulting sustainable multicomponent materials may find applications as gel electrolyte for biobattery systems or supercapacitors.

Un polyélectrolyte hydrophobe est un polymère portant des charges électriques lorsqu'il est en solution aqueuse et dont l'eau est un mauvais solvant pour le squelette. Cette thèse a pour objectif d'établir l'influence de la nature hydrophobe du squelette sur les propriétés physiques des polyélectrolytes. Pour cela, nous avons tout d'abord synthétisé une série de poly(styrène-\emph(co)-styrènesulfonate de sodium), appelés PSS, possédant des taux de charge $f$ variant entre 30\% et 100\% et comportant entre $N=120$ et $N=2520$ monomères par chaîne. Ces PSS sont caractérisés précisément et peuvent être considérés comme des polyélectrolytes hydrophobes modèles. Nous avons alors étudié leurs propriétés volumiques puis interfaciales.\\ \emph(1. Propriétés en volume.) Le taux de charge effectif de la chaîne unique est anormalement réduit par rapport au cas du polyélectrolyte hydrophile. D'autre part, les propriétés structurales ont été caractérisées par la diffusion des rayons X et la technique de la sonde colloïdale en microscopie à force atomique (AFM). La conformation des chaînes se fait ressentir puisque la longueur de corrélation varie comme $N^0C_p^(-\alpha)$ où $C_p$ est la concentration en polymère et $\alpha$ un exposant dépendant de $f$, décroissant de 1/2 ($f=100\%$) à 1/3 au voisinage de la limite de solubilité. Ces observations sont interprétées dans le cadre d'un modèle théorique prédisant la conformation de la chaîne isolée comme un collier de perles, constitué de globules denses (les perles) reliés deux à deux par un segment de chaîne étirée. La dynamique collective des chaînes, quant à elle, est très proche de celle des polyélectrolytes hydrophiles.\\ \emph(2. Propriétés aux interfaces.) Nous avons conçu une expérience permettant, par adsorption électrostatique ou hydrophobe, de fixer les chaînes de PSS sur une surface solide plane modifiée chimiquement. La couche de PSS adsorbée, immergée dans l'eau, est caractérisée $in~situ$ par ellipsométrie, réflectivité des rayons X haute énergie et microscopie à force atomique. Nous avons ainsi trouvé que la taille de perles varie entre 1 et 5 nm en fonction de $f$. Cette variation est en parfait accord avec les prédictions du modèle dit du collier de perles. Enfin, les polyélectrolytes hydrophobes s'adsorbent également aux interfaces hydrophobes, les perles, dans certains cas, s'étalant sur la surface.